High flexible flame retardant PC(polycarbonate)/ABS alloy

A high-toughness, alloy technology, applied in the field of thermoplastic resin compositions, can solve the problems of poor processing fluidity, easy stress cracking, easy wear, etc., and achieve the effect of improving processing performance and reducing melt viscosity

Inactive Publication Date: 2007-07-25
MITAC PRECISION TECH CO LTD SHUNDE DISTRICT FOSHAN CITY
View PDF0 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] PC also has some obvious defects, such as: poor processing fluidity, easy stress cracking, sensitive to notch, easy to wear, poor chemical resistance, high price, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0059] Take PC recycled materials, ABS, grafts, MBS, epoxy resin, antioxidant, flame retardant and other components, and blend all the raw materials according to the following composition formula:

[0060] (a) 59 pieces of recycled PC materials

[0061] (b) ABS 20 parts

[0062] (c) 4 parts of ABS-g-MAH

[0063] (d) 5 copies of MBS

[0064] (e) 0.5 parts of epoxy resin

[0065] (f) Antioxidant 2921 0.2 parts

[0066] (g) 9 parts of brominated polycarbonate

[0067] (h) 1.5 parts of antimony trioxide

[0068] (i) 1.5 parts of zinc borate

[0069] (j) 0.5 parts of polytetrafluoroethylene

[0070] Then the blended material is mixed and granulated in an extruder, and the resulting mixed and granulated product is made into a finished product by injection molding. Finally, the mechanical properties of the finished product are tested according to the national standard GB13525 / T-92 and the UL94 standard of the American Electrotechnical Association. The flame retardant performa...

Embodiment 2

[0074]Take PC recycled materials, ABS, grafts, MBS, epoxy resin, antioxidant, flame retardant and other components, and blend all the raw materials according to the following composition formula:

[0075] (a) 52 pieces of recycled PC materials

[0076] (b) ABS 30 parts

[0077] (c) 2 parts of ABS-g-MAH

[0078] (d) 8 copies of MBS

[0079] (e) 0.1 parts of epoxy resin

[0080] (f) Antioxidant 2921 0.3 part

[0081] (g) 6 parts of brominated polycarbonate

[0082] (h) 1 part antimony trioxide

[0083] (i) 1 part zinc borate

[0084] (j) 0.3 parts of polytetrafluoroethylene

[0085] Then the blended material is mixed and granulated in an extruder, and the resulting mixed and granulated product is made into a finished product by injection molding. Finally, the mechanical properties of the finished product are tested according to the national standard GB13525 / T-92 and the UL94 standard of the American Electrotechnical Association. The flame retardant performance was tested...

Embodiment 3

[0089] Take PC recycled materials, ABS, grafts, MBS, epoxy resin, antioxidant, flame retardant and other components, and blend all the raw materials according to the following composition formula:

[0090] (a) 34 pieces of recycled PC materials

[0091] (b) ABS 35 parts

[0092] (c) 5 parts of ABS-g-MAH

[0093] (d) MBS 10 copies

[0094] (e) 0.3 parts of epoxy resin

[0095] (f) Antioxidant 2921 0.3 part

[0096] (g) 12 parts of brominated polycarbonate

[0097] (h) 2 parts of antimony trioxide

[0098] (i) Zinc borate 2 parts

[0099] (j) 0.8 parts of polytetrafluoroethylene

[0100] Then the blended material is mixed and granulated in an extruder, and the resulting mixed and granulated product is made into a finished product by injection molding. Finally, the mechanical properties of the finished product are tested according to the national standard GB13525 / T-92 and the UL94 standard of the American Electrotechnical Association. The flame retardant performance was t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
bending strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

This invention relates to a formula for preparing flame-retardant PC / ABS alloy with high toughness by modifying recovered PC. The formula comprises: recovered PC 45-60 parts, ABS 20-35 parts, grafting monomer 1-5 parts, acrylate copolymer 3-10 parts, epoxy resin 0.1-1 part, antioxidant 0.1-0.5 part, bromine series flame retardant 6-12 parts, stibium series flame retardant 1-2 parts, inorganic flame retardant 1-2 parts, and polytetrafluoroethylene 0.2-0.8 part. This invention adopts high-efficiency compatibilizer to modify recovered PC and ABS and prepare PC / ABS alloy, thus can reduce the melt viscosity of PC and improve its processability, and is environmentally friendly due to resue of recovered PC.

Description

technical field [0001] The invention relates to the field of thermoplastic resin compositions in polymer material technology, in particular to a formula for modifying PC (Polycarbonate, polycarbonate) recycled materials into high-toughness flame-retardant PC (polycarbonate) / ABS alloys. Background technique [0002] PC is an engineering plastic with superior comprehensive performance. It has excellent impact toughness, dimensional stability, electrical insulation, creep resistance, weather resistance, transparency and non-toxicity. It is widely used in mechanical equipment, construction engineering, Transportation, instrumentation and electrical and electronic lighting and other fields. [0003] PC also has some obvious defects, such as: poor processing fluidity, easy stress cracking, sensitive to notch, easy to wear, poor chemical resistance, high price, etc. The consumption of PC is large, and at the same time, the amount of secondary materials, nozzle materials and recycl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L69/00C08K5/06C08L55/02C08L33/04C08L63/00C08L27/18
Inventor 汪克风岳瑟杨得志
Owner MITAC PRECISION TECH CO LTD SHUNDE DISTRICT FOSHAN CITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com