Method for preparing high-potential gradient zinc oxide piezoresistance by low-temperature sintering

A technology of varistor and zinc oxide, applied in the direction of varistor, varistor core, resistor, etc., can solve the problems of high sintering temperature and low absolute value of potential gradient, so as to reduce the sintering temperature and simplify the process , the effect of eliminating the pre-sintering and granulation process

Inactive Publication Date: 2009-05-06
EAST CHINA NORMAL UNIV
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, not only the absolute value of the potential gradient is low, but the sintering temperature is too high (both greater than 1200°C)

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] Commercially available micron-sized zinc oxide (ZnO), bismuth trioxide (Bi 2 o 3 ), antimony trioxide (Sb 2 o 3 ), chromium trioxide (Cr 2 o 3 ), cobalt trioxide (Co 2 o 3 ), manganese dioxide (MnO 2 ) and diyttrium trioxide (Y 2 o 3 ) powder, mixed according to the following formula, put into a planetary high-energy ball mill, using steel wear-resistant balls and nylon tanks, rotating speed 550rpm, ball-to-powder ratio 20:1, after wet milling in absolute ethanol for 3 hours, from the spherical tank Take it out, dry it in a resistance furnace at 150°C, formula calculation: Substitute X=0.02 into the following formula, zinc oxide: bismuth trioxide: antimony trioxide: chromium trioxide: cobalt trioxide: manganese dioxide: The mole percentage of diyttrium trioxide=(96.5-X):0.7:1.0:0.5:0.8:0.5:X, get formula, zinc oxide: bismuth trioxide: antimony trioxide: chromium trioxide: dichromium trioxide Cobalt: manganese dioxide: the molar percent of diyttrium trioxide=96...

Embodiment 2

[0048] Commercially available micron-sized zinc oxide (ZnO), bismuth trioxide (Bi 2 o 3 ), antimony trioxide (Sb 2 o 3 ), chromium trioxide (Cr 2 o 3 ), cobalt trioxide (Co 2 o 3 ), manganese dioxide (MnO 2 ) and diyttrium trioxide (Y 2 o 3 ) powder, mixed according to the following formula, put into a planetary high-energy ball mill, using steel wear-resistant balls and nylon tanks, rotating speed 500rpm, ball-to-powder ratio 20:1, after wet milling in absolute ethanol for 5 hours, from the spherical tank Take it out, dry it in a resistance furnace at 200°C, formula calculation: Substitute X=0.08 into the following formula, zinc oxide: bismuth trioxide: antimony trioxide: chromium trioxide: cobalt trioxide: manganese dioxide: The mole percentage of diyttrium trioxide=(96.5-X):0.7:1.0:0.5:0.8:0.5:X, get formula, zinc oxide: bismuth trioxide: antimony trioxide: chromium trioxide: dichromium trioxide Cobalt: manganese dioxide: the molar percentage of diyttrium trioxide...

Embodiment 3

[0050] Commercially available micron-sized zinc oxide (ZnO), bismuth trioxide (Bi 2 o 3 ), antimony trioxide (Sb 2 o 3 ), chromium trioxide (Cr 2 o 3 ), cobalt trioxide (Co 2 o 3 ), manganese dioxide (MnO 2 ) and diyttrium trioxide (Y 2 o 3 ) powder, mixed according to the following formula, put into a planetary high-energy ball mill, using steel wear-resistant balls and nylon tanks, rotating speed 450rpm, ball-to-powder ratio 20:1, after wet milling in absolute ethanol for 7 hours, from the spherical tank Take it out, dry it in a resistance furnace at 250°C, formula calculation: substitute X=0.1 into the following formula, zinc oxide: bismuth trioxide: antimony trioxide: chromium trioxide: cobalt trioxide: manganese dioxide: The mole percentage of diyttrium trioxide=(96.5-X):0.7:1.0:0.5:0.8:0.5:X, get formula, zinc oxide: bismuth trioxide: antimony trioxide: chromium trioxide: dichromium trioxide Cobalt: manganese dioxide: the molar percent of diyttrium trioxide=96....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
currentaaaaaaaaaa
densityaaaaaaaaaa
currentaaaaaaaaaa
Login to View More

Abstract

The preparation method for high-potential gradient ZnO piezoresistor material comprises: with high-energy ball grinding technology, adding rare earth oxides included Bi2O3, Sb2O3, Cr2O3, Co2O3, MnO2, and Y2O3; sintering at 800Deg, and obtaining the product. The advantages of this invention comprises: simple process technology, low sintering temperature, fit to traditional device, well properties of the product, 5.50-5.64g / cm3 density, 1845.66-2233.33V / mm voltage-sensitive potential gradient, 21.3-25.8 nonlinear index, and 1.55-10.2muA drain current (given 0.75V1mA).

Description

technical field [0001] The invention relates to a method for preparing a high-potential gradient zinc oxide varistor, belonging to the technical field of varistor manufacture. Background technique [0002] Zinc oxide varistors have excellent volt-ampere characteristics and are widely used in the manufacture of arrester valves. In order to realize the miniaturization and light weight of the arrester valve plate and reduce the manufacturing cost, the development of high potential gradient is the development trend [1] . Viswanath [2] Zinc oxide varistors with a potential gradient as high as 3000V / mm were prepared at a sintering temperature of 750°C by using ultrafine nanopowder obtained by gel suspension and centrifugal separation. Duran [3] The nano-powder prepared by chemical method was also used to prepare zinc oxide varistors with a potential gradient of 2000V / mm at two-stage sintering temperatures of 900°C and 825°C. The above two methods all have the disadvantages of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01C7/112H01C17/00
Inventor 刘宏玉孔慧蒋冬梅马学鸣
Owner EAST CHINA NORMAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com