Absorbent article

Abstract

Absorbent articles and processes for making absorbent articles are provided. The process includes spraying onto a fibrous web a blend containing superabsorbent polymer particles, superabsorbent forming monomer, initiator and water, and subjecting the web to polymerization conditions. The resulting web is useful as an absorbent article particularly in disposable hygiene products.

Description

[0001] The present invention relates to an absorbent article, particularly an absorbent article which is useful in personal care products.DESCRIPTION OF THE RELATED ART[0002] Personal care products for the absorption of body fluids are known. Such products include adult incontinence products, diapers, training pants, feminine care products, wound dressings and the like. As a general rule, such personal care products generally comprise an amount of a cellulosic fiber such as wood pulp fluff. Wood pulp fluff is known to be a suitable absorbent for body fluids. As a general rule, 1 gram of wood pulp fluff is able to absorb from about 5 to about 8 grams of a discharged body fluid such as urine. A personal care product such as an infant diaper, generally has an absorbent capacity of at least about 200 to 400 grams of urine. Thus, when such an infant diaper is formed from wood pulp fluff, a relatively large quantity of wood pulp fluff must be employed.[0003] In order to reduce the amount ...

AI Technical Summary

Benefits of technology

[0030] The superabsorbent forming monomers are present in the sprayable blends at a level of from about 15 to 50 percent by weight, preferably from 17 to 40 percent by weight, most preferably from 20 to 35 percent by weight. If the level of superabsorbent forming monomer in the sprayable blend is too low, the resulting web is likely to have poor performance characteristics. Within the preferred ranges, the conversion of superabsorbent forming monomer into polymer, when subjected to polymerization conditions, is generally much better. Also, increasing the relative amount of superabsorbent forming monomer in the sprayable blend generally reduces the amount of water in the sprayable blend. This is beneficial since it requires time, energy and expense to remove additional water from the final web. .

Problems solved by technology

Nonetheless, the use of such high absorbency materials is not without problems.

For example, some high absorbency materials are known to cause gel blocking.

Thus, while the high absorbency materials may be able to absorb an initial insult (in other words, exposure to fluid), subsequent insults are unable to pass through the now swollen high absorbency material.

As a result, subsequent insults tend to pool and run off of the absorbent product resulting in leakage.

While the structures described in the referenced patents have often proven beneficial, they have not completely solved the problems associated with the use of high-absorbency materials.

This is because the cost of such high-absorbency materials is generally greater than the cost of a material such as wood pulp fluff.

The high-absorbency materials are not generally able to absorb urine at the rate at which it is applied.

This may lead to leakage in absorbent structures having high concentrations of absorbent materials.

Such a structure reduces the likelihood of superabsorbent shifting and thereby creating regions of high and low concentration of superabsorbent which can result in uneven absorption of fluids.

If the level of superabsorbent forming monomer in the sprayable blend is too low, the resulting web is likely to have poor performance characteristics.

It has been observed that if the level of superabsorbent polymer particles is too high, premature polymerization can occur in the sprayable blend even in the absence of any other initiators.

Low neutralization levels (less than 50 mole percent) tend to result in superabsorbent polymers having low absorbency properties.

Large particles over 300 microns are undesired since they may tend to clog the nozzle of spray equipment used to spray the sprayable blend.

Also, large particles may cause the absorbent article to have an abrasive feel.

Ethylene glycol was found to be an undesired solvent because it tends to swell the superabsorbent polymer particles and their surfaces becomes tacky which results in undesired particle agglomeration.

In addition, ethylene glycol is undesirable because of its toxicity and biodegradability properties.

A common undesirable trend seen among most commercially available diapers on the market today is the fact that strikethrough times tend to increase with successive doses of fluid during rewet testing.

With conventional fluff-based absorbent structures the cellulosic fibers can lose resiliency and collapse when wetted.

As a result, the liquid uptake rate of the wetted structures may become too low to adequately accommodate subsequent, successive fluid insults.

Swelling of the particles can then diminish the void volume of the absorbent structure and reduce the ability of the structure to rapidly uptake fluid.