Preparation of fluorine-containing aqueous crackle lacquer and coating method thereof

A kind of water-based crack paint, water-based technology, applied in the field of art paint, can solve the problems of unfriendly, high volatile organic compound environment, complex construction and other problems, and achieve the effect of simple preparation process, low cost and convenient operation

Inactive Publication Date: 2009-06-24
JILIN UNIV
View PDF3 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

If a protective layer is applied on top of this topcoat, although it can improve the surface effect, it will require four or more coats and the application will be more complicated
CN100441645C discloses "a kind of nitro-crack paint and its preparation method and use conditions" although the effect is better than traditional crack paint, but the higher volatile organic compounds are not friendly to the environment,

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Prepare colored water-based primer: Add 30g of water to a 500mL beaker, then disperse 18g of iron red, 2g of titanium dioxide, 5g of 1250 mesh talc powder, 1g of bentonite, 4.8g of light calcium carbonate, 4g of precipitated barium sulfate, and Deqian DP511 Deqian Defom W-090 type defoamer 0.2g, Deqian Defom W-090 type defoamer 0.1g was added to the water, dispersed evenly with a mixer, and ground to a fineness of 40μm to obtain a water-based color paste, and then mixed with AB-EP-20 water-based epoxy resin emulsion 28g Mix, add 0.4g thickener WT-115, 0.5g film-forming aid TEXANOL, 1g propylene glycol, stir evenly, then add AB-HGA curing agent 5g, stir evenly to get the finished primer;

[0030] Preparation of colored water-based topcoat: Add 33g of water to a 500mL beaker, 5g of carbon black, 5g of 1250 mesh talc powder, 1g of bentonite, 2g of light calcium carbonate, 1g of precipitated barium sulfate, 1g of nano-zinc oxide, and 0.1g of DP511 dispersant , Add 0.1g of D...

Embodiment 2

[0033] Preparation of colorless water-based primer: Add 40g of water, 53g of AB-EP-37 water-based epoxy resin emulsion, 0.1g of Deqian WT-090 defoamer, 0.5g of TEXANOL film-forming aid, and Thickener 0.4g, propylene glycol 1g, disperse evenly with a mixer, and then add curing agent AB-HGA 5g to obtain a colorless water-based primer.

[0034] Preparation of water-based topcoat: add 18g of water to a 500mL beaker, then add 30g of titanium dioxide, 10g of 1250 mesh talc powder, 9.5g of precipitated barium sulfate, 0.5g of nano zinc oxide, 0.1g of Deqian DP511 dispersant, Deqian Defom W-090 type defoamer 0.1g, disperse evenly with a mixer, grind to a fineness of 40μm to obtain a water-based color paste, then mix with 30g of fluorine-containing resin emulsion A603, add WT-115 thickener 0.4g, TEXANOL after mixing 0.5 g of film-forming aid and 0.9 g of propylene glycol were stirred evenly to obtain a colored water-based finish paint.

[0035] After 20 minutes, spray the primer onto ...

Embodiment 3

[0037]Prepare colored water-based primer: Add 30g of water to a 500mL beaker, then add 18g of phthalocyanine green, 2g of titanium dioxide, 3g of 1250 mesh talc powder, 3g of bentonite, 3.8g of light calcium carbonate, 5g of precipitated barium sulfate, and Deqian DP511 Add 0.2g of dispersant and 0.1g of Deqian Defom W-090 defoamer into water, disperse evenly with a mixer, and grind to a fineness of 40μm to obtain a water-based color paste, which is then mixed with AB-EP-20 water-based epoxy resin emulsion Mix 30g, add 0.5g of WT-115 thickener, 0.4g of TEXANOL film-forming aid, 2g of propylene glycol, stir evenly, then add 4g of AB-HGA curing agent, stir evenly to get the finished primer;

[0038] Preparation of colored water-based topcoat: add 35g of water to a 500mL beaker, mix 4g of permanent violet, 4g of talc powder of 1250 mesh, 3g of bentonite, 1g of light calcium carbonate, 2g of precipitated barium sulfate, 1g of nano-zinc oxide, and 0.1 g of DP511 dispersant g, add 0...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a preparation of fluorine-containing water-based crackle paint and coating method thereof. The fluorine-containing water-based crackle paint is composed of water-based epoxy primer and water-based fluorine-containing finish paint. Paint, filler and auxiliary are added to a sand mill according to percentages by weight to be grinded to be less than or equal to 40 microns; epoxy resin is added for homogeneous mixing to constitute the water-based epoxy primer; paint, filler and auxiliary are added to water according to percentages by weight to be grinded to be less than or equal to 40 microns after stirring, and are then mixed with fluorine-containing resin emulsion to constitute the water-based fluorine-containing finish paint. The coating method is as follows: the water-based epoxy primer is brush-coated or spray-coated on a substrate, and the thickness of dry film of the water-based primer is controlled; after the surface of the dry film is dry, the water-based fluorine-containing finish paint is spray-coated on the epoxy primer. Compared with the prior art, the fluorine-containing water-based crackle paint has lower content of volatile organic compound, no pollution for the environment, no poison for operating staff, excellent coating performance, strong adhesive attraction, water logging resistance, scrub resistance, simple preparation technology, convenient operation and low cost.

Description

Technical field: [0001] The invention relates to an art paint, especially a fluorine-containing water-based paint, especially the preparation and coating method of the fluorine-containing water-based crack paint. Background technique: [0002] Crackle paint is a kind of art paint, which is made of nitrocellulose, pigments, fillers and solvents. In the formula, there are few film substances, many pigments and fillers, and the solvent is highly volatile. With common nitro varnish as bottom layer, also cover light with nitro varnish sometimes in order to protect cracked paint layer. Nitro dyes, which have -NO in the chromogenic system 2 A class of dyes, except for those containing nitro-NO 2 In addition, it usually contains -OH or -SO at the same time 3 H. Ruoamic acid is one of the earliest nitro dyes. There are not many varieties, mainly acid dyes, yellow dyes, and a few disperse dyes. [0003] Crackle paint is mainly used for artworks and handicrafts, and is also used ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D127/12C09D5/28B05D7/24B05D1/36B05D3/02
Inventor 王洪艳赵永超崔学军王建刚张巧云
Owner JILIN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap