Process for preparing magnetic powder and sintered magnet and product produced thereby

A technology of sintered magnets and manufacturing methods, applied in the direction of inductance/transformer/magnet manufacturing, inorganic material magnetism, electrical components, etc., can solve the problems of unreasonable raw material formula, high intrinsic coercive force, and low intrinsic coercive force temperature coefficient And other issues

Active Publication Date: 2005-08-17
HENGDIAN GRP DMEGC MAGNETICS CO LTD
View PDF1 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The invention mainly solves the single crystal structure caused by the iron in the ferrite sintered magnet being completely trivalent due to the unreasonable raw material formula in the production process of the prior art. When other substances are added in the sintering process, the crystal structure is very Easy to change, seriously affecting the magnetic properties
[0007] The present invention also solves the problems in the prior art that the ferrite has high residual magnetic induction, high coercive force, high intrinsic coercive force, high magnetic energy product and low intrinsic coercive force temperature coefficient, etc. Problem; provide a formula that can comprehensively and effectively optimize the parameters of ferrite and the method of manufacturing the ferrite powder and sintered ferrite
[0008] At the same time, the present invention solves the technical problem that the batching and sintering processes in the prior art must meet the charge balance conditions in non-stoichiometric conditions, which adversely affects the performance of the batching and products; it provides an easy-to-configure, The obtained product has superior performance and is compatible with reasonable magnet powder and sintered magnet

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Process for preparing magnetic powder and sintered magnet and product produced thereby
  • Process for preparing magnetic powder and sintered magnet and product produced thereby
  • Process for preparing magnetic powder and sintered magnet and product produced thereby

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0077] The following raw materials are used as raw materials:

[0078] Fe 3 o 4 Powder and Fe 2 o 3 powder (of which Fe 2 o 3 The purity of the powder ≥ 99.2wt%, the original average particle size of the particles: 1.0um) 85.6wt%

[0079] SrCO 3 Powder (purity ≥ 98.0wt%, original average particle size of particles: 2.1um) 12.1wt%

[0080] La 2 o 3 Powder (purity ≥ 99.0wt%, original average particle size of particles: 0.8um) 1.5wt%

[0081] co 2 o 3 Powder (purity ≥ 99.0wt%, original average particle size of particles: 0.8um) 0.8wt%

[0082] Perform physical and chemical analysis on various raw materials, take them in a molar ratio, then add raw materials and additives (specific substances) in a wet ball mill, mix them, and then dry them, pre-burn them in the air at 1210°C, and keep them warm for 2 hours. Obtain a granulated calciner with a ferrite main phase as:

[0083] Sr 1-X La x [(Fe 3+ a Fe 2+ b ) 12-y co y ]O 19 .

[0084] The dispersant of 0.4wt%...

Embodiment 2

[0104] The following raw materials are used as raw materials:

[0105] Fe 3 o 4 Powder and Fe 2 o 3 powder (of which Fe 2 o 3 The purity of the powder ≥ 99.2wt%, the original average particle size of the particles: 1.0um) 84.5wt%

[0106] SrCO 3 Powder (purity ≥ 98.0wt%, original average particle size of particles: 2.1um) 10.8wt%

[0107] La 2 o 3Powder (purity ≥ 99.0wt%, original average particle size of particles: 0.8um) 3.2wt%

[0108] co 2 o 3 Powder (purity ≥ 99.0wt%, original average particle size of particles: 0.8um) 1.5wt%

[0109] Add raw materials and additives in a wet ball mill, mix them, then dry them, pre-fire them in the air at 1200°C, and keep them warm for 1.5 hours to obtain granular pre-fired materials, so that they have a ferrite main phase:

[0110] Sr 1-X La x [(Fe 3+ a Fe 2+ b ) 12-y co y ]O 19 .

[0111] The obtained calcined material was dry coarsely pulverized in a continuous dry vibrating ball mill for 10 minutes, and the avera...

Embodiment 3

[0131] The following raw materials are used as raw materials:

[0132] Fe 3 o 4 Powder and Fe 2 o 3 powder (of which Fe 2 o 3 The purity of the powder ≥ 99.2wt%, the original average particle size of the particles: 1.0um) 82.5wt%

[0133] SrCO 3 Powder (purity ≥ 98.0wt%, original average particle size of particles: 2.1um) 7.6wt%

[0134] La 2 o 3 Powder (purity ≥ 99.0wt%, original average particle size of particles: 0.8um) 6.3wt%

[0135] co 2 o 3 Powder (purity ≥ 99.0wt%, original average particle size of particles: 0.8um) 3.6wt%

[0136] Use the following materials as additives

[0137] SiO 2 : Powder (purity ≥ 99.0wt%, original average particle size of particles: 0.5um) 0.2wt%

[0138] CaCO 3 : Powder (purity ≥ 99.0wt%, original average particle size of particles: 1.5um) 0.2wt%

[0139] Add raw materials and additives in a wet ball mill, mix them, then dry them, pre-fire them in the air at 1250°C, and keep them warm for 2.5 hours to obtain granular pre-fire...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Average particle sizeaaaaaaaaaa
Average particle sizeaaaaaaaaaa
Average particle sizeaaaaaaaaaa
Login to View More

Abstract

This invention relates to magnetic material field and especially to a process method improvement and its formula to hexagonal magnetic lead ferrite powder and sinter magnetism, wherein the said magnetism or magnetic powder has one-Curie temperature with A,R, B and Fe hexagonal ferrite main phase and the following molecular formula: A1-XRx[(Fe3+aFe2+b)12-yBy]zO19, through adding positive three Co and optimizing the formula and improving the magnetism crystal aeolotropism constant K1.

Description

technical field [0001] The invention relates to the field of magnetic materials, in particular to an improvement in the manufacturing method of hexagonal magnetoplumbite ferrite magnet powder, a sintered magnet and its formula. Background technique [0002] Sintered permanent magnet ferrite has the advantages of stable magnetic properties and strong demagnetization resistance; it is not easy to rust and does not need to be coated with a protective layer; it is hard and brittle and can be used for special tool processing and cutting; Suitable for automobiles, household appliances, industrial automation and other industries. The sintered permanent ferrite is made of hexagonal sintered ferrite magnets, especially the hexagonal magnetoplumbite ferrite is more widely used. Oxide permanent magnet ferrite material mainly adopts strontium ferrite (SrO·6Fe) with magnetoplumbite (M type) hexagonal structure 2 o 3 ) and barium ferrite (BaO·6Fe 2 o 3 ) as a raw material to sinter m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B22F3/10B22F9/00H01F1/10H01F1/11H01F41/02
Inventor 何时金何震宇丁伯明包大新何军义
Owner HENGDIAN GRP DMEGC MAGNETICS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com