Ultraviolet light solidified wear resistant lacquer in use for coating layer on surface of dense board plastes

A technology of surface coating and ultraviolet light, which is applied in the direction of coating, polyurea/polyurethane coating, etc., can solve the problems of poor wear resistance, and achieve the effect of excellent wear resistance, clear wood grain and soft matte effect

Inactive Publication Date: 2005-11-16
湖南亚大新材料科技股份有限公司
View PDF1 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to overcome the problem of poor wear resistance of the existing UV-curable coatings coated on the surface of density boards, and provide a UV-curable wear-resistant coating for the surface coating layer of density boards

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ultraviolet light solidified wear resistant lacquer in use for coating layer on surface of dense board plastes
  • Ultraviolet light solidified wear resistant lacquer in use for coating layer on surface of dense board plastes
  • Ultraviolet light solidified wear resistant lacquer in use for coating layer on surface of dense board plastes

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] Hexafunctional acrylate modified amino resin 30%

[0038] Hexafunctional Urethane Acrylate 10%

[0039] Bisphenol A epoxy acrylate 10%

[0040] Trimethylolpropane Triacrylate 30%

[0041] 2-Methyl-2-hydroxyester-1-oxyphenylpropane (Darocure 1173 Ciba product) 5%

[0042] Matting Powder (OK 500 Degussa, Germany) 8%

[0043] Al 2 o 3 Powder (KD203 Hangzhou Xinglong) 7%

[0044] Mix the above components in a reaction kettle, heat to a temperature of 50-60°C, stir evenly for 0.5-3 hours, and disperse and emulsify for 0.5-3 hours. After cooling, the UV-curable wear-resistant coating specially used for the density plate of the heat-pressed paper film of the present invention is obtained. The paint was coated on the tinplate plate and the density plate with heat-pressed paper film with a wire bar, and its performance was measured after UV curing. The results are shown in Table 1.

Embodiment 2

[0046] Trifunctional acrylate modified amino resin 35%

[0047] Hexafunctional Urethane Acrylate 10%

[0048] Bisphenol A epoxy acrylate 15%

[0049] Trimethylolpropane Triacrylate 30%

[0050] 2-Methyl-2-hydroxyester-1-oxyphenylpropane (Darocure 1173 Ciba product) 3%

[0051] Matting powder (OK 500 Germany Degussa) 2%

[0052] Al 2 o 3 (KD 203 Hangzhou Xinglong) 5%

[0053] Prepared according to the method of Example 1, the UV-curable wear-resistant coating dedicated to the density plate of the present invention was obtained.

Embodiment 3

[0055]Hexafunctional acrylate modified amino resin 30%

[0056] Hexafunctional Urethane Acrylate 10%

[0057] Bisphenol A Epoxy Methacrylate 5%

[0058] Pentaerythritol Triacrylate 20%

[0059] Propoxylated Trimethylolpropane Trimethacrylate 10%

[0060] Ethoxylated Trimethylolpropane Triacrylate 5%

[0061] 2-Methyl-2-hydroxyester-1-oxyphenylpropane (Darocure 1173 Ciba product) 5%

[0062] Matting Powder (OK 500 Degussa, Germany) 8%

[0063] al 2 o 3 Powder (KD 203 Hangzhou Xinglong) 7%

[0064] Prepared according to the method of Example 1, the UV-curable wear-resistant coating dedicated to the density plate of the present invention can be obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
wear coefficientaaaaaaaaaa
Login to View More

Abstract

An ultraviolet solidified antiwear paint for the surface of high-density board with hot-pressed surficial paper layer contains proportionally acrylate (or methylacrylate) modified amino resin, polyurethane acrylate or polyurethane methylacrylate, epoxy acrylate or epoxy methyl acrylate, acrylate or methylacrylate, optical trigger, antiwear inorganic powder and dulling powder.

Description

technical field [0001] The invention belongs to the photocurable paint in the field of chemical industry, and relates to an ultraviolet light curable wear-resistant paint used for woodware, especially a surface coating layer of a density board that has been heat-pressed with a paper film. Background technique [0002] At present, laminate flooring has been widely used in large quantities. The manufacturing process of laminate flooring is generally as follows: medium density floor (MDF) is hot-pressed with a paper film impregnated with melamine, and covered with a very thin layer of aluminum oxide particles. As reported in US Patent No. 5,654,091, the laminated floor using this process is very rough, easily loses gloss, and has a poor surface effect. The U.S. patent uses a layer of 100um thick thermoplastic film to replace the paper film soaked in melamine. As a result, the surface is very smooth, and a very ideal surface effect is obtained, basically...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/14
Inventor 胡辉何吉钢曾进粟亚红
Owner 湖南亚大新材料科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More