Deep punching stewing-resistant transparent aluminum lid gloss oil and preparation method thereof

A retort-resistant, transparent aluminum technology, applied in the field of coatings, can solve problems such as mild discoloration, water quality changes, and mild water stains

Active Publication Date: 2009-09-23
无锡市太湖防腐材料有限公司
View PDF0 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to overcome the above-mentioned deficiencies and provide a deep-drawing and cooking-resistant transparent aluminum cover varnish, which solves the problems of water quality changes after cooking in the current transparent aluminum cover varnish, such as slight water stains and slight discoloration. Reach deep drawing of 60mm (with paint) and 35mm (with primer and ink) and the aluminum cover has good cooking resistance, no discoloration, no loss of gloss, no water stains

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0070] According to the following formula and production method, the deep-drawing and cooking-resistant transparent aluminum cover varnish is produced, and the weight parts of the raw materials used are as follows:

[0071] Polyester resin (60% solid content) 70.76

[0072] Methylated melamine resin BIP303 1.0

[0073] Butylated benzomelamine resin BIP659 1.0

[0074] Blocked polyisocyanate TOLONATE D2SN 0.72

[0075] (50%) epoxy resin liquid 7.7

[0076] Acid catalyst 0.07

[0077] Auxiliary wax for paint 0.32

[0078] Leveling agent 0.15

[0079] Smoothing and flow agent 0.05

[0080] Anti-bake foaming aid 0.6

[0081] Anti-friction additive 0.10

[0082] Mixed solvent 16.83;

[0083] The mixed solvent is prepared by mixing the following raw materials in parts by weight:

[0084] High boiling point 150# solvent oil (Jiangsu Hualun) 52

[0085] Propylene glycol butyl ether 8

[0086] Propylene glycol methyl ether acetate 7

[0087] DBE 15

[0088] Isooctyl alcoh...

Embodiment 2

[0096] According to the production method described in Example 1, the deep-drawing and cooking-resistant transparent aluminum cover varnish is produced, and the weight parts of raw materials used are as follows:

[0097] Material name Proportion

[0098] Polyester resin 60% 70.85

[0099] BIP303 1.0

[0100] BIP659 1.64

[0101] (50%) epoxy resin solution 7.6

[0102] Acid catalyst 0.07

[0103] 731 wax 0.32

[0104] Leveling agent 0.20

[0105] LAP-10 anti-bake foaming aid 0.5

[0106] Anti-friction additive 0.10

[0107] Mixed solvent 16.92;

[0108] Wherein the mixed solvent is prepared by the following raw materials in parts by weight:

[0109] 150# high boiling point solvent oil 52

[0110] DBE 15

[0111] Isophorone 5

[0112] Diacetone Alcohol 0.7.

Embodiment 3

[0114] According to the production method described in Example 1, the deep-drawing and cooking-resistant transparent aluminum cover varnish is produced, and the weight parts of raw materials used are as follows:

[0115] Material name Proportion

[0116] Polyester resin 60% 70.8

[0117] BIP303 1.0

[0118] TOLONATE D2SN 2.0

[0119] (50%) epoxy resin solution 7.5

[0120] Acid catalyst 0.06

[0121] 731 wax 0.32

[0122] Leveling agent 0.15

[0123] TEGO Glide smoothing and flow agent 0.05

[0124] LAP-10 anti-bake foaming aid 0.5

[0125] Anti-friction additive 0.10

[0126] Mixed solvent 17.52;

[0127] Wherein the mixed solvent is prepared by the following raw materials in parts by weight:

[0128] 150# high boiling point solvent oil 52

[0129] DBE 15

[0130] Isophorone 5

[0131] Isooctyl alcohol 6

[0132] Propylene glycol butyl ether 8

[0133] Propylene glycol methyl ether acetate 7

[0134] Butanol 7.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to light industry aluminum and iron printing coating, in particular to deep punching stewing-resistant transparent aluminum lid gloss oil which is prepared by following steps: polyester resins is taken as basal materials, right amount of methyl etherified tripolycyanamide and butyl etherified benzoguanamine is taken as a cross linking agent, also right amount of closed type polymeric isocyanate and epoxide resins is taken as an additive in an auxiliary way, an auxiliary agent,is added, right amount of acid catalyst is induced, and reserved carboxyl of the basal materials and a small quantity of hydroxide radical are carried out cross linking solidifying reaction under set temperature and time with activated functional groups of epoxide resin carboxyl, a cross linking resin and the acid catalyst. The invention adopts the maximum basal materials-polyester resins, adopts the butyl etherified benzoguanamine, the closed type polymeric isocyanate and the polyester resins to be matched with the polyester resins to be used and has optimized mixture ratio among the composites, thereby reaching the reasonable cross linking density, reducing the internal stress and enhancing the stretchability resistance, the flexible property and the water and stewing resistant property.

Description

Technical field: [0001] The invention relates to coatings, especially aluminum and iron coatings for light industry printing. Background technique: [0002] With the development of glass bottled foreign wine, beverages and various medicinal wines and health wines in our country, the demand for bottle caps made of aluminum is increasing day by day. At present, there are nearly 200 aluminum bottle cap production plants in my country, with an annual design and production of more than 10 billion bottle caps. According to industry forecasts, the consumption of China's anti-theft bottle caps will grow at an annual rate of 10%. In 2010, the domestic market alone will require about 15 billion anti-theft bottle caps, and a large number of products will be supplied to the international market. In recent years, with the improvement of people's living standards, especially with the improvement of environmental protection laws and the laws and regulations of food, pharmaceutical and oth...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D167/00
Inventor 门启珠
Owner 无锡市太湖防腐材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com