Water-based solid lubricant

A lubricant and water-based technology, applied in the field of water-based solid lubricants, can solve problems such as volatile, non-wear-resistant, and high toxicity, and achieve the effects of low surface energy, strong adhesion, and excellent friction performance

Inactive Publication Date: 2010-07-07
NEW MATERIAL INST OF SHANDONG ACADEMY OF SCI +1
View PDF2 Cites 29 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It overcomes the problem of high toxicity, volatility and wear resistance of organic solvents in previous solid lubricating materials, and has a good application prospect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] An aqueous dispersion solid lubricant, the weight ratio of its raw materials is: aqueous polyamide-imide solution 100g, polytetrafluoroethylene emulsion 30g, graphite powder 20g, molybdenum disulfide powder 5g, zinc oxide powder 1g, carbon Nanotube 10g, wherein graphite powder, molybdenum disulfide powder, zinc oxide powder its fineness is 1 micron; Carbon nanotube is industrial grade single-walled carbon nanotube; Described aqueous polyamide-imide solution is commercially available An aqueous solution with a solid content of 25-35%; polytetrafluoroethylene emulsion is a commercially available aqueous solution with a solid content of 55-65%.

[0028] The preparation method is as follows: mix the aqueous polyamide-imide solution and the polytetrafluoroethylene emulsion according to the above dosage under high-speed stirring at 500rpm, and then disperse them in the mixed solution according to the proportion of the formula Graphite powder, molybdenum disulfide powder, zinc...

Embodiment 2

[0031] An aqueous dispersion solid lubricant, the weight ratio of its raw materials is: aqueous polyamide-imide solution 200g, polytetrafluoroethylene emulsion 100g, graphite powder 70g, molybdenum disulfide powder 40g, zinc oxide powder 1g, carbon 10g of nanotubes, wherein the fineness of graphite powder, molybdenum disulfide powder and zinc oxide powder is 1 micron. Carbon nanotubes are industrial-grade single-walled carbon nanotubes; the aqueous polyamide-imide solution is a commercially available aqueous solution with a solid content of 25-35%; polytetrafluoroethylene emulsion is a commercially available solid content of 55-65%. aqueous solution.

[0032] The preparation method is as follows: mix the water-based polyamide-imide solution and the polytetrafluoroethylene emulsion according to the above dosage under high-speed stirring at 400 rpm, and then disperse graphite powder in the mixed solution according to the proportion of the recipe under high-speed stirring at 400 ...

Embodiment 3

[0035] An aqueous dispersion solid lubricant, the weight ratio of its raw materials is: 150g of aqueous polyamide-imide solution, 40g of polytetrafluoroethylene emulsion, 30g of graphite powder, 60g of molybdenum disulfide powder, 1g of zinc oxide powder, carbon 30g of nanotubes, wherein the fineness of graphite powder, molybdenum disulfide powder and zinc oxide powder is 1 micron. Carbon nanotubes are industrial-grade single-walled carbon nanotubes; the aqueous polyamide-imide solution is a commercially available aqueous solution with a solid content of 25-35%; polytetrafluoroethylene emulsion is a commercially available solid content of 55-65%. aqueous solution.

[0036] The preparation method is as follows: mix the aqueous polyamide-imide solution and the polytetrafluoroethylene emulsion according to the above dosage under high-speed stirring at 300rpm, and then disperse graphite powder in the mixed solution in sequence according to the composition ratio under 300rpm high-spe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
friction coefficientaaaaaaaaaa
friction coefficientaaaaaaaaaa
friction coefficientaaaaaaaaaa
Login to View More

Abstract

The invention aims to provide a water-based dispersoid solid lubricant material and the preparation method thereof; wherein, the water-based dispersoid solid lubrication material can be used as solid lubrication material, has good filming and adhesive properties, anticorrosion and wear resistance, and adopts polyamide imide and PTFE as main adhesive material; the water-based solid lubricant is environmental protection, anticorrosive and wear resistant, has low friction coefficient and good high and low temperature resistance, overcomes the problems that the organic solvent of solid lubrication material in prior art has greater toxicity, easy volatilization and is not wear resistant so that the water-based solid lubricant has good application prospect.

Description

technical field [0001] The invention relates to the field of lubricants, in particular to a water-based solid lubricant. Background technique [0002] The lubrication mechanism of solid lubricating materials is not like liquid and colloidal lubricating materials that form some form of fluid or semi-fluid film on the friction interface to effectively lubricate, but mainly rely on the low shear characteristics of the material itself or its transfer film. Has excellent anti-wear and wear-reducing effects. As a new type of lubricating material, the performance of solid lubricating materials has greatly broken through the use limit of traditional materials. It provides strong technical support for friction and wear problems under typical special working conditions such as media, and also lays an important foundation for improving the stability and reliability of machinery. Now its application scope has shifted from aviation and aerospace military technology to automobiles. Mach...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C10M169/04C10M147/02C10M149/14C10M125/22C10M125/02C10M173/02C10N50/02
Inventor 律微波张利孟宪铎
Owner NEW MATERIAL INST OF SHANDONG ACADEMY OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com