Gold extraction process with low pollution and high recovery for refractory gold concentrate

A high recovery rate, refractory gold technology, applied in the direction of improving process efficiency, to achieve the effect of reducing pollution, improving recovery rate, and comprehensive recovery effect

Active Publication Date: 2010-03-24
CHANGCHUN GOLD RES INST +1
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a low-pollution and high-recovery refractory gold concentrate gold extraction process, which not only solves the oxidation problem of sulfide and carbon substances; but also fully exposes and dissociates gold, making most of the sulfur and arsenic After being oxidized, it enters the liquid phase, which completely solves the problem of gold adsorption in the subsequent cyanidation operation. This process improves the recovery rate of gold, reduces environmental pollution, and is easy to be automatically controlled, so that this part of refractory gold resources can be fully utilized.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Gold extraction process with low pollution and high recovery for refractory gold concentrate
  • Gold extraction process with low pollution and high recovery for refractory gold concentrate
  • Gold extraction process with low pollution and high recovery for refractory gold concentrate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0066] (1) Grinding of gold concentrate and dense drug removal:

[0067] Grind the above-mentioned refractory gold concentrate until the grinding particle size is -0.045mm and the content is 95%, and then carry out dense drug removal and adjust the pulp concentration to 16%;

[0068] (2) Biological oxidation:

[0069] Feed the ore pulp with a certain concentration adjusted in step (1) into the biological oxidation system. Under the process conditions of guaranteed temperature of 40°C, dissolved oxygen amount of 4mg / l, medium dosage of 4kg / t, and oxidation time of 8 days, microorganisms can oxidize, decompose and vulcanize Minerals, so that gold is fully exposed and dissociated. After biological oxidation, the oxidized washing liquid undergoes primary neutralization and secondary neutralization to remove arsenic, separates solids and liquids, discharges neutralized slag, and returns the neutralized liquid to wash, then press filter and dry Powdered into oxide slag, enter the n...

Embodiment 2

[0079] (1) Grinding of gold concentrate and dense drug removal:

[0080] Grind the above refractory gold ore until the grinding particle size is -0.045mm and the content is 95%, and then carry out dense drug removal and adjust the pulp concentration to 16%;

[0081] (2) Biological oxidation:

[0082] Feed the ore pulp with a certain concentration adjusted in step (1) into the biological oxidation system. Under the process conditions of guaranteed temperature of 40°C, dissolved oxygen amount of 5mg / l, medium consumption of 4kg / t, and oxidation time of 7 days, microorganisms can oxidize, decompose and vulcanize Minerals, so that gold is fully exposed and dissociated. After biological oxidation, the oxidized washing liquid undergoes primary neutralization and secondary neutralization to remove arsenic, separates solids and liquids, discharges neutralized slag, and returns the neutralized liquid to wash, then press filter and dry Powdered into oxide slag, enter the next step of m...

Embodiment 3

[0092] (1) Grinding of gold concentrate and dense drug removal:

[0093] Grind the above refractory gold ore until the grinding particle size is -0.045mm and the content is 95%, and then carry out dense drug removal and adjust the pulp concentration to 16%;

[0094] (2) Biological oxidation:

[0095] Feed the ore pulp with a certain concentration adjusted in step (1) into the biological oxidation system. Under the technological conditions of guaranteed temperature of 38°C, dissolved oxygen amount of 5mg / l, medium dosage of 4kg / t, and oxidation time of 8 days, microorganisms can oxidize, decompose and vulcanize Minerals, so that gold is fully exposed and dissociated. After biological oxidation, the oxidized washing liquid undergoes primary neutralization and secondary neutralization to remove arsenic, separates solids and liquids, discharges neutralized slag, and returns the neutralized liquid to wash, then press filter and dry Powdered into oxide slag, enter the next step of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a process for extracting gold of refractory gold concentrates with low pollution and high recovery rate, belonging to the metallurgical process class. The process proposal which combines organically the bacterial oxidation technology with the microwave irradiation technology comprises the following steps of: oxidizing and decomposing sulfide minerals by means of the bacterial oxidation technology first; exposing and dissociating sufficiently the gold; oxidizing a large part of sulfur and arsenic to enter a liquid-phase; carrying out the neutralization treatment to theoxidizing liquid and returning to use; roasting oxidizing slag with microwave at the low temperature; and removing organic carbon in ore. The process solves completely the problem of absorbing the gold in the subsequent cyaniding gold extraction work. The process has high recovery rate of the gold and less environment pollution, is easy to automatically control and saves energy.

Description

technical field [0001] The invention relates to a process for refractory gold ore, in particular to a process for extracting gold from refractory gold concentrate with low pollution and high recovery rate. Background technique [0002] As we all know, with the rapid development of the gold industry, the gold ore resources that are easy to be directly extracted by cyanide are gradually exhausted, and the refractory gold ore resources have become the main raw materials for the gold industry in the future. Such ores account for an increasing proportion of the proven gold geological reserves, and are widely distributed in Liao, Hunan, Guangxi, Guizhou, Gansu, Sichuan, Anhui, Jilin and other regions. Its remarkable feature is that gold exists in pyrite or arsenopyrite crystal lattice in the form of fine particles and packages, and contains more elements that interfere with leaching, such as arsenic, sulfur, antimony, organic carbon or other adsorbed gold cyanide complexes. It ha...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22B11/08C22B3/18C22B4/04
CPCY02P10/20
Inventor 郑晔高金昌赵俊蔚巩春龙
Owner CHANGCHUN GOLD RES INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com