Rubber wire sheath material and manufacturing method thereof

A sheath material and rubber technology, which is applied in the field of environmentally friendly rubber wire sheath materials and their manufacturing, can solve problems such as harming human health and polluting the environment, and achieve the effects of less pollution, low product toxicity and less precipitation.

Inactive Publication Date: 2010-06-16
佛山市顺德区凯华电器实业有限公司
View PDF0 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the above-mentioned stabilizers and flame retardants can improve the stability and flame retardancy of rubber materials, these additives contain a large amount of toxic substances, which will be precipitated during the use or combustion of electric wires, seriously polluting the environment and damaging human health

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rubber wire sheath material and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] The rubber wire sheath material of the present invention mainly includes chlorinated polyethylene rubber, flame retardant, filler, plasticizer, cross-linking assistant, peroxide cross-linking agent, stabilizer, active agent, reinforcing agent and coupling agent joint agent. The flame retardant is environmentally friendly antimony trioxide; the filler is superfine talc; the plasticizer is dioctyl adipate; the crosslinking aid is triallyl isocyanurate; peroxide crosslinking The agent is di-tert-butyl cumene peroxide; the stabilizer is calcium stearate; the active agent is activated magnesium oxide; the reinforcing agent is carbon black; and the coupling agent is aluminum-titanium composite coupling agent. The contents of the above components are 100 parts of chlorinated polyethylene rubber, 4 parts of environmentally friendly antimony trioxide, 60 parts of ultrafine talc, 15 parts of dioctyl adipate, and 2 parts of triallyl isocyanurate. parts, 2 parts of bis-tert-butyl ...

Embodiment 2

[0046] The rubber wire sheath material of the present invention mainly includes chlorinated polyethylene rubber, flame retardant, filler, plasticizer, cross-linking assistant, peroxide cross-linking agent, stabilizer, active agent, reinforcing agent and coupling agent joint agent. The flame retardant is environmentally friendly antimony trioxide; the filler is a mixture of superfine talc, calcium carbonate and clay; the plasticizer is dioctyl adipate; the crosslinking aid is triallyl isocyanuric acid ester; peroxide cross-linking agent is bis-tert-butyl cumene peroxide; stabilizer is calcium stearate; active agent is activated magnesium oxide; reinforcing agent is carbon black; coupling agent is aluminum-titanium composite couple joint agent. The contents of the above components are 100 parts of chlorinated polyethylene rubber, 8 parts of environmentally friendly antimony trioxide, 40 parts of ultrafine talc, 30 parts of calcium carbonate, 30 parts of clay, 30 parts of diocty...

Embodiment 3

[0055] The rubber wire sheath material of the present invention mainly includes chlorinated polyethylene rubber, flame retardant, filler, plasticizer, cross-linking assistant, peroxide cross-linking agent, stabilizer, active agent, reinforcing agent and coupling agent joint agent. The flame retardant is environmentally friendly antimony trioxide; the filler is a mixture of ultra-fine talc, calcium carbonate and clay; the plasticizer is dioctyl adipate; the cross-linking aid is triallyl isocyanurate acid ester; peroxide cross-linking agent is bis-tert-butyl cumene peroxide; stabilizer is calcium stearate; active agent is activated magnesium oxide; reinforcing agent is carbon black; coupling agent is aluminum-titanium composite coupling agent. The contents of the above components are 100 parts of chlorinated polyethylene rubber, 5 parts of environmentally friendly antimony trioxide, 30 parts of ultrafine talc, 20 parts of calcium carbonate, 20 parts of clay, 18 parts of dioctyl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a rubber wire sheath material which is characterized in that the wire insulating material comprises the following components in parts by weight: 100 parts of chlorinated polyethylene rubber, 4-8 parts of flame retardant, 60-100 parts of filler, 15-30 parts of plasticizer, 2-5 parts of cross-linking additive, 2-5 parts of peroxide crosslinking agent, 3-7 parts of stabilizer, 5-10 parts of active agent, 5-10 parts of reinforcing agent and 1-5 parts of coupling agent. The rubber wire sheath material has few toxic substances, good environmental protection performance and strong safety.

Description

technical field [0001] The invention relates to a rubber wire sheath material and a manufacturing method thereof, in particular to an environment-friendly rubber wire sheath material and a manufacturing method thereof. Background technique [0002] With the gradual strengthening of environmental protection awareness, people's requirements for the environmental performance of electrical accessories (such as wire sheaths, etc.) are getting higher and higher. The environmental protection performance is mainly aimed at the content of toxic and harmful substances in the product. The above-mentioned harmful substances include lead, mercury, cadmium, hexavalent chromium, polybrominated biphenyls and polybrominated diphenyl ethers. The current rubber wire sheath is generally produced by natural rubber, chlorinated polyethylene material and EPDM rubber. Affected by the performance of the rubber material itself, stabilizers and flame retardants need to be added in the production proc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/28C08K13/02C08K3/22C08K5/11C08K5/098H01B3/28H01B7/295
Inventor 麦志荣
Owner 佛山市顺德区凯华电器实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap