Imitation natural stone sheet and making process thereof

A technology imitating natural stone and manufacturing process, which is applied in the field of wall insulation and decoration materials, can solve the problems of fast fading of pigments, serious flow lines, single color tone of molded sheets, etc., and achieve good flame retardant effect, high strength and high hardness Effect

Inactive Publication Date: 2010-09-08
山东中南集团有限公司
View PDF4 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide an imitation natural stone sheet and its production process to solve the problem of single color tone of the molded sheet in the prior art, uneven flow of inner coloring under high temperature and high pressure, serious flow lines, discoloration, flowering, and fading of the existing technology. Yellow: prone to pinholes, dents, few varieties of designs and colors, single product, poor UV resistance, fast pigment fading, not aging resistance, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0012] Taking the production of 1,000 kg of molded sheets for imitation granite exterior wall panels as an example, the raw materials are first to use high-temperature resistant resin, increase the resin content by 20%, second, reduce the content of shrinkage agent by 20%, and third, increase the anti-ultraviolet absorber, Antioxidant, the third is to reduce the original main filler calcium powder by 75%, and add aluminum hydroxide, 60-mesh natural colored stone particles and 15-mesh real stone particles. The raw material formula and weight ratio are: resin 230kg, low shrinkage agent 90kg, anti-ultraviolet absorber 2kg, antioxidant 1.4kg, dispersant 9kg, calcium powder 100kg, aluminum hydroxide 105kg, natural colored stone particles 390kg, glass fiber 66kg , Release agent 6kg, magnesium oxide 3.5kg, curing agent 2,6kg. Its preparation process is as follows:

[0013] 1. Preparation of low-shrinkage agent; put polystyrene, antioxidant, and anti-ultraviolet absorber into styrene...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an imitation natural stone SMC / BMC sheet and a making process thereof, relating to a thermal insulating decoration material for a wall. Heat-resistant resin is adopted for the imitation natural sheet to increase the resin content, reduces the shrinking agent content, increases the ultraviolet-resistant absorbent and antioxidant, reduces calcium powder, and increases the aluminum hydroxide, natural color stone particles and real stone particles. The components of the raw material comprises resin, low shrinking agent, ultraviolet-resistant absorbent, antioxidant, dispersant, calcium powder, aluminum hydroxide, natural color stone particles, glass fiber, release agent, magnesium oxide and curing agent. The steps of confecting the low shrinking agent, mixing, adding filler, online mixing and thickening are performed to obtain the product. The invention can produce imitation stones and granite products of various colors and patterns and external wall panels of various veined patterns and tones as well as internal wall decoration board. The invention has the characteristics of aging resistance, no color change, great strength, high hardness, good flame retardant effect and the like, and is an excellent product for both indoor and external wall decoration.

Description

technical field [0001] The invention relates to a wall thermal insulation decoration material. Background technique [0002] At present, the SMC molding process and BMC injection molding process in composite materials are composed of polymer resin, glass fiber, calcium powder, shrinkage agent, thickener and so on. Due to the existing formula ratio, the tone of the molded sheet in actual production is single. The inner coloring has problems such as uneven flow direction and serious flow lines under high temperature and high pressure. The main color is original white, and there are few varieties of designs and colors, which plague the development of products in the field of building materials. In order to open up the market and increase varieties, some companies have changed the single pigment paste into small granules, etc., but the thermal variation coefficient of calcium powder and glass fiber is different, and problems such as pinholes and depressions are prone to occur a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/02
Inventor 苏跃峰
Owner 山东中南集团有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products