AM (Acrylamide)/DMDAAC (Dimethyl Diallyl Ammonium Chloride)/cyclodextrin polymer filtrate reducer and preparation method thereof

A technology of allyl cyclodextrin and fluid loss control agent, which is applied in the direction of drilling compositions, chemical instruments and methods, etc., can solve problems such as well wall instability and increased water loss, and achieve excellent fluid loss control effects , mild reaction conditions, simple and feasible preparation method

Inactive Publication Date: 2012-10-17
SOUTHWEST PETROLEUM UNIV
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a kind of AM / DMDAAC / allyl cyclodextrin polymer fluid loss reducer and its preparation method in order to solve the problem of oil and gas wells with a large increase in water loss at the bottom of the well under high temperature conditions, resulting in instability of the well wall

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • AM (Acrylamide)/DMDAAC (Dimethyl Diallyl Ammonium Chloride)/cyclodextrin polymer filtrate reducer and preparation method thereof
  • AM (Acrylamide)/DMDAAC (Dimethyl Diallyl Ammonium Chloride)/cyclodextrin polymer filtrate reducer and preparation method thereof
  • AM (Acrylamide)/DMDAAC (Dimethyl Diallyl Ammonium Chloride)/cyclodextrin polymer filtrate reducer and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0013] The preparation method of example 1 AM / DMDAAC / allyl cyclodextrin polymer fluid loss reducer

[0014] Add 50 mL of the prepared aqueous solution of 0.01 g / mL allyl cyclodextrin into a 150 mL beaker, then add 7 mL of the aqueous solution of 0.5 g / mL acrylamide (AM) and 0.5 g / mL of dimethyl dimethicone Allyl ammonium chloride (DMDAAC) aqueous solution 3mL. Then add 1 mL of disodium ethylenediaminetetraacetic acid (EDTA) chelating agent with a concentration of 0.5 g / mL, 1 mL of potassium persulfate oxidant with a concentration of 0.5 g / mL and sodium bisulfite reducing agent with a concentration of 0.5 g / mL. mL. Fully stir and mix evenly on a magnetic stirrer, then fill with nitrogen gas for 40 minutes to remove oxygen, and react at 45°C for 7 hours to obtain a transparent colloidal AM / DMDAAC / allyl cyclodextrin polymer.

[0015] Measure the intrinsic viscosity of AM / DMDAAC / allyl cyclodextrin polymer according to the standard described in GB12005.1-89, and then measure the ...

example 2A

[0016] The fluid loss effect of example 2A M / DMDAAC / allyl cyclodextrin polymer

[0017] In order to evaluate the fluid loss reduction effect of AM / DMDAAC / allyl cyclodextrin polymer at higher temperature, the base slurry was prepared according to the national standard GB / T16783-1997. That is, add 0.6g of anhydrous sodium carbonate, 12g of bentonite and 9g of evaluation soil to 300mL of ion-free water stirred at high speed, continue to stir for 30 minutes, and then keep it sealed for 24 hours to obtain a freshwater base slurry. Similarly, add 0.9g of anhydrous sodium carbonate, 18g of bentonite, 30g of evaluative clay and 90g of sodium chloride into 300mL of ion-free water stirred at high speed, continue to stir for 30min and then keep it sealed for 24h to obtain a saturated brine base slurry.

[0018] Table 1 shows the fluid loss control effect of AM / DMDAAC / allyl cyclodextrin polymer. It can be seen from Table 1 that the polymer of the present invention has good temperature re...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an AM (Acrylamide) / DMDAAC (Dimethyl Diallyl Ammonium Chloride) / cyclodextrin polymer filtrate reducer used in petroleum and gas drilling fluid and a preparation method thereof. The invention can solve the technical problems that a well wall is not stable as water loss increases at the pit bottom under the condition of high temperature, and the like. The AM / DMDAAC / cyclodextrin polymer filtrate reducer is characterized by comprising three monomers of AM, DMDAAC and cyclodextrin; the preparation method comprises the following steps of: firstly adding the AM and the DMDAACinto an allyl cyclodextrin water solution according to the mol ratio among the allyl cyclodextrin water solution, the AM and the DMDAAC of 69.2-84.2:30-15:0.8 in sequence; then adding a chelating agent, an oxidant and a reducing agent in sequence; finally evenly mixing, then injecting nitrogen for 20-40min and deoxidizing, and reacting at 30-50 DEG C for 6-8h to obtain the AM / DMDAAC / cyclodextrin polymer filtrate reducer. The preparation method of the polymer is simple, convenient and available and mild in reaction conditions; and the polymer has good filtrate reduction effect in the drilling fluid, is resistant to temperature up to more than 250 DEG C and used in the petroleum and gas drilling fluid.

Description

technical field [0001] The invention relates to an AM / DMDAAC / allyl cyclodextrin polymer fluid loss reducer used in drilling fluids in the petroleum and natural gas industry and a preparation method thereof. Background technique [0002] Reservoir damage during oil and gas well drilling is an important issue in the petroleum industry. In order to overcome the problem of oil layer damage during drilling, the petroleum industry uses various fluid loss control agents during drilling (Yan Siming, Liao Li, Long Xueli. Laboratory research on starch graft copolymer anti-temperature fluid loss control agent SALS, Oilfield Chemistry, 2009, 26(2) 118-120). However, when the drilling fluid is under high temperature conditions at the bottom of the hole, the performance of the fluid loss control agent is weakened. The invention provides a drilling fluid fluid loss reducer that can be used under high temperature conditions, and solves technical problems such as a large increase in water ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09K8/035C08F220/56
Inventor 邹长军王猛雷英田强张菊
Owner SOUTHWEST PETROLEUM UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com