Composite material capable of releasing volatile substances persistently and preparation method thereof

A technology for volatile substances and composite materials, which is applied in the field of composite materials that can permanently release volatile substances and their preparation, can solve the problems of complex production, inability to decompose polymer materials, and high cost, and achieves a simple production method and good mosquito repellent. Effect, effect of low production cost

Inactive Publication Date: 2010-08-11
漳州市奈特新型建材有限责任公司
View PDF6 Cites 42 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Among the volatile substances, essential oils can give off a pleasant smell, but the simple use of essential oils is easy to volatilize, and the fragrance cannot last; similarly, the active ingredients of repelling (killing) insects also have the problem of being easy to volatilize and not lasting in efficacy
In order to prolong the action time of essential oils and insect repelling (killing) active ingredients, the existing method is to use special polymer material carriers to reduce the volatilization of volatile substances, such as making mosquito repellent patches and mosquito repellent crystal jelly, etc., but its Not only is the production complicated and the cost is high, but the polymer materials used in large quantities cannot be directly decomposed in the natural state

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Take water-based bisphenol A epoxy resin E51 (water-based resin) 20g, wood flour (natural fiber) 100g, diethylenetriamine (water-soluble hardener) 5g, polyethylene glycol (phase transfer catalyst) by weight 10g, 100g of clay powder (filler), 1g of Mielin (anthelmintic), 5g of jasmine essence (essence) and 200g of water.

[0028] Among them, the water-based bisphenol A epoxy resin E51 is obtained in the following manner: get 15g of bisphenol A epoxy resin E51 and 5g of 4,4-azobis(4-cyanovaleric acid) as raw materials, and prepare the bisphenol A ring Oxygen resin E51 and 4,4-azobis(4-cyanovaleric acid) were mixed in a reaction kettle, and obtained after pressurized reaction at 150° C. for 1 hour.

[0029] Add the above water, water-based bisphenol A epoxy resin E51 and diethylene triamine into the stirring tank, disperse the water-based bisphenol A epoxy resin E51 and diethylene triamine in water to form an emulsion, and then add The wood powder, polyethylene glycol and...

Embodiment 2

[0034]Take water-based bisphenol A epoxy resin E20 (water-based resin) 20g, wood flour (natural fiber) 100g, diethylenetriamine (water-soluble hardener) 5g, polyethylene glycol (phase transfer catalyst) by weight 10g, clay powder (filler) 100g, N, N-diethyl m-benzamide (insect repellent) 1g, jasmine essence (essence) 1g and water 200g.

[0035] Among them, water-based bisphenol A epoxy resin E20 is obtained by the following method: get bisphenol A epoxy resin E20 19g and 4,4-azobis (4-cyanovaleric acid) 1g raw materials, bisphenol A ring Oxygen resin E20 and 4,4-azobis(4-cyanovaleric acid) were mixed in a reaction kettle, and obtained after pressurized reaction at 150°C for 1 hour.

[0036] Add the above water, water-based bisphenol A epoxy resin E20 and diethylene triamine into the stirring tank, disperse the water-based bisphenol A epoxy resin E20 and diethylene triamine in water to form an emulsion, and then add The wood powder, polyethylene glycol and clay powder are mixe...

Embodiment 3

[0041] Take water-based bisphenol A epoxy resin E44 (water-based resin) 20g, wood flour (natural fiber) 100g, diethylenetriamine (water-soluble hardener) 5g, polyethylene glycol (phase transfer catalyst) by weight 10g, clay powder (filler) 100g, menthol (anthelmintic) 1g, jasmine essence (essence) 5g and water 200g.

[0042] Among them, the water-based bisphenol A epoxy resin E44 is obtained by the following method: get bisphenol A epoxy resin E44 15g and 4,4-azobis (4-cyanovaleric acid) 5g raw materials, bisphenol A ring Oxygen resin E44 and 4,4-azobis(4-cyanovaleric acid) were mixed in a reaction kettle, and obtained after pressurized reaction at 150°C for 1 hour.

[0043] Add the above water, water-based bisphenol A epoxy resin E44 and diethylene triamine into the stirring tank, disperse the water-based bisphenol A epoxy resin E44 and diethylene triamine in water to form an emulsion, and then add The wood powder, polyethylene glycol and clay powder are mixed evenly, mixed ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a composite material capable of releasing volatile substances persistently and a preparation method thereof. The composite material is prepared from the following main components in parts by weight: 10-50 parts of aqueous resin, 50-180 parts of natural fiber, 3-8 parts of water-solubility hardening agent, 8-15 parts of phase transfer catalyst, 50-150 parts of filler, 2-9 parts of volatile substance and 100-200 parts of water. The invention uses the natural fiber and common high molecular materials as carriers of the volatile substances, has simple preparation and low production cost and can be decomposed directly in a natural state.

Description

technical field [0001] The invention relates to a composite material and a preparation method thereof, in particular to a composite material capable of sustainably releasing volatile substances and a preparation method thereof. Background technique [0002] Among the volatile substances, essential oils can give off a pleasant smell, but the simple use of essential oils is easy to volatilize, and the fragrance cannot last; similarly, the active ingredients of repelling (killing) insects also have the problem of easy volatilization and long-lasting drug effect. In order to prolong the action time of essential oils and insect repelling (killing) active ingredients, the existing method is to use special polymer material carriers to reduce the volatilization of volatile substances, such as making mosquito repellent patches and mosquito repellent crystal jelly, etc., but its Not only is the production complicated and the cost is high, but also the polymer materials used in large q...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L97/02C08L1/02C08L61/06C08L33/00C08L75/04C08L63/00C08L63/02C08L63/04C08K13/02C08K5/17C08K5/43C08K3/34
Inventor 阮韶铭林镇辉阮榆
Owner 漳州市奈特新型建材有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More