Anti-neutron size putty

A putty and neutron technology, which is applied in the field of anti-neutron quick-drying putty and its preparation, can solve the problems of long drying time of putty and achieve good social benefits, convenient construction and excellent neutron shielding performance

Active Publication Date: 2008-11-12
北京富迪创业科技有限公司 +1
View PDF0 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Due to the slow evaporation rate of water at room temperature, the traditional water-based putty has a long drying time for the putty. In some special applications, the putty must be dried quickly after construction to ensure the safety of equipment and shielding structures. Therefore, it is urgently needed in the market. Development of a fast-drying putty for neutron shielding

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] The anti-neutron quick-drying putty of the present embodiment is made of following components:

[0022] Cement 42.5R: 50 kg

[0023] Polyethylene powder: 30 kg

[0024] Boronite: 8 kg

[0025] Iron oxide black: 5 kg

[0026] Water: 25kg

[0027] The coagulant is cement 42.5R sold in the market, and the solid material is weighed and mixed evenly. When using, add the above-mentioned amount of water, and it can be used after mixing evenly.

Embodiment 2

[0029] The anti-neutron quick-drying putty of the present embodiment is made of following components:

[0030] Cement 42.5R: 60 kg

[0031] Polyethylene powder: 30 kg

[0032] Boron carbide: 10 kg

[0033] Iron oxide black: 15 kg

[0034] Water: 35kg

[0035] The coagulant uses cement 42.5R sold on the market, weighs the solid material and puts it into a high-speed mixer, mixes it uniformly for 5 minutes, and then it can be used. When using on-site, add the above-mentioned amount of water, mix evenly and start construction.

Embodiment 3

[0037] The anti-neutron quick-drying putty of the present embodiment is made of following components:

[0038] 821 wall scraping putty: 45 kg

[0039] Polyethylene powder: 20 kg

[0040] Lithium fluoride: 5 kg

[0041] Iron oxide black: 10 kg

[0042] Water: 24kg

[0043] The coagulant uses the 821 wall scraping putty sold on the market, weighs the solid material, puts it into a high-speed mixer, mixes it evenly for 5 minutes, and then it can be used. When using on-site, add the above-mentioned amount of water when using, mix evenly and start construction.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Densityaaaaaaaaaa
Login to View More

Abstract

The invention provides a quick dry type neutron-shielding lacquer putty and a method for preparing the same. The quick dry type neutron-shielding lacquer putty is used for filling a hole or an aperture of a neutron radiant point shielding structure in order to reduce the leakage of neutron radiation and improve the whole protective performance of a shielding system. The material is prepared by adopting a coagulant, a neutron moderator, a neutron absorber, a colorant, water and other compositions mixed together. The quick dry type neutron-shielding lacquer putty has good neutron-shielding performance, short drying time, simple structure, convenient construction, strong practicability and good economical benefit.

Description

technical field [0001] The invention relates to a neutron-proof quick-drying putty and a preparation method thereof, which are used for shielding protection of various neutron radiation sources such as isotope neutron sources, nuclear reactors, and electron accelerators. Background technique [0002] Isotopic neutron sources, nuclear reactors and accelerators will produce nuclear radiation during operation, especially neutron radiation has a strong penetrating ability, which poses a huge threat to the health of operators. Nowadays, iron, lead, polyethylene, paraffin or composite shielding materials are generally used to shield these radiation sources. During the installation and use of these materials, a small gap will be left at the material connection, and neutron radiation will pass through these gaps. It will damage the operator and greatly reduce the protective effect of the overall shielding structure. Secondly, there are many pipes and holes around the radiation sour...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D5/34
Inventor 尚宏忠曾心苗郭振涛鲍矛王红杰周成飞郑金美张龙
Owner 北京富迪创业科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com