Polyamide elastomer thermal shrinkable material, polyamide elastomer double-layer material and preparation methods

A polyamide elastomer, polyamide technology, which is applied in the field of preparation of the heat shrinkable material and the double-layer material, can solve the problems of poor oil resistance, chemical resistance, high temperature resistance, wear resistance, etc., and achieve flexural resistance. Good oil resistance, chemical solvent resistance, simple preparation method

Active Publication Date: 2010-01-20
CHANGYUAN ELECTRONICS DONGGUAN +3
View PDF0 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is to overcome the problems of existing conventional polyolefin heat-shrinkable materials such as low temperature resistance, poor oil resistance and chemical resistance, low strength, and non-abrasion resistance, and provide a high temperature resistance, oil resistance and chemical resistance. Polyamide elastomer heat-shrinkable material with high strength and simple wear-resistant preparation method, polyamide elastomer double-layer material made of the heat-shrinkable material, and preparation method of the heat-shrinkable material and the double-layer material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyamide elastomer thermal shrinkable material, polyamide elastomer double-layer material and preparation methods
  • Polyamide elastomer thermal shrinkable material, polyamide elastomer double-layer material and preparation methods

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0052] The preparation method of polyamide elastomer heat-shrinkable material of the present invention comprises the following steps:

[0053] Step 1: According to the relative weight ratio, 0-50 parts of halogen-containing flame retardant, 0-20 parts of flame retardant synergist, 0-3 parts of multifunctional acrylate reaction monomer, 0.5-6 parts of antioxidant, light 0-3 parts of stabilizer and 0-5 parts of color masterbatch are fully mixed at room temperature;

[0054] Step 2: Mix the material uniformly mixed in step 1 with the polyamide elastomer with a relative weight ratio of 100 parts in a twin-screw mixer in the temperature range of 150°C-250°C, then extrude the strands, water-cool, air-dry, cut grain;

[0055] Step 3: extruding the above-mentioned pellets into a tube at a temperature of 150°C-250°C;

[0056] Step 4: irradiate the above-mentioned pipes with gamma rays or electron accelerators, and the radiation dose is 80-250KGY;

[0057] Step 5: Then expand and str...

preparation Embodiment 1

[0062] Polyamide elastomer substrate (Vestamid E55-S1, PA12 elastomer, German Degussa company) 100Kg and tetrakis [3-(3,5,-di-tert-butyl-4-hydroxyphenyl) propionate] pentaerythritol ester (anti- Oxygen agent 1010) 6Kg, trimethylolpropane trimethacrylate (TMPTMA) 1.5Kg;

[0063] Mix evenly in a high-speed mixer at a speed of 60 to 120rpm, and extrude into transparent or translucent polyamide elastomer pipe semi-finished products after mixing by a twin-screw mixer at a temperature of 190°C. After the electron beam is irradiated with a dose of 150KGY, it is expanded by 4 times to become a heat-shrinkable tube.

[0064] Its shrinkage performance is shown in the following table: (shrink in a glycerin pool at 180°C for 3 minutes)

[0065]

preparation Embodiment 2

[0067] Polyamide elastomer substrate (Vestamid E47-S1, PA12 elastomer, German Degussa company) 100Kg and tetrakis [3-(3,5,-di-tert-butyl-4-hydroxyphenyl) propionate] pentaerythritol ester (anti- Oxygen agent 1010) 1Kg, trimethylolpropane trimethacrylate (TMPTMA) 3Kg, decabromodiphenylethane 20Kg, antimony trioxide 8Kg, color masterbatch 5Kg;

[0068] Mix well at a speed of 60-120rpm in a high-speed mixer. Then, at a temperature of 190° C., the strands are extruded after kneading by a twin-screw kneader, water-cooled, air-dried, and pelletized. It is then extruded into a tube, irradiated by an electron accelerator at 100KGY, and then expanded twice to become a heat-shrinkable tube. The measurements are as follows:

[0069]

[0070]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a polyamide (commonly called nylon) elastomer thermal shrinkable material which comprises the following components by weight part: 100 parts of polyamide elastomer, 0.5-6 parts of antioxidant, 0-50 parts of halogenated flame retardant, 0-20 parts of flame-retardant synergist, 0-3 parts of polyfunctional acrylic ester reaction monomer, 0-3 parts of light stabilizer and 0-5 parts of color master batch, wherein the polyamide material is a segmental type segmented copolymer which uses polyamide as hard segments and polyether as soft segments; and the antioxidant is one or a compound of more of an amine antioxidant, a phenol antioxidant and an ester antioxidant. The polyamide elastomer thermal shrinkable material has good thermal ageing resistance, high temperature resistance and oil resistivity and also has the characteristics of excellent mechanical property, strong toughness, good wear-resisting property and simple preparation method. The invention also provides a polyamide elastomer double-layer material made of the thermal shrinkable material and preparation methods of the two materials.

Description

technical field [0001] The invention relates to a radiation-crosslinked polyamide elastomer heat-shrinkable material, a polyamide elastomer double-layer material made of the material, and a preparation method of the heat-shrinkable material and the double-layer material. Background technique [0002] Heat-shrinkable materials are used in a wide range of applications, including insulation and protection of cables in aerospace, aviation, locomotives, and military industries. In specific use environments, such as places with high temperature requirements, high requirements for oil resistance and chemical resistance, and high requirements for mechanical strength and wear resistance, the effect of conventional polyolefin heat shrinkable materials is relatively poor, so it is necessary to develop special heat shrinkable materials. shrinkage materials and their products. Contents of the invention [0003] The technical problem to be solved by the present invention is to overcome...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L77/00C08K5/134B29C69/02B29C47/92B29C71/04B29C55/22B29C47/06C09J7/02C09J177/00C09J167/00B29C48/92
Inventor 刘军麦家星鲁尔兵文磊鲁雪莲
Owner CHANGYUAN ELECTRONICS DONGGUAN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com