Stainless steel plate fin type heat exchanger core body high-temperature brazing jig and manufacturing process thereof

A technology of finned heat exchanger and stainless steel plate, applied in the direction of manufacturing tools, welding equipment, welding equipment, etc., can solve the problems of misalignment of assembly components, loss of elasticity of fixtures, and reduction of yield, so as to reduce stress and increase weld strength , Improve the effect of welding rate

Inactive Publication Date: 2008-11-12
NANJING UNIV OF TECH
View PDF0 Cites 26 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At such a high temperature, if a traditional clamp is used, the pre-tightening force of the bolts and springs will be released due to high temperature creep and relaxation, and the clamp will lose its elasticity and be in a "loose" state, resulting in misalignment of assembly components
There is no clamping force after the solder is melted, and the small gap required by the brazing capillary action cannot be maintained between the parts, which affects the welding quality, and causes the product to be "de-soldered", resulting in the scrapping of the product and greatly reducing the yield of the product

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Stainless steel plate fin type heat exchanger core body high-temperature brazing jig and manufacturing process thereof
  • Stainless steel plate fin type heat exchanger core body high-temperature brazing jig and manufacturing process thereof
  • Stainless steel plate fin type heat exchanger core body high-temperature brazing jig and manufacturing process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0056] Example: such as figure 1 As shown, a fixture for high-temperature brazing of the core of a stainless steel plate-fin heat exchanger is composed of an upper splint 1, a lower splint 2, bolts 3, nuts 4 and a spherical crown pressure vessel 5. The upper and lower splints, bolts and nuts are made of high-temperature alloy KHR SA, and the lower splint is a whole piece with a rectangular "Tian" skeleton structure to increase the rigidity of the lower splint. The inside of the container is filled with argon gas at a certain pressure (0.1-1.0MPa), and the expansion of the gas at high temperature will generate pressure, so that the core body can obtain uniform pressure during the whole brazing process.

[0057] The special fixture for high temperature packaging of the stainless steel plate-fin heat exchanger core can be manufactured by the following method, which includes the following steps:

[0058] 1. Select the high temperature resistant alloy KHR SA (30Cr-48Ni-13W) to pr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Surface roughnessaaaaaaaaaa
Flatnessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a clamp used for high-temperature brazing of a stainless steel plate fin-typed heat exchanger core, which is characterized in that the clamp consists of an upper clamping plate (1), a lower clamping plate (2), a bolt (3), a nut (4) and a pressure vessel (5), wherein, the bolt (3) and the nut (4) are used for clamping the upper clamping plate (1) and the lower clamping plate (2); the core of the stainless steel plate fin-typed heat exchanger is placed between the upper clamping plate (1) and the lower clamping plate (2); the pressure vessel (5) is directly and flatly placed on the upper clamping plate (1); the vessel is internally filled with argon which expands under the high temperature and generates uniform pressure so as to lead the equipment elements of the core to be closely contacted with each other and ensure the welding quality of the core of the fin-typed heat exchanger. The clamp of the invention can meet the manufacture requirement of the core of the stainless steel plate tin-typed heat exchanger, generates uniform pressure under high temperature and greatly improves the qualified rate of the products.

Description

technical field [0001] The invention relates to a jig and its manufacturing process, in particular to a high-temperature brazing jig specially used for brazing the core body of a stainless steel plate-fin heat exchanger and its manufacturing process. Background technique [0002] Plate-fin heat exchanger is a kind of heat exchanger. It has the characteristics of high thermal conductivity, small size, light weight and high strength. It is more and more widely used in petrochemical, atomic energy, nuclear power and other industries. The core of the plate-fin heat exchanger is composed of fins, partitions, seals and deflectors. A metal plate (partition) is placed at the upper and lower ends of the fin, and the two sides are sealed with edge seals to form a basic unit. A solder foil is preset between the separator, the fins and the seal. The melting point of the brazing filler metal is lower than that of the base metal, and the brazing filler metal alloy melts at the brazing t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B23K37/053B23P15/00B23K9/16B23K9/235
Inventor 蒋文春巩建鸣涂善东耿鲁阳
Owner NANJING UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products