Formaldehyde-free rubber film for synthesizing multilayer solid wood base material

A zero-formaldehyde and substrate technology, applied in the field of zero-formaldehyde film, can solve the problems of low yield, affect the quality of finished products, carbonization, etc., and achieve the effects of strong viscosity, improved qualification rate, and enhanced stability

Inactive Publication Date: 2008-11-26
牛桂祥 +1
View PDF1 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the adhesives used to synthesize multi-layer solid wood substrates in the market have the following deficiencies: First, the commonly used adhesives are mainly synthetic resins, such as urea-formaldehyde glue, phenolic glue, melamine glue, etc. These adhesives all contain formaldehyde, which is seriously harmful The health of the human body; secondly, the traditional sizing method is to apply liquid adhesive on the dry veneer. There will be sandwich or hollow defects between the boards. In addition, the use of liquid glue will increase the water content of the finished product, that is, the multi-layer solid wood substrate, and will also cause distortion of the multi-layer solid wood substrate.
Publication number published by the National Patent Office: CN101058199A, application number: 200710028074.6; in the technical solution of the disclosed document, the adhesive used is a hot-melt adhesive film or a thermoplastic film, and this technical solution makes up for the above-mentioned defects. However, there are new deficiencies in itself: due to the instability of the melting point of the hot melt adhesive film or thermoplastic film, in the production process, when the heating device exceeds 200 ° C, not only energy is wasted, but also the plate will be scorched. , carbonization phenomenon; when the temperature is lower than 150°C, the bonding adhesive cannot be completely melted and bonded, which affects the quality of the finished product. Therefore, when the technical solution is implemented, the yield is very low, and large-scale and mass production cannot be formed.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] 1. Raw material selection: Polyethylene uses blown film-grade polyethylene particles with a melt index (MI) of 4g / 10min; EVA260 resin: selects DuPont EVA260 resin from the United States; low molecular weight PE wax: select commonly used ones; titanium dioxide: select up to Industrial grade titanium dioxide.

[0036] 2. Weigh each raw material: polyethylene: 81 kg; EVA260 resin: 19 kg; low-molecular weight PE wax: 0.3 kg; titanium dioxide: 0.4 kg, then mix the above-mentioned raw materials, stir and mix well.

[0037] 3. Put the above-mentioned weighed raw materials into the barrel of the SJJ-120X32 / 120X6 two-stage extrusion granulation unit for granulation. After the raw materials are heated, they are slowly plasticized under the push of the two-stage screw, from After being formed in the die, it is cooled in water, and then pelletized as needed.

[0038] 4. Use the SJ-BMZ type high and low pressure polyethylene film blowing machine to blow the above raw material parti...

Embodiment 2

[0041] 1. Raw material selection: Polyethylene uses blown film-grade polyethylene particles with a melt index (MI) of 4g / 10min; EVA260 resin: selects DuPont EVA260 resin from the United States; low molecular weight PE wax: select commonly used ones; titanium dioxide: select up to Industrial grade titanium dioxide.

[0042] 2. Weigh each raw material: polyethylene: 85 kg; EVA260 resin: 14 kg; low molecular weight PE wax: 0.5 kg; titanium dioxide: 0.5 kg, then mix the above weighed raw materials, stir and mix well.

[0043] 3. Put the above-mentioned weighed raw materials into the barrel of the SJJ-120X32 / 120X6 two-stage extrusion granulation unit for granulation. After the raw materials are heated, they are slowly plasticized under the push of the two-stage screw, from After being formed in the die, it is cooled in water, and then pelletized as needed.

[0044] 4. Use the SJ-BMZ type high and low pressure polyethylene film blowing machine to blow the above raw material particl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Melt indexaaaaaaaaaa
Login to View More

Abstract

The invention discloses zero-formaldehyde glue film used for synthesizing multilayered solid wood base material, which has the technical proposal that the zero-formaldehyde glue film is prepared by the materials with the following weight parts: 80-90 parts of polyethylene, 5-19 parts of EVA260 resin, 0.1-0.5 parts of low molecular weighted PE wax and 0.1-0.5 parts of titanium dioxide. The glue film has the advantages that as the zero-formaldehyde glue film used for synthesizing multilayered solid wood base material is characterized by stable melting point, the qualification rate of the finished products of multilayered solid wood base material is greatly improved, thus laying the foundation for the development of mass industrialization; as the glue layer is characterized by low water content, the stability of the shapes and sizes of the multilayered solid wood base material is greatly strengthened; as the glue film is characterized by strong adhesion and zero formaldehyde, the multilayered solid wood base material is firmer and more environment-friendly.

Description

technical field [0001] The invention relates to a zero-formaldehyde adhesive film, in particular to a zero-formaldehyde adhesive film for synthesizing multi-layer solid wood substrates. Background technique [0002] At present, the adhesives used to synthesize multi-layer solid wood substrates in the market have the following deficiencies: First, the commonly used adhesives are mainly synthetic resins, such as urea-formaldehyde glue, phenolic glue, melamine glue, etc. These adhesives all contain formaldehyde, which is seriously harmful The health of the human body; secondly, the traditional sizing method is to apply liquid adhesive on the dry veneer. There will be sandwich or hollow defects between the boards. In addition, the use of liquid glue will increase the water content of the finished product, that is, the multi-layer solid wood substrate, and will also cause distortion of the multi-layer solid wood substrate. Publication number published by the National Patent Offi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09J7/00C09J123/06B29C55/28B32B21/13B32B37/12C09J123/08
Inventor 黄国胜
Owner 牛桂祥
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products