Quick wax spray rubber composition and preparation method thereof

A rubber composition and rapid technology, which is applied in the field of rapid wax spray rubber composition and its preparation, can solve the problems of paraffin not being able to flow freely, difficulty in spraying out paraffin, spraying out, etc., to achieve good protection against ozone aging and reduce friction coefficient Effect

Inactive Publication Date: 2011-01-05
SHANGHAI ZHONGLI AUTO PARTS
View PDF5 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, it is difficult for many domestic rubber product manufacturers to quickly spray out the paraffin from the inside of the rubber, forming a thick layer of paraffin on the surface of the rubber, and some even increase the amount of paraffin greatly. purpose, some even have difficulty spraying out paraffin for a long time
[0004] Nowadays, there are many kinds of paraffin wax in our country, which may also lead to rubber technicians not choosing the type of paraffin wax or its combination well, resulting in the paraffin wax not being able to flow freely and quickly from the inside of the rubber.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Quick wax spray rubber composition and preparation method thereof
  • Quick wax spray rubber composition and preparation method thereof
  • Quick wax spray rubber composition and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] The invention provides a kind of quick wax spray rubber composition, is made up of following components in parts by weight:

[0021]

[0022] Its processing technology is as follows:

[0023] Step 1, one stage of rubber mixing:

[0024] Step 1.1, kneading the above-mentioned rubber by weight in an internal mixer for 20 seconds to soften, and controlling the temperature of the internal mixing chamber at 60°C;

[0025] Step 1.2, adding the active agent, anti-aging agent, processing aid and paraffin wax in the above parts by weight and kneading in the internal mixer, the kneading time is 4min;

[0026] Step 1.3. Pour the reinforcing agent and plasticizer in the above parts by weight into the internal mixer and continue kneading. After 5 minutes of kneading, transfer to the open mixer for thin pass 3 times, and then thicken it. Cutting knife 2 times each;

[0027] Step 2. Parking: put the mixed rubber completed through the above steps into a constant temperature room...

Embodiment 2

[0033] The invention provides a kind of quick wax spray rubber composition, is made up of following components in parts by weight:

[0034]

[0035] Its processing technology is as follows:

[0036] Step 1, one stage of rubber mixing:

[0037] Step 1.1, kneading the above-mentioned parts by weight of the plasticized rubber in an internal mixer for 40 seconds to soften, and controlling the temperature of the internal mixing chamber at 100°C;

[0038] Step 1.2, adding the active agent, anti-aging agent, processing aid and paraffin wax in the above parts by weight and kneading in the internal mixer, the kneading time is 6min;

[0039] Step 1.3. Pour the reinforcing agent and plasticizer in the above weight parts into the internal mixer and continue kneading. After the kneading time is 8 minutes, transfer it to the open mixer for thin pass 3 times, and then thicken it. Cutting knife 2 times each;

[0040] Step 2. Parking: put the mixed rubber completed through the above step...

Embodiment 3

[0045] A kind of rubber composition of automobile chassis with self-lubricating stabilizer bushing products, containing the following components in parts by weight:

[0046]

[0047] Its processing technology is as follows:

[0048] Step 1, one stage of rubber mixing:

[0049] Step 1.1, kneading the above-mentioned parts by weight of the plasticized rubber in an internal mixer for 30 seconds to soften, and controlling the temperature of the internal mixing chamber at 100°C;

[0050] Step 1.2, adding the active agent, anti-aging agent, processing aid and paraffin wax in the above parts by weight and kneading in the internal mixer, the kneading time is 6min;

[0051] Step 1.3. Pour the reinforcing agent and plasticizer in the above weight parts into the internal mixer and continue kneading. After the kneading time is 8 minutes, transfer it to the open mixer for thin pass 3 times, and then thicken it. Cutting knife 2 times each;

[0052] Step 2. Parking: put the mixed rubbe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a quick wax spray rubber composition. The composition is characterized by comprising the following components in parts by weight: 100 parts of rubber, 4-6 parts of organic active agent, 0.5-1.5 parts of inorganic active agent, 2-4 parts of anti-aging agent, 5-8 parts of paraffin, 2-3 parts of processing aid, 20-80 parts of reinforcing agent, 5-15 parts of plasticizer, 1.8-2.5 parts of accelerator and 1.5-2 parts of vulcanizing agent. The invention also provides a preparation method of the quick wax spray rubber composition. The method is characterized by comprising the following steps of: making rubber and parking; sulphurating; and finally, parking. In the invention, a paraffin layer can be quickly adhered on the surface of the rubber within a short time, and the paraffin can even be quickly sprayed out of the interior of a rubber product in a slightly dynamic state so as to better prevent aging by ozone, clear up friction abnormal sound on the surface of the rubber, keep a self-lubricating function and reduce the friction coefficient, and moreover, the anti-aging agent cannot be taken out of the surface so as to avoid blushing and over quick aging.

Description

technical field [0001] The invention relates to a formula of rapid wax spraying of a rubber composition and a processing technology thereof. Background technique [0002] Many foreign rubber products, such as shock absorbing products, stabilizer bar bushings, rubber pads and other products, have a thick protective paraffin layer on the surface. Lubricating function, reducing the coefficient of friction, and does not take the anti-aging agent out of the surface to cause blooming and premature aging. [0003] At present, it is difficult for many domestic rubber product manufacturers to quickly spray out the paraffin from the inside of the rubber, forming a thick layer of paraffin on the surface of the rubber, and some even increase the amount of paraffin greatly. For some purposes, it is even difficult to spray out paraffin for a long time. [0004] Nowadays, there are many kinds of paraffin wax in our country, which may also cause rubber technicians to choose the type of pa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L7/00C08L9/00C08K13/02C08K5/01B29B7/28
Inventor 李庆团
Owner SHANGHAI ZHONGLI AUTO PARTS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap