Photocured cyanoacrylate adhesives

A technology of cyanoacrylate and acrylate, which is applied in the field of ester copolymer adhesives, can solve the problems that the bonding performance needs to be improved and the brittleness of the adhesive is high, and achieve high bonding strength, fast curing ability, good adhesion The effect of knot strength

Inactive Publication Date: 2007-07-11
DALIAN POLYTECHNIC UNIVERSITY
View PDF4 Cites 35 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For example, U.S. Patents USP6,906,112, USP6,867,241, USP6,734,221, and USP6,726,795 report a light-curing cyanoacrylate adhesive respectively, which are cured by a photoinitiator, but the brittleness of the adhesive is higher, and the adhesive Junction performance needs to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Photocured cyanoacrylate adhesives
  • Photocured cyanoacrylate adhesives

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Prepare photocurable cyanoacrylate adhesive according to the ratio in the table below, take 134.80g of methyl a-cyanoacrylate, add 0.20g of ferrocene, photocuring initiator 2-hydroxy-2-methyl-1-benzene Base-1-acetone 5.00g, dimethoxyphenyl acetophenone 5.00g, after dissolving, add isobornyl methacrylate 40.00g, 1,6-hexanediol diacrylate 9.00g, methacrylate phosphoric acid 3.00 g of ester and 3.00 g of Deqian 1121 adhesion promoter were mixed uniformly to obtain light-curable cyanoacrylate adhesive.

[0022] components

Embodiment 2

[0024] Prepare photocurable cyanoacrylate adhesive according to the ratio in the table below, take 172.60g of α-methyl cyanoacrylate, 7.20g of α-allyl cyanoacrylate, add 0.20g of methyl ferrocene, phthalate Formic anhydride 1.00g, photocuring initiator 2,4,6-trimethylbenzoyldiphenylphosphine oxide 3.00g, after dissolving, add propylene glycol diacrylate 6.00g, trimethylolpropane triacrylate 8.00g, Deqian 1121 adhesion promoter 2.00g, mixed evenly to obtain photocurable cyanoacrylate adhesive.

[0025] components

Embodiment 3

[0027] Prepare photocurable cyanoacrylate adhesive according to the ratio in the table below, take 161.60g of ethyl cyanoacrylate, add 0.20g of ferrocene, 1.60g of phthalic anhydride, photocuring initiator dimethoxy 2.00g of phenylacetophenone, 2.00g of 1-hydroxycyclohexyl phenone, after dissolving, add 20.00g of isobornyl methacrylate, 10.00g of dipropylene glycol diacrylate, 2.60g of Deqian 1121 adhesion promoter, mix Evenly, a photocurable cyanoacrylate adhesive is obtained.

[0028] components

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an optical solidifying cyanacrylate binder, which comprises the following parts: 65. 00-90.00% alpha-cyanacrylate, 5. 00-30.00% (methyl) acrylate, 0.10-4. 00% adhesion accelerant, 0.01-2. 00% stabilizer and 0.10-5. 00% optical initiator. the invention is fit for binding metal, plastic, rubber, wood, polyolefin and fluorine product, which possesses excellent binding effect.

Description

technical field [0001] The present invention relates to an ester copolymer binder, especially an acrylate copolymer; wherein it also relates to its raw material cyanoacrylate monomer. In addition, the present invention also relates to the fact that the adhesive can adopt dual curing technologies of light curing and moisture curing. Background technique [0002] When the α-cyanoacrylate adhesive is applied to the surface of the adherend, it can quickly polymerize and solidify in the presence of traces of water, and it can be used in a very short period of time for certain inert materials such as polyethylene and Teflon. Almost all materials can be bonded. Due to such a superior property, α-cyanopropylene carboxylate adhesive is widely used as a room temperature curing one-component instant adhesive for bonding metal, plastic, rubber, wood, etc. Generally, cyanoacrylate adhesives do not cure well when the surface is exposed to air. They rely on the surface moisture of the ma...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09J4/04
Inventor 刘彦军赵欣
Owner DALIAN POLYTECHNIC UNIVERSITY
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com