Formulation of environment-friendly ceramic polymer composite material and preparation thereof

A composite material and polymer technology, which is applied in the formulation and preparation of environment-friendly porcelain-plastic polymer composite materials, can solve the problems of unstable physical and chemical properties, consumption of large forest resources, limited bearing capacity, etc., and achieve social benefits and The effect of obvious environmental protection significance, high economic added value, and stable flow ratio

Active Publication Date: 2009-11-18
SHANDONG HUAZHIYE NEW MATERIAL TECH CO LTD
View PDF0 Cites 28 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This type of material has limited environmental tolerance, is prone to cracking, warping and deformation, corrosion, and unstable physical and chemical properties.
On the other hand, both wood-plastic materials and logs will consume a lot of forest resources

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] An environment-friendly porcelain-plastic polymer composite material consists of the following components by weight:

[0027] Thermoplastic PE 60

[0028] Fly Ash 20

[0029] bamboo wood powder 20

[0030] Aluminate coupling 0.6

[0031] Polyethylene wax 0.45

[0032] Zinc stearate 0.15

[0033] Atactic polypropylene 0.5

[0034] Antioxidant 168 0.15

[0035] Antioxidant 1010 0.08

[0036] Anti-ultraviolet agent UV-531 0.15

[0037] Decabromane 3

[0038] Antimony silicon trioxide 2

[0039] ACR processing aid 0.7

[0040] Appropriate amount of pigment

[0041] A method for preparing an environment-friendly porcelain-plastic polymer composite material, the specific steps of which are:

[0042] (1) prepare raw materials by above-mentioned proportioning by weight;

[0043] (2) the ash is sieved to obtain a fineness of 300 mesh ash;

[0044] (3) ashes and bamboo wood powder are mixed;

[0045] (4) put ash material and bamboo wood powder into the high mixer a...

Embodiment 2

[0050] Thermoplastic PVC 50

[0051] Ceramic Gray 50

[0052] Aluminate coupling 0.8

[0053] Polyethylene wax 0.75

[0054] Zinc stearate 0.35

[0055] Atactic polypropylene 0.8

[0056] Antioxidant 168 0.14

[0057] Antioxidant 1010 0.07

[0058] Anti-ultraviolet agent UV-531 0.13

[0059] Decabromane 2

[0060] Antimony silicon trioxide 1

[0061] ACR processing aid 0.6

[0062] Appropriate amount of pigment

[0063] A method for preparing an environment-friendly porcelain-plastic polymer composite material, the specific steps are:

[0064] (1) Raw materials are prepared according to the above-mentioned proportioning by weight;

[0065] (2) Sieving the ashes to obtain the ashes with a particle size of 200 to 1200 mesh;

[0066] (3) Put the ashes into the high mixer for dehydration and drying treatment, so that the water content reaches 3‰;

[0067] (4) Put the aluminate coupling, polyethylene wax and random polypropylene into the high-mixer to fully mix the ash, ...

Embodiment 3

[0071] Thermoplastic PP 40

[0072] Brick and fly ash 60

[0073] Aluminate Coupling 1

[0074] Polyethylene wax 0.9

[0075] Calcium stearate 0.45

[0076] thermoplastic rubber 0.9

[0077] Antioxidant 168 0.12

[0078] Antioxidant 1010 0.06

[0079] Anti-ultraviolet agent UV-531 0.12

[0080] Decabromane 1.6

[0081] Antimony silicon trioxide 0.7

[0082] ACR processing aid 0.5

[0083] Appropriate amount of pigment

[0084] The preparation method of an environment-friendly porcelain-plastic polymer composite material is the same as that in Example 2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of building materials, an in particular relates to a formulation of an environment-friendly ceramic polymer composite material and a preparation thereof. The technical proposal is that the environment-friendly ceramic polymer composite material comprises thermoplastic plastics, bamboo powder, plasticizers, internal and external lubricants, cross-linking modifiers, bulking agents, fire retardants, pigments, and gray materials. The technical proposal is energy conservation and emission reduction and has the advantages that the materials are acid resistant and alkali resistant, the temperature sensitivity is low and the physical and chemical properties are superior. Various sectional materials prepared from the environment-friendly ceramic polymer composite material have the advantages of stable physical and chemical properties, high strength, no toxicity, tastelessness, acid and alkali resistance, and high and low temperature resistance; and after surface treatment, the sectional materials can generate woody feelings, and have high imitative degree and secondary processing properties of sawing, nailing, cutting or bolt fixing.

Description

technical field [0001] The invention belongs to the field of building materials, and in particular relates to an environment-friendly porcelain-plastic polymer composite material formula and a preparation method thereof. Background technique [0002] With the transformation of sludge treatment ideas at home and abroad, the technical ideas of sludge drying and incineration have been gradually unified. The industry has been in a state of contention about how to dispose of the solid waste formed after sludge incineration - "incineration ash". At the same time, the way out of the "fly ash" produced by various large, medium and small thermal power plants has not been effectively resolved. Waste scraps from various ceramic factories and waste from brick and tile factories are randomly piled up and dumped, causing serious damage to the environment. At present, most of the profiles and panels used in municipal administration, garden construction, building materials, home furnishin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L23/06C08L23/12C08K3/26
CPCC08L97/02C08K3/04C08K3/34C08L2205/03C08L27/06C04B26/06Y02W30/91C04B18/08C04B18/165C04B18/248C04B2103/54C04B2103/63C04B14/28C08L2666/26C08L23/12C08L91/08C08L101/00C08K13/02
Inventor 章建华徐月明
Owner SHANDONG HUAZHIYE NEW MATERIAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com