Method for manufacturing bright aluminum alloy welding wire

A technology of aluminum alloy welding wire and manufacturing method, which is applied in the directions of manufacturing tools, welding media, welding equipment, etc., can solve the problems of rising production cost of aluminum alloy welding wire, affecting the plasticity of welding wire process, increasing the probability of wire breakage, etc., so as to prevent surface oxidation, The effect of improving the plasticity of the welding wire process and increasing the production speed

Inactive Publication Date: 2010-06-16
ZHEJIANG DONGQING HI TECH WELDING WIRES
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the annealing of the ordinary furnace annealing, the cooling is slow during the annealing process. On the one hand, since aluminum and magnesium are active metals, the surface is oxidized normally when cooled in the air. The existing means eliminate the oxidation on the surface of the welding wire by scraping film, and scraping the surface of the welding wire will produce a large amount of aluminum alloy debris, which will affect the yield, which will not only increase the production cost of aluminum alloy welding wire, but also reduce the production speed
On the other hand, normal cooling in air is also prone to precipitation of hard and brittle phases of high-magnesium aluminum alloys, which affects the alloy structure, affects the plasticity of the welding wire process, and increases the probability of wire breakage during welding

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0019] The manufacturing method of the bright aluminum alloy welding wire of the present invention, as in the existing continuous casting and rolling process, scrapes the surface of the cast blank to ensure the product quality of the welding wire. It is very necessary to scrape the surface of the welding wire blank, because there are a large number of oxide films, inclusions, segregation and other defects on the surface of the high-magnesium aluminum alloy wire wool produced by continuous casting and rolling. cannot eliminate its defects.

[0020] The manufacturing method of the bright aluminum alloy welding wire of the present invention includes the steps of batching-melting-casting-extrusion-drawing-annealing-cleaning.

[0021] 1. Ingredients: The amount of new aluminum is not less than 50%, such as 60%, 70%, 75%. Mg is added in the form of pure metal, Ti, Mn and Cr are added in the form of intermediate alloys, and trace protective elements are added to prevent excessive bu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for manufacturing a bright aluminum alloy welding wire, which comprises the steps of burdening, smelting, casting, scraping, broaching, annealing and cleaning, wherein the annealing step is to, after heating a drawn wire to 300 to 490 DEG C for 30 and keeping the temperature for 90 minutes in a protective environment of inert gases, cool a drawn wire first with heavy wind and then with sprayed water when the temperature drops to 230 to 280 DEG C. The method has the characteristics that: 1, electrical heating strong circulation diversion is adopted, and strongly cooling annealing is performed under the protection of the inert gases, so that the surface oxidation of magnalium magnesium is stopped, and the scraping for eliminating an oxidation film on the surface of the welding wire after the annealing is left out; and 2, under the protection of the inert gases, the strongly cooling annealing can effectively prevent hard and brittle phases of high magnalium from being separating out, so that an alloy structure is improved, the quality and process plasticity of the welding wire are improved, and the probability of broken wires in the process of welding the welding wire is reduced.

Description

technical field [0001] The invention relates to an aluminum alloy welding wire and a manufacturing method thereof, and more particularly to a manufacturing method of a bright aluminum alloy welding wire. Background technique [0002] With the development of lightweight and high-speed railway transportation vehicles, aluminum alloy profiles and plates have gradually replaced steel plates or stainless steel plates for high-speed train carriages. For the corresponding long plates, especially the ultra-long aluminum alloy profiles, advanced advanced Automated welding. [0003] The current aluminum alloy welding wire is generally made of aluminum-magnesium alloy welding wire. The national standard for "aluminum and aluminum alloy welding wire" (GB / T10858- 2008) on page 3, the chemical composition of several types of aluminum alloy welding wires is disclosed, such as the chemical composition (mass fraction)% of the aluminum alloy welding wire with model SA15356 [chemical composit...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B23K35/40
Inventor 郑志荣张万金夏建奎王梅李春生潘洪波
Owner ZHEJIANG DONGQING HI TECH WELDING WIRES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products