Non-halogen flame-proof polyvinyl composite and method of producing the same

A technology for flame-retardant polyethylene and composition, applied in the field of flame-retardant polyethylene resin and its preparation, can solve the problems of poor processing performance, water resistance and compatibility, and achieve good comprehensive mechanical properties, low addition amount, High flame retardant efficiency

Inactive Publication Date: 2009-04-08
BEIJING INSTITUTE OF TECHNOLOGYGY
View PDF0 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, APP has poor processing performance, water resistance, and compatibility with organic substances.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Non-halogen flame-proof polyvinyl composite and method of producing the same
  • Non-halogen flame-proof polyvinyl composite and method of producing the same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0028] Below in conjunction with embodiment, further illustrate the present invention.

[0029] raw material :

[0030] polyethylene resin :

[0031] ① Low-density polyethylene (LDPE), produced by the chemical plant of Beijing Yanshan Petrochemical Corporation, brand: AC-100, density 0.9225g / cm 3 , Melt flow rate 2.0g / 10min, granular.

[0032] ② Ammonium polyphosphate (APP): Produced by Hangzhou JLS Flame Retardant Chemical Co., Ltd., brand: JLS-APP101, its phosphorus content is 28-30%, and its nitrogen content is 17-20%.

[0033] ③ Melamine cyanurate (MC): Produced by Hangzhou JLS Flame Retardant Chemical Co., Ltd., brand: JLS-MC25.

[0034] ④ Resorcinol (diphenyl diphosphate) (RDP): Produced by Xu Ruida Company of the United States, brand: FyrolflexRDP.

[0035] ⑤ Maleic anhydride grafted ethylene-vinyl acetate copolymer (EVA-g-MAH): produced by Nanjing Deba Chemical Co., Ltd., brand: EVA-G-1, grafting rate 1.10%, melt flow rate 1-15g / 10min, VA content 28%. ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
melt flow indexaaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to View More

Abstract

The invention provides a non-halogen flame-retardant polyethylene composition and a preparation method thereof, which relates to the field of the flame-retardance modification of resins. The composition contains 100pbw (parts by weight) of polyethylene resin, 35 parts to 55 parts of non-halogen fire retardants and 8 parts to 20 parts of flame-retardant synergists. The non-halogen fire retardant is compounded by ammonium polyphosphate, melamine cyan urate and hydroxyphenol (diphenyl phosphate), wherein, the total amount of the ammonium polyphosphate and the melamine cyan urate accounts for 32pbw to 50pbw, and the weight ratio of the ammonium polyphosphate and the hydroxyphenol is 1:1 to 4:1; the hydroxyphenol (Diphenyl phosphate) accounts for 3pbw to 5pbw. The flame-retardant synergist can be graft copolymer of vinyl acetic ester and maleic anhydride, or graft copolymer of maleic anhydride and ethylene / octane, or ethylene / octane copolymer or polyphenyl ether. All components are mixed according to the parts by weight and then melted to obtain the polyethylene composition. Under the condition that FV-0 grade is ensured to reached, the polyethylene composition has high flame-retardant efficiency, generates no molten drop, creates small volume of smoke during burning and has good comprehensive mechanical properties.

Description

Technical field: [0001] The invention relates to a flame-retardant polyethylene composition, and furthermore, relates to a flame-retardant polyethylene resin modified by a halogen-free flame retardant and a preparation method thereof. Background technique: [0002] Widely used polyethylene (PE) is one of the five general-purpose plastics in the world. It has the advantages of light weight, non-toxicity, convenient processing and molding, low price, and chemical corrosion resistance. It is widely used. However, the limiting oxygen index of polyethylene is very low (about 17.5), and its flame retardant performance is poor. Therefore, the application of polyethylene is greatly limited, and it needs to be modified to a certain extent by flame retardancy. [0003] At present, the flame retardant means for polyethylene is still mainly to add halogenated flame retardants, which have the best flame retardant effect among many types of flame retardants. However, due to its large am...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L51/06C08L23/08C08L71/12C08K3/32C08K5/3492C08K5/523
Inventor 臧充光焦清介吴中伟张亚群
Owner BEIJING INSTITUTE OF TECHNOLOGYGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com