Nano coating

A nano-coating and nano-powder technology, applied in the direction of anti-fouling/underwater coatings, coatings, paints containing biocides, etc., can solve the problem of not having weather resistance, color retention, gloss retention and aging resistance, and short service life , low scrub resistance and other issues, to achieve the effect of delicate hand feeling, extended service life and good construction performance

Active Publication Date: 2009-12-09
赵青山
View PDF0 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The scrub resistance of nano-coatings depends on the surface effect of nano-materials, and it shows scrub resistance on the coating. For ordinary latex paints, the scrub resistance is very low, generally only 1000-2000 times. Therefore, use The number of years is short and cannot meet people's requirements
[0005] General paint coatings do not have strong weather resistance, color retention, gloss retention and aging resistance. Therefore, the service life of the coating is short. Nanomaterials have a strong shielding effect on ultraviolet rays, which can greatly slow down the sunlight on the coating. The destruction of the layer makes the coating have stronger weather resistance, color retention, gloss retention and aging resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nano coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0076] A nano-coating, nano-composite slurry made of nano-silica, nano-titanium dioxide and nano-calcium carbonate water slurry and composite additives, and then adding fillers and various additives, mixing reaction, shearing emulsification, sanding in a reactor The nano-coating is prepared by machine grinding and dispersing, mixing in the paint kettle and filtering by the filter. The nano-powder formed by coating in the nano-coating has a particle size of 30-40 nanometers and an average particle size of 35 nanometers. It has a closed surface The surface microstructure of the end and lotus leaf, the shape of the nano powder is spherical, with a tap density of 0.15-0.5g / cm, 125-180m 2 / g specific surface area, the nano coating is composed of the following material components by weight percentage:

[0077] Deionized water 3.8%

[0078] Nano composite pulp 11%

[0079] Ethylene glycol 2.7%

[0080] Hydroxyethyl cellulose (concentration 2%) 5.5%

[0081] Film forming aid (commercially...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A nano coating is prepared by nano-composite size added with fillers and various auxiliary agents; wherein, the average grain size of the nano powder formed by covering in the nano coating is 35 nanometers; the spherical nano powder has ends with surfaces closed and lotus leaf-like surface microstructure; the nano powder also has tap density of 0.15-0.5g / cm and specific surface area of 125-180 / g; the nano coating comprises the following materials by weight percent: 3.8% of ionized water, 10-12% of nano size, 2.5-2.8% of glycol, 5.3-5.7% of hydroxyethyl cellulose, 1.4-1.7% of film forming auxiliary agent, 28-29% of titanium dioxide, 2-3% of calcined kaolin, 2-3% of heavy calcium carbonate, 39-40% of phenylethylene-propyl ethylene acid ester emulsion, 0.5-0.6% of propylene glycol, 0.1-0.2% of bactericide, 0.2-2% of thickener, 0.1% of defoamer, 0.27% of dispersant, 0.06% of wetting agent and 0.2% of pH value regulator. The coating is bactericidal, nontoxic, tasteless and resistant to 300000 times of washing.

Description

Technical field [0001] The invention relates to a wall decoration paint, in particular to an inorganic nano-level paint used for decorating the inner wall or the outer wall of a wall. Background technique [0002] At present, the wall coatings sold on the market in our country contain a large amount of organic solvents. Although some powder materials are inorganic powders, the material components used contain certain toxic pigments and fillers, which will cause certain problems in production and use. Pollution affects human health. [0003] The reason why the coating is not resistant to stains, dust, and dirt is mainly determined by the surface structure of the coating and the characteristics of the material. The coatings sold on the market are either hydrophobic or oleophobic, the former Good water resistance, but not resistant to oil stains; the latter has good resistance to oil stains, but not water resistant. For this reason, the double sparse structure made of nano-coating i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D125/14C09D7/12C09D5/14
Inventor 赵青山
Owner 赵青山
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products