Bismuth titanate photocatalytic material with visible light response and preparation method thereof

A photocatalytic material, bismuth titanate technology, applied in the direction of catalyst activation/preparation, chemical instruments and methods, physical/chemical process catalysts, etc., to achieve the effects of environmental protection, simple preparation process, and low cost

Inactive Publication Date: 2009-11-11
SHANDONG UNIV
View PDF0 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Currently, with Bi 20 TiO 32 Bismuth titanate photocatalytic materials are mainly impure phases, due to Bi 20 TiO 32 metastability of the material, there is currently no information on the preparation of pure phase Bi 20 TiO 32 Reports on photocatalytic materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Bismuth titanate photocatalytic material with visible light response and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Preparation of bismuth titanate photocatalytic material with visible light response:

[0019] 1) Preparation of raw materials: Weigh the analytically pure TiO 2 and Bi 2 o 3 As a raw material, according to TiO 2 with Bi 2 o 3 The molar ratio of the mixture is 1:20 for batching, put the prepared raw materials into the mixer and mix evenly, the mixer speed is 200 rpm, and the mixing time is 2 hours;

[0020] 2) Heating reaction: put the mixture obtained in step 1) into a platinum crucible, then put the platinum crucible into a muffle furnace preheated to 900°C in advance, and react for 2 minutes;

[0021] 3) Quenching and cooling: take out the reacted platinum crucible and quickly put it into cold water for quenching, and grind the obtained sample finely in an agate mortar.

Embodiment 2

[0023] Preparation of bismuth titanate photocatalytic material with visible light response:

[0024] 1) Preparation of raw materials: Weigh the analytically pure TiO 2 and Bi 2 o 3 As a raw material, according to TiO 2 with Bi 2 o 3 The molar ratio of the mixture is 1:20 for batching, put the prepared raw materials into the mixer and mix evenly, the mixer speed is 200 rpm, and the mixing time is 2 hours;

[0025] 2) Heating reaction: put the mixture obtained in step 1) into a platinum crucible, then put the platinum crucible into a muffle furnace preheated to 900°C in advance, and react for 3 minutes;

[0026] 3) Quenching and cooling: take out the reacted platinum crucible and quickly put it into cold water for quenching, and grind the obtained sample finely in an agate mortar.

Embodiment 3

[0028] Preparation of bismuth titanate photocatalytic material with visible light response:

[0029] 1) Preparation of raw materials: Weigh the analytically pure TiO 2 and Bi 2 o 3 As a raw material, according to TiO 2 with Bi 2 o 3 The molar ratio of the mixture is 1:20 for batching, put the prepared raw materials into the mixer and mix evenly, the mixer speed is 200 rpm, and the mixing time is 2 hours;

[0030] 2) Heating reaction: put the mixture obtained in step 1) into a platinum crucible, then put the platinum crucible into a muffle furnace preheated to 1000°C in advance, and react for 3 minutes;

[0031] 3) Quenching and cooling: take out the reacted platinum crucible and quickly put it into cold water for quenching, and grind the obtained sample finely in an agate mortar.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a bismuth titanate photocatalytic material with visible light response, which is a pure phase material with a chemical formula of Bi20TiO32 and prepared by the steps of preparation of raw materials, heating reaction, and quenching and cooling. The material has the advantages of good photocatalytic activity, low cost, capability of recycling catalyst, simple method, easy large-scale production, and the like.

Description

technical field [0001] The invention relates to a photocatalytic material, in particular to a bismuth titanate photocatalytic material with visible light response and a preparation method thereof, belonging to the technical field of semiconductor materials. Background technique [0002] With the development of human society, the requirements for the environment are getting higher and higher, and environmental pollution is a problem that people need to solve urgently. Fujishima and Honda at TiO since 1972 2 Since hydrogen and oxygen are cracked under light on the electrode, semiconductor photocatalytic materials have aroused widespread interest among scientists in energy development and environmental governance. Among these semiconductor catalytic materials, TiO 2 It has become the most widely used photocatalytic material due to its advantages of non-toxicity, low price and good stability. However, due to TiO 2 It has a wide band gap (the anatase phase band gap is 3.2eV, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B01J23/18B01J21/06B01J37/00
Inventor 黄柏标程合锋张晓阳秦晓燕
Owner SHANDONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com