High-temperature dechlorinating agent and preparing method thereof

A dechlorination agent, high temperature technology, applied in separation methods, chemical instruments and methods, dispersed particle separation, etc., can solve the problems of inability to apply at the same time, the dechlorination agent has a low chlorine capacity and cannot achieve a higher dechlorination effect, and achieves excellent The effect of pore system, increasing stability and improving dechlorination activity

Active Publication Date: 2008-10-01
BEIJING SJ ENVIRONMENTAL PROTECTION & NEW MATERIAL CO LTD
View PDF3 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] What the present invention aims to solve is that the chlorine capacity of the dechlorination agent in the prior art is low and cannot achieve a high dechlorination effect, and the dechlorination agent cannot be applied to coal gasification fuel cell (MCFC) system and coal gasification combined cycle power generation at the same time. (IGCC) system and the problem of dechlorination in catalytic reforming regeneration gas, and then provide a method that can be applied to coal gasification fuel cell (MCFC) system, coal gasification combined cycle power generation (IGCC) system and catalytic reforming simultaneously at high temperature High dechlorination effect of hydrogen chloride removal in regeneration gas, dechlorination agent with high chlorine capacity

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] Weigh 28 kg of calcium hydroxide, 18 kg of calcium oxide, 32 kg of hydrotalcite, 17 kg of kaolin, and 5 kg of sodium silicate, grind the above materials to more than 200 mesh, and fully mix the above ground materials ;Put the ground and mixed powder into the rolling ball machine, and spray an appropriate amount of water to form it while rolling. When the particle size of the rolling ball reaches Φ3-5mm, take out the spherical particles; put the above spherical particles in Stand at room temperature for 10 hours; then, dry the cured spherical particles at 100°C, and then roast at 550°C for 3 hours to obtain the dechlorination agent of the present invention.

[0015] The prepared dechlorination agent is subjected to a dechlorination test. The dechlorination reaction conditions are: the raw gas contains 2000-3000PPm (volume fraction) of hydrogen chloride, and the reaction temperature is 650°C. The dechlorination agent can reduce the hydrogen chloride content of the outlet g...

Embodiment 2

[0017] Weigh 20 kg of calcium hydroxide, 30 kg of calcium oxide, 40 kg of hydrotalcite, 6 kg of kaolin, 1 kg of sheep liver soil, and 3 kg of sodium silicate, and grind the above materials to more than 200 mesh respectively, and grind the above The finished materials are fully mixed; put the above ground and mixed powder into the rolling ball machine, spray an appropriate amount of water while rolling to form, when the particle size of the rolling ball reaches Φ3 ~ 5mm, take out the spherical particles The above-mentioned spherical particles are kept at room temperature for 10 hours; after that, the spherical particles after curing are dried at 100°C, and then roasted at 560°C for 3 hours to obtain the dechlorination agent of the present invention.

[0018] The prepared dechlorination agent is subjected to a dechlorination test. The dechlorination reaction conditions are: the raw gas contains 2000-3000PPm (volume fraction) of hydrogen chloride, and the reaction temperature is 6...

Embodiment 3

[0020] Weigh 25 kg of calcium hydroxide, 25 kg of calcium oxide, 40 kg of hydrotalcite, 3 kg of attapulgite clay, and 7 kg of sodium silicate, grind the above materials to more than 200 mesh respectively, and carry out Mix well; put the ground and mixed powder into the rolling ball machine, spray appropriate amount of water to form it while rolling, when the particle size of the rolling ball reaches Φ3~5mm, take out the spherical particles; put the above spherical The granules are kept at room temperature for 15 hours; after that, the cured spherical granules are dried at 110°C, and then roasted at 570°C for 4 hours to obtain the dechlorination agent of the present invention.

[0021] The prepared dechlorination agent is subjected to a dechlorination test. The dechlorination reaction conditions are: the raw gas contains 2000-3000PPm (volume fraction) of hydrogen chloride, and the reaction temperature is 650°C. The dechlorination agent can reduce the hydrogen chloride content of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a high-temperature dechlorination agent, which consists of 0 to 42 wt percent of CaOH, 18 to 70 wt percent of CaO, 20 to 40 wt percent of hydrotalcite, 7 to 17 wt percent of clay and 0 to 7 wt percent of adhesive. Based on the high-temperature dechlorination agent, the invention further discloses a preparation method of the high-temperature dechlorination agent. The high-temperature dechlorination agent prepared by the preparation method can be applied to a coal gasification fuel cell (MCFC) system, a coal gasification combination circulation power generation (IGCC) system and catalytic reforming regeneration gas so as to remove the HCl; furthermore, the dechlorination agent has high chlorine content and good dechlorination effect.

Description

technical field [0001] The invention relates to a dechlorination agent for removing hydrogen chloride at relatively high temperature, belonging to the technical field of gas purification. Background technique [0002] In the raw material gas or other gaseous materials in the production process of petrochemical and chemical fertilizer industries, there are often more or less residual hydrogen chloride gas. Hydrogen chloride gas is an acidic corrosive gas, which has a strong corrosive effect on production equipment, and can easily cause cave-shaped spots on production equipment, seriously affecting the safety of industrial production; The high-efficiency catalysts used in production have side effects, which can easily lead to catalyst poisoning and deactivation, thus directly affecting the above-mentioned normal industrial production. In addition, in the petrochemical industry, residual hydrogen chloride (converted from residual organic chlorine in the oxygen chlorination pro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01D53/68
Inventor 冯续蒲延芳刘彦芳
Owner BEIJING SJ ENVIRONMENTAL PROTECTION & NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com