Clad net cloth gluing and surface processing technology

A technology of surface treatment and surface treatment agent, which is applied in the field of sandwich cloth lamination and surface treatment technology, can solve the problem that the physical performance indicators of peel strength and tear strength are not as good as those of scratching, difficult to control production process conditions, and poor air tightness of products Good and other problems, to achieve the effect of improving surface self-cleaning and anti-fouling, low product cost, and scientific and reasonable production process

Inactive Publication Date: 2010-04-28
思嘉环保材料科技(上海)有限公司
View PDF5 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, most of the mesh fabrics on the market are produced by scraping or laminating alone. The products produced by these two production processes currently have certain defects. The physical performance indicators such as resilience are good, but the products produced by this process have poor airtightness, high formula cost, and difficult control of production process conditions
The cost of the product produced by laminating process is lower, and the appearance and variety are easy to replace, but its physical performance indicators such as peel strength and tear strength are not as good as those produced by coating and scraping.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Clad net cloth gluing and surface processing technology
  • Clad net cloth gluing and surface processing technology

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] The specific steps of the production process are:

[0023] (1) Paste pretreatment on the mesh cloth: use a coating machine to carry out PU paste or PVC paste dip coating treatment on the polyester mesh cloth, the raw material formula of the PVC paste is: EPVC 100PHR, and the K value of the EPVC is 63. DINP: 80PHR, liquid low-toxic barium zinc stabilizer 2PHR, solid low-toxic barium zinc stabilizer: 1PHR, P adhesion promoter: 4PHR; the preparation method of PVC paste is: mix EPVC, liquid plasticizer and other additives Soak in the container for 3 days to make it fully absorbed, stir with a high-speed mixer, use the friction and shear force between the material and the barrel wall and the material to fully mix and absorb, and 150 meshes before use Filtration through a filter screen; the PU paste is: according to the mass ratio: PU: ​​methyl ethyl ketone: white glue: bridging agent ratio = 100: 4: 10: 2; mixed and stirred by a mixer; the coating amount is 50 g / m 2 ;

[0...

Embodiment 2

[0036] The specific steps of the production process are:

[0037] (1) Paste pretreatment on the mesh cloth: use a coating machine to carry out PU paste or PVC paste dip coating treatment on the polyester mesh cloth, the raw material formula of the PVC paste is: EPVC 100 PHR, the K value of the EPVC For 63, DINP: 110PHR, liquid low-toxic barium zinc stabilizer 4PHR, solid low-toxic barium zinc stabilizer: 2PHR, P adhesion promoter: 6PHR; the preparation method of PVC paste is: mix EPVC, liquid plasticizer and other Soak the additive container for 5 days to make it fully absorbed, stir it with a high-speed mixer, and use the friction and shear force generated between the material and the barrel wall and the material to fully mix and absorb it. Before use, 150 The purpose filter is filtered; the PU paste is: according to the mass ratio: PU: ​​methyl ethyl ketone: white glue: bridging agent ratio = 100: 4: 10: 2; mixed and stirred by a mixer and prepared; the coating amount is 350...

Embodiment 3

[0050] The specific steps of the production process are:

[0051] (1) Paste pretreatment on the mesh cloth: use a coating machine to carry out PU paste or PVC paste dip coating treatment on the polyester mesh cloth, the raw material formula of the PVC paste is: EPVC 100 PHR, the K value of the EPVC 63, DINP: 100PHR, liquid low-toxic barium zinc stabilizer 3PHR, solid low-toxic barium zinc stabilizer: 1.50PHR, P adhesion promoter: 5PHR; the preparation method of PVC paste is: mix EPVC, liquid plasticizer and Soak the other additives in the container for 4 days to make them fully absorbed, stir them with a high-speed mixer, and use the friction and shear force between the material and the barrel wall and materials to fully mix and absorb them. 150-mesh filter screen; the PU paste is: according to the mass ratio: PU: ​​methyl ethyl ketone: white glue: bridging agent ratio = 100: 4: 10: 2; mixed and stirred by a mixer to prepare; coating amount 250 g / m 2 ;

[0052] (2) Mesh se...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a clad net cloth gluing and surface processing technology. A preparation of the clad net cloth comprises the steps of: previously impregnating polyester fiber net cloth by means of PU glue or PVC glue with a coating impregnating machine; laminating and gluing the double faces of the polyester fiber net cloth with a PVC thin film under high temperature by a gluing machine; and surface processing with surface processing agent after cooling and shaping. The technology combines the impregnating with a coating machine, the laminating and the gluing with the gluing machine, with the subsequent surface processing with the surface processing machine of the clad net cloth; is scientific and reasonable; can produce a product with good physical indexes such as peel strength and tear strength, and the like, as well as good air tightness; can greatly improve the surface self-cleaning and pollution-resistant performance, and the surface abrasion resistance and tear resistance; can prevent from photooxidation aging; can prolong the service life; and has low cost, good competitiveness and obvious economic benefit.

Description

technical field [0001] The invention belongs to the field of chemical materials, and more specifically relates to a bonding and surface treatment process of a sandwich cloth. Background technique [0002] At present, most of the sandwich fabrics on the market are produced by scraping or laminating alone. The products produced by these two production processes currently have certain defects. Physical performance indicators such as resilience are good, but the products produced by this process have poor airtightness, high formula cost, and difficult control of production process conditions. The cost of the products produced by the bonding process is low, and the appearance and variety are easy to replace, but its physical performance indicators such as peel strength and tear strength are not as good as those produced by coating and scratching. Contents of the invention [0003] The purpose of the present invention is to provide a bonding and surface treatment process for th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06N3/18B32B27/12B32B27/32B32B27/40B32B37/06B32B37/10
Inventor 张宏旺黄万能李如晓蒋石生
Owner 思嘉环保材料科技(上海)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com