Melamine decorative veneer and preparation method thereof

A technology for melamine and decorative panels, applied in the field of decorative materials, can solve the problems of low activity, non-uniform resin, low brightness of melamine decorative panels, etc., and achieves the effect of enhancing molecular activity, easy and reasonable curing state

Active Publication Date: 2011-03-30
QUANYOU FURNITURE
View PDF0 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the low activity of the existing melamine thermosetting resin, the resin cannot be uniformly and thoroughly impregnated into the decorative paper, so that the brightness of the existing melamine veneer is not high, which cannot meet the needs of the market for high-gloss veneer

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] The melamine veneer of this embodiment is composed of particleboard and melamine-impregnated film paper.

[0029] The preparation method of the melamine veneer of the present embodiment is as follows:

[0030] (1) Preparation of glue base material: accurately weigh each component according to the proportion of glue base material: 50kg of water, 90kg of formaldehyde aqueous solution with a concentration of 37.4% by weight, 80kg of melamine powder, and 10kg of diethylene glycol; 0.69 kg of organic acid curing agent, 0.69 kg of 523 release agent produced by Germany Woods, 0.69 kg of 959 penetrating agent produced by Germany Woods, and 0.69 kg of 905 brightener produced by Germany Woods. In this embodiment, the weight ratio of the glue base material to the glue auxiliary agent is: 100:1.2.

[0031] Add water and formaldehyde solution to the reaction kettle, stir evenly, then add melamine powder, start the stirrer to stir at a speed of 900 rpm, raise the temperature to 98-1...

Embodiment 2

[0036]The melamine veneer of this embodiment is composed of medium density fiberboard and melamine-impregnated film paper.

[0037] The preparation method of the melamine veneer of the present embodiment is as follows:

[0038] (1) Preparation of glue base material: accurately weigh each component according to the proportion of glue base material: 55kg of water, 120kg of formaldehyde aqueous solution with a concentration of 34% by weight, 90kg of melamine powder, and 18kg of diethylene glycol; Organic acid curing agent 1.51kg, epoxy resin release agent 1.51kg, dioctyl maleate sodium sulfonate penetrating agent 1.89kg, styrene brightener 1.89kg. In this embodiment, the weight ratio of the glue base material to the glue auxiliary agent is: 100:2.4.

[0039] Add water and formaldehyde solution to the reaction kettle, stir evenly, then add melamine powder, start the agitator to stir at a speed of 1500 rpm, raise the temperature to 98-102°C, let the mixed solution react for 90 min...

Embodiment 3

[0044] The melamine veneer of this embodiment is composed of hard fiberboard and melamine-impregnated film paper.

[0045] The preparation method of the melamine veneer of the present embodiment is as follows:

[0046] (1) Preparation of glue base material: accurately weigh each component according to the proportion of glue base material: 60 kg of water, 130 kg of formaldehyde aqueous solution with a concentration of 35% by weight, 100 kg of melamine powder, and 20 kg of diethylene glycol; aromatic organic acid anhydrides are solidified 1.4kg agent, 1.4kg phenolic resin release agent, 1.4kg sodium dibutylnaphthalenesulfonate penetrating agent, 1.4kg acrylate brightener. In this embodiment, the weight ratio of the glue base material to the glue auxiliary agent is: 100:1.8.

[0047] Add water and formaldehyde solution to the reaction kettle, stir evenly, then add melamine powder, start the agitator to stir at a speed of 1200 rpm, raise the temperature to 98-102°C, and let the m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a melamine veneer and a preparation method thereof, and belongs to the technical field of decorating materials. The melamine veneer is composed of a substrate and melamine impregnated paper. The melamine impregnated paper is obtained by impregnating paper in a melamine resign adhesive and processing the impregnated paper. The melamine resin adhesive has better activity as the formula thereof is determined by repeated tests. The melamine veneer has a simple processing technology, which causes the melamine resin adhesive to be more evenly and thoroughly immersed into decorating paper. The veneer formed by pressing has a plurality of advantages of the traditional melamine veneer such as high hardness, good abrasion resistance and good heat resistance, good chemical resistance, smooth and clean surface, easy maintenance and cleaning and the like, and further has the advantage of high luminance.

Description

technical field [0001] The invention discloses a melamine veneer and a preparation method thereof, belonging to the technical field of decorative materials. Background technique [0002] At present, the decorative panels used in large quantities include UV panels, baking varnish panels, and melamine veneer panels. The UV board is based on MDF, and the surface is cured by UV (Ultraviolet, ultraviolet light), so that the liquid paint becomes a solid film in a short time, and the base material and the coating film form a firm claw-shaped penetration, making the board The surface will not fall off. UV board has good brightness, bright color, strong chemical resistance, long service life, not easy to change color, easy to clean, but high cost, high requirements for mechanical equipment and process technology, and the surface is not resistant to wipe test, easy to self-crack, Self-explosion, the core material is self-heavy. Baking varnish board is a board that has been heated a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B27N7/00
Inventor 张友全
Owner QUANYOU FURNITURE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com