Sterilization containers comprising polyester compositions formed from 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 1,4-cyclohexanedimethanol

Abstract

Described are infant-care sterilization containers comprising polyester compositions comprising polyesters which comprise (a) a dicarboxylicacidcomponent having terephthalic acid residues; optionally, aromatic dicarboxylic acid residues or aliphatic dicarboxylic acid residues or ester residues thereof; 2,2,4,4-tetramethyl-1,3-cyclobutanediol residues; and 1,4-cyclohexanedimethanol residues.

Description

CROSS-REFERENCES TO RELATED APPLICATIONS [0001] This application claims priority under 35 U.S.C. §119(e) to U.S. Provisional Application Ser. No. 60 / 691,567 filed on Jun. 17, 2005, U.S. Provisional Application Ser. No. 60 / 731,454 filed on Oct. 28, 2005, U.S. Provisional Application Ser. No. 60 / 731,389, filed on Oct. 28, 2005, U.S. Provisional Application Ser. No. 60 / 739,058, filed on Nov. 22, 2005, and U.S. Provisional Application Ser. No. 60 / 738,869, filed on Nov. 22, 2005, U.S. Provisional Application Ser. No. 60 / 750,692 filed on Dec. 15, 2005, U.S. Provisional Application Ser. No. 60 / 750,693, filed on Dec. 15, 2005, U.S. Provisional Application Ser. No. 60 / 750,682, filed on Dec. 15, 2005, and U.S. Provisional Application Ser. No. 60 / 750,547, filed on Dec. 15, 2005, all of which are hereby incorporated by this reference in their entireties.FIELD OF THE INVENTION [0002] The present invention generally relates to infant-care sterilization containers comprising a polyester compositio...

AI Technical Summary

Benefits of technology

[0010] It is believed that certain infant-care sterilization containers comprising polyester compositions formed from terephthalic acid, an ester thereof, or mixtures thereof, 1,4-cyclohexanedimethanol and 2,2,4,4-tetramethyl-1,3-cyclobutanediol with certain monomer compositions, inherent viscosities and / or glass transition temperatures are superior to polyesters known in the art and to polycarbonate with respect to one or more of high impact strengths, hydrolytic stability, toughness, chemical resistance, good color and clarity, long crystallization half-times, low ductile to brittle transition temperatures, lower specific gravity, and thermoformability. These compositions are believed to be similar to polycarbonate in heat resistance and are still processable on the standard industry equipment.

[0147] Also, in one aspect, use of the polyester compositions of the invention minimizes and / or eliminates the drying step prior to melt processing or thermoforming.

Problems solved by technology

This polyester crystallizes rapidly upon cooling from the melt, making it very difficult to form amorphous articles by methods known in the art such as extrusion, injection molding, and the like.

While these copolyesters are useful in many end-use applications, they exhibit deficiencies in properties such as glass transition temperature and impact strength when sufficient modifying ethylene glycol is included in the formulation to provide for long crystallization half-times. For example, copolyesters made from terephthalic acid, 1,4-cyclohexanedimethanol, and ethylene glycol with sufficiently long crystallization half-times can provide amorphous products that exhibit what is believed to be undesirably higher ductile-to-brittle transition temperatures and lower glass transition temperatures than the compositions revealed herein.

Although bisphenol-A polycarbonate has many good physical properties, its relatively high melt viscosity leads to poor melt processability and the polycarbonate exhibits poor chemical resistance.

It is also difficult to thermoform.

Generally, however, these polymers exhibit high inherent viscosities, high melt viscosities and / or high Tgs (glass transition temperatures) such that the equipment used in industry can be insufficient to manufacture or post polymerization process these materials.