Waterproof colored solid paint and preparation method thereof

A solid, color technology, applied in multi-color effect coatings, coatings, buildings, etc., can solve the problems of insufficient waterproof performance of emulsion coatings, pollute the production environment, and affect product sales, and achieve excellent waterproof effect, uniform color, and excellent products. The effect of selling

Inactive Publication Date: 2011-01-12
湖北万利环保节能材料有限公司
View PDF18 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, solvent-based coatings can be colored, but they have a strong odor during the spraying process, which seriously pollutes the production environment; emulsion coatings are not waterproof enough; hot-melt spray waxes are acceptable in waterproofing, but difficult to color, which affects the appearance of the product

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A preparation method of waterproof color solid paint, it comprises the steps:

[0027] 1) Selection of raw materials: according to the parts by weight of each raw material: 100 parts by weight of acrylic resin, 1 part by weight of sunflower oil, 1 part by weight of polymerized linseed oil, 1 part by weight of solvent-free alkyd resin, high chlorinated 1 part by weight of polyethylene resin, 1 part by weight of pigment, 0.01 part by weight of vanadium isooctanoate, 0.01 part by weight of cobalt isooctanoate, select acrylic acid resin, sunflower oil, polymerized linseed oil, solvent-free alkyd resin, high chlorinated Polyethylene resin, pigment, vanadium isooctanoate and cobalt isooctanoate raw materials, spare;

[0028] The acrylic resin is a solid acrylic resin, and Mitsubishi BR-113 thermoplastic acrylic resin is selected for use.

[0029] The sunflower oil is semi-dry sunflower oil, and the mass content of water is 0-0.1%.

[0030] The solvent-free alkyd resin is BD...

Embodiment 2

[0045] A preparation method of waterproof color solid paint, it comprises the steps:

[0046] 1) Selection of raw materials: according to the parts by weight of each raw material: 100 parts by weight of acrylic resin, 5 parts by weight of sunflower oil, 5 parts by weight of polymerized linseed oil, 5 parts by weight of solvent-free alkyd resin, high chlorinated 5 parts by weight of polyethylene resin, 5 parts by weight of pigment, 0.2 parts by weight of vanadium isooctanoate, 0.2 parts by weight of cobalt isooctanoate, select acrylic resin, sunflower oil, polymerized linseed oil, solvent-free alkyd resin, high chlorinated Polyethylene resin, pigment, vanadium isooctanoate and cobalt isooctanoate raw materials, spare;

[0047] Acrylic resin is solid thermoplastic glass resin of Yangzhou Shixing Xing Resin Co., Ltd.

[0048] The sunflower oil is semi-dry sunflower oil, and the mass content of water is 0-0.1%.

[0049] The solvent-free alkyd resin is BD251 super long oil solven...

Embodiment 3

[0063] A preparation method of waterproof color solid paint, it comprises the steps:

[0064] 1) Selection of raw materials: according to the parts by weight of each raw material: 100 parts by weight of acrylic resin, 8 parts by weight of sunflower oil, 8 parts by weight of polymerized linseed oil, 8 parts by weight of solvent-free alkyd resin, high chlorinated 8 parts by weight of polyethylene resin, 8 parts by weight of pigment, 0.4 part by weight of vanadium isooctanoate, 0.4 part by weight of cobalt isooctanoate, select acrylic acid resin, sunflower oil, polymerized linseed oil, solvent-free alkyd resin, high chlorinated Polyethylene resin, pigment, vanadium isooctanoate and cobalt isooctanoate raw materials, spare;

[0065] Acrylic resin is a solid acrylic resin American Rohm and Haas B-72 thermoplastic solid acrylic resin.

[0066] The sunflower oil is semi-dry sunflower oil, and the mass content of water is 0-0.2%.

[0067] The solvent-free alkyd resin is BD250 super ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a hot-melt waterproof paint for enhancing the waterproofness of the circumference of a composite wood floor and a preparation method thereof. The invention is characterized in that the waterproof colored solid paint is prepared from the following raw materials in parts by weight: 100 parts of acrylic resin, 1-10 parts of sunflower seed oil, 1-10 parts of polymer flax oil, 1-10 parts of solvent-free alkide resin, 1-10 parts of high chlorinated polyethylene resin, 1-10 parts of pigment, 0.01-0.5 part of vanadium isooctoate and 0.01-0.5 part of cobalt isooctoate. The invention has the characteristics of good waterproof effect, beautiful appearance and environment friendliness, and the hot-melt waterproof coating obtained at the circumference of the enhanced composite wood floor has the advantages of smoothness, flatness, uniform color and no odor and looks extremely attractive.

Description

technical field [0001] The invention relates to a hot-melt waterproof paint for strengthening the waterproofing of the periphery of a composite wood floor and a preparation method thereof. Background technique [0002] Hot-melt paint (hot-melt waterproof paint) is an environmentally friendly green paint that does not contain organic solvents. It exists in a solid form. After the paint is heated and melted, it is applied to the surface of the substrate while it is hot, and the temperature is cured to form a film. Hot-melt coatings differ from both traditional solvent-based coatings and modern powder coatings. Compared with solvent-based coatings, hot-melt coatings have unique advantages such as no solvent pollution, convenient and fast coating, fast cooling and curing of the coating film, and excellent performance. Compared with powder coatings, hot-melt coatings directly heat and melt the coatings into a fluid, and then apply them to the surface of an unheated substrate to ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/00C09D167/08C09D123/28C09D7/12C09D5/00C09D5/29E04F15/02
Inventor 舒波
Owner 湖北万利环保节能材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com