Triple anti-forge material and triple anti-forge paper product thereof
A technology of anti-counterfeiting paper and products, which is applied in the direction of textiles and papermaking, papermaking, fiber raw material processing, etc., can solve the problems of poor publicity, etc., and achieve the effects of enhanced bonding, good acid resistance, and high bonding fastness
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0028] Make polyvinyl alcohol into a solution of about 35%, and add anti-counterfeiting powder (all particle sizes are less than 3 μm, can directly withstand 365nm ultraviolet light continuous irradiation for 60 hours; can withstand 140°C for 30 minutes) into the solution:
[0029] Temperature-changing powder (produced by Beijing Chenlei Technology Co., Ltd.): reversible discoloration in the temperature range of 50-60 ° C, red at room temperature, red disappears after heating, the amount added is equivalent to about 3% of the polyvinyl alcohol content by weight;
[0030] Phosphor powder (produced by Peking University Deli Technology Co., Ltd.): the amount added is equivalent to about 1% by weight of the polyvinyl alcohol content, and it shows blue fluorescence under ultraviolet light;
[0031] Infrared powder (produced by Peking University Deli Technology Co., Ltd.): the amount added is equivalent to about 1% of the weight of polyvinyl alcohol, and it will show green fluorescen...
Embodiment 2
[0039] Polyvinyl alcohol is prepared into a solution of about 30-40%, and anti-counterfeiting powder is added to the solution (the particle size should be less than 3 μm):
[0040] Temperature-changing powder (produced by Beijing Chenlei Technology Co., Ltd.): reversible discoloration in the temperature range of 50-60°C, blue at room temperature, and disappears after heating. The amount added is equivalent to 3-4% by weight of polyvinyl alcohol content about;
[0041] Phosphor powder (produced by Peking University Deli Technology Co., Ltd.): the amount added is equivalent to about 2% by weight of the polyvinyl alcohol content, and it shows yellow fluorescence under ultraviolet light;
[0042] Infrared powder (produced by Peking University Deli Technology Co., Ltd.): the amount added is equivalent to about 1.5% by weight of the polyvinyl alcohol content, and it will show red fluorescence under infrared irradiation;
[0043] The above-mentioned polyvinyl alcohol solution added ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com