Tissue renovation material of polymer form and preparation method thereof
A tissue repair and polymer technology, applied in medical science, prosthesis, etc., can solve the problems of difficult PA-6 degradation, uncontrollable degradation speed, unmatched degradation process and mechanical properties, etc., to achieve good biocompatibility and Effect of bioactivity, good bioactivity and compatibility, good biomechanical properties
Active Publication Date: 2011-09-14
SICHUAN GUONA TECH
View PDF0 Cites 6 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
The main problems of the natural polymer materials currently used are low strength and rejection
Synthetic controllable degradable polymer materials (such as polylactic acid, etc.), whose degradation rate in the body cannot be controlled, the degradation process and mechanical properties cannot be matched, and the degradation products cause side effects such as irritation and inflammation to the tissue; while the controllable degradation of aliphatic polyester The strength of the series of materials is low, which cannot meet the repair and reconstruction of bearing parts
Among the synthetic polymer materials, although polyamide (PA) has the same amide bond-N-C=O as protein, the research results show that the commonly used synthetic polyamide PA-66 cannot be degraded by esterase, but can only be degraded by papain. , trypsin and chymotrypsin, and the degree of degradation is very low; the degradation of PA-6 is also very difficult
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreExamples
Experimental program
Comparison scheme
Effect test
example 1~9
example 10
example 11
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Property | Measurement | Unit |
---|---|---|
compressive strength | aaaaa | aaaaa |
flexural strength | aaaaa | aaaaa |
tensile strength | aaaaa | aaaaa |
Login to View More
Abstract
The present invention relates to a tissue-repairing material in the form of a polymer and a preparation method thereof. Epsilon-aminocaproic acid is polymerized with at least two other types of amine acids to form the tissue-repairing material shown in the formula, wherein, the mole ratio of the Epsilon-aminocaproic acid is 50 percent to 90 percent, and the rest is the other amine acids includingaminoacetic acid, lactamic acid, phenylalanine, lysine and proline. After being sufficiently and uniformly dispersed into water, the materials, amine acids, are heated to less than or equal to 200 DEG C, so that various forms of water can be removed from the materials; the materials are then pre-polymerized under the temperature between 200 DEG C and 220 DEG C and polymerized under the temperature between 220 DEG C and 250 DEG C; and the preparation process is conducted and fulfilled under the protection of an inert gas. The tissue-repairing material has ideal mechanical property, biological activity and controllable degradation property, and the degradation product of the tissue-repairing material is non-toxic and non-irritant. The tissue-repairing material can be widely used for the reparation and reconstruction of the tissues of the human body.
Description
technical field The present invention relates to a tissue repairing material in the form of a polymer in the medical field and a preparation method thereof, more specifically a tissue repairing material polymerized from polyamino acids and a preparation method thereof. Background technique Synthetic polymer materials play an important role in biomedicine such as medical hoses, syringe snares, valves, urinary catheters, catheters, heart valves, etc., and have been widely used in the treatment of human hard tissue injuries and diseases in recent years. Repaired and rebuilt with excellent performance. For example, polyether ether ketone (PEEK) is considered to be a hard tissue replacement material with good biomechanical compatibility, and is widely used in the fields of spinal repair and correction; ultra-high molecular weight polyethylene (UHMWPE) has a wide range of uses in artificial joints. Currently used medical polymer materials can be divided into two types: non-degra...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A61L27/18C08G69/08
Inventor 严永刚李鸿吕国玉曹侠杨爱萍蒋伟裴福兴宋跃明段宏
Owner SICHUAN GUONA TECH
Who we serve
- R&D Engineer
- R&D Manager
- IP Professional
Why Patsnap Eureka
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com