Colored curable resin composition, colored pattern forming method, colored pattern, method for manufacturing color filter, liquid crystal display element

A technology of curable resin and coloring pattern, which is applied in the direction of optical components, photoplate making process of pattern surface, instruments, etc.

Inactive Publication Date: 2012-08-29
FUJIFILM CORP
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] On the other hand, although the technology of using a specific adhesive to control the uneven thickness of the coating film is also disclosed, there are still problems that cannot cope with high-speed coating slits. The problem of coating (for example, refer to JP-A-2002-20442

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Colored curable resin composition, colored pattern forming method, colored pattern, method for manufacturing color filter, liquid crystal display element
  • Colored curable resin composition, colored pattern forming method, colored pattern, method for manufacturing color filter, liquid crystal display element
  • Colored curable resin composition, colored pattern forming method, colored pattern, method for manufacturing color filter, liquid crystal display element

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0128] As the preparation method of titanium black, there is a method of heating and reducing the mixture of titanium dioxide and metallic titanium under a reducing atmosphere (Japanese Patent Application No. 49-5432). The method of reduction in reducing atmosphere (JP-A-57-205322), the method of reducing titanium dioxide or titanium hydroxide at high temperature in the presence of ammonia (JP-A-60-65069, JP-A-61-201610 ), a method of attaching a vanadium compound to titanium dioxide or titanium hydroxide and reducing it at high temperature in the presence of ammonia (JP-A-61-201610), etc., but these methods are not limited.

[0129] Examples of commercially available titanium black include titanium black 10S, 12S, 13R, 13M, and 13M-C manufactured by Mitsubishi Materials.

[0130] As examples of other black pigments, nigrosine, iron oxide-based black pigments, and three-color organic pigments of red, green, and blue can be mixed and used as black pigments.

[0131] In additio...

Embodiment 1

[0398] Components of the following compositions were mixed to prepare a pigment dispersion.

[0399] [Pigment dispersion]

[0400] ·Pigment (a)

[0401] C.I. Pigment Red 254 5 parts

[0402] C.I. Pigment Red 177 5 parts

[0403] ·Dispersion resin

[0404] Byk-161 by Bitsuku Chemi Co., Ltd. (active ingredient: 30 13.3 parts by mass%)

[0405] ·(b) Solvent

[0406] Propylene glycol monomethyl ether acetate 32.7 parts

[0407] In addition, the following components were mixed separately to prepare a transparent resist solution.

[0408] [Composition of transparent resist solution]

[0409] ・(c) Binder resin

[0410] 2.0 parts of acrylic resin (c1) represented by the following formula (6)

[0411] 2.0 parts of acrylic resin (c2) (A) shown in Table 1

[0412] ·(c3) Monomer

[0413] Dipentaerythritol hexaacrylate 4.0 parts

[0414] ·(d) Photopolymerization initiator

[0415] 0.4 parts of 2-(2-chlorophenyl)-4,5-diphenylimidazole dimer

[0416] 0.2 parts of 4,4'-bis(dieth...

Embodiment 2～4

[0447] Except having changed the binder resin (c2) in Example 1 into the compound shown in Table 2, it carried out similarly to Example 1, prepared the composition for coloring pattern formation, and evaluated it.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
acid valueaaaaaaaaaa
particle diameteraaaaaaaaaa
acid valueaaaaaaaaaa
Login to view more

Abstract

The invention provides a colored curable resin composition having good coating properties even in high speed coating situation. The colored curable resin composition includes (a) a color material, (b) a solvent, (c) at least two kinds of binder resins, (c) a photopolymerization initiator and (e) a surfactant, wherein at least two kinds of the binder resins are resins having 0.0005-0.0050 eq / g of a (meth)acryloyl group and having an acid number of 15-150 mgKOH / g. The invention also provides colored pattern forming method of using the colored curable resin composition, colored pattern, method for manufacturing color filter, color filter and liquid crystal display element.

Description

technical field [0001] The present invention relates to a colored curable resin composition, a colored pattern forming method, a colored pattern, a color filter manufacturing method, a color filter, and a liquid crystal display element. Background technique [0002] A color filter is a colored curable resin composition that contains a binder resin and / or a monomer, a photopolymerization initiator, and other components in a solvent dispersion composition of coloring materials such as organic pigments and inorganic pigments, and uses this The colored curable resin composition is produced by photolithography or the like. [0003] In recent years, in the application of liquid crystal display elements (LCD), there is a trend of expanding the use of color filters not only in monitors but also in televisions (TVs). Also gradually require a high degree of color characteristics. In addition, color filters with high color characteristics are also increasingly required for applicati...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): G03F7/032G03F7/028G02B5/20G02F1/1335
CPCG02B1/04G02B5/201G03F7/0007G03F7/027G03F7/028G03F7/038G03F7/105
Inventor 阿出川丰
Owner FUJIFILM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap