Metal color decorative thin slice and decorative metal plate

A metal color and metal plate technology, which is applied in the field of decorative metal plates and metal color decorative sheets, can solve problems such as processing obstacles and deformation, and achieve the effect of small thermal deformation

Inactive Publication Date: 2007-03-07
角正三郎
View PDF2 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] On the other hand, in recent years, from the viewpoint of reducing the weight of metal plates, imparting sound absorption properties, imparting vibration damping properties, and imparting heat insulation properties, decorative metal plates combining metal plates and plastic sheets have been developed. It has been widely used in the field of home appliances and weak currents of various home appliances and AV equipment. When this laminated composite is used to coat parts that have undergone secondary processing such as bending, piercing, cutting, and deep drawing, the following will occur. The problem is that the molten resin flows out from the cutting part and the piercing processing part, which hinders the post-processing. The molten resin shrinks greatly during the cooling and solidification process, so the vicinity of the cutting processing part will be deformed.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Metal color decorative thin slice and decorative metal plate
  • Metal color decorative thin slice and decorative metal plate
  • Metal color decorative thin slice and decorative metal plate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0072] Co-extruded polypropylene resin modified with maleic anhydride (modification rate 0.8% by weight, tensile stress at 5% elongation is 80MPa) and polypropylene resin (tensile stress at 5% elongation is 120MPa) and made into thin slices. The thickness of the modified polypropylene is 20 μm, and the thickness of the polypropylene is 20 μm. Corona treatment (6KW, processing speed 20m / min) was performed on the polypropylene resin side of the obtained sheet to adjust the surface tension to 45dyne / cm or more, and then a polyester-based adhesive (Dainichi Seika Co., Ltd.: Seikabond E295 ), dry-laminated with 50 μm-thick aluminum foil that has been subjected to hairline processing. A light black transparent polyurethane resin ink was applied to the aluminum foil by gravure printing, and then, a 25 μm-thick polyester adhesive (Dainichi Seika Co., Ltd.: Seikabond E295) was dry laminated on the printed surface. A polyester film (manufactured by Toyobo) was used to provide a transp...

Embodiment 2

[0082] In Example 1, instead of the hairline-processed aluminum foil having a thickness of 50 μm, a polypropylene film obtained by subjecting a 30-μm-thick hairline-processed polypropylene film to 500 Ȧ of aluminum evaporation film treatment was used, A decorative steel plate was obtained in the same manner as in Example 1.

Embodiment 3

[0084] A polypropylene resin modified with maleic anhydride (modification ratio: 0.8% by weight, tensile stress at 5% elongation: 80 MPa) was extruded to form a sheet. The thickness of the flakes was 30 μm. Corona treatment (6KW, processing speed 20m / min) was carried out on one side of the obtained sheet, the surface tension was adjusted to be more than 45dyne / cm, and then a polyester-based adhesive (Dainichi Seika Co., Ltd.: Seikabond E295) was used, Dry lamination is carried out with 50 μm thick aluminum foil with hairline processing. A light black transparent polyurethane resin ink was applied to the aluminum foil by gravure printing, and then, a 25 μm-thick polyester adhesive (Dainichi Seika Co., Ltd.: Seikabond E295) was dry laminated on the printed surface. A polyester film (manufactured by Toyobo) was used to provide a transparent resin layer.

[0085] Next, an ionizing radiation-curable resin paint (composition shown below) was applied on the transparent resin layer ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile stressaaaaaaaaaa
thicknessaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a decorate sheet with metallic color. Wherein, it is formed by modified polyolefin resin layer, metal foil layer, and transparent film layer which selects at least one of modified polypropylene, polyethylene and ethene-propone rubber as main component that passed with non-saturated carboxylic acid or non- saturated carboxylic acid derivate, while the extending stress at 5% length is 25-500MPa. Therefore, the inventive sheet will not flow resin at the section in cutting or holing process.

Description

technical field [0001] The present invention relates to a metallic color decorative sheet which can be used as a surface material for house interior decoration such as kitchen doors, storage doors, etc., and as a surface material for home appliances such as refrigerators, etc., and to provide the surface with a metallic color pattern design, and A decorative metal plate using this sheet. Background technique [0002] Conventionally, as surface materials for such residential interior materials, home appliances such as refrigerator doors, and kitchen doors, there are painted steel sheets coated on metal sheets, and vinyl chloride films filled with metal powder. A decorative sheet made of polyester film is attached to a decorative metal plate on a steel plate with an adhesive. In the coated steel sheet, the coating film peels off during processing, or cracks are caught in the coating film, which may cause problems in workability, or easily cause damage to the coating film. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B27/00
Inventor 角正三郎飞鸟政宏小泉进
Owner 角正三郎
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com