Composition for increasing hydrophobic and oleophobic behavior of paper product and method of making the same

A composition and oleophobic technology, applied in papermaking, paper coatings, adding water repellents, etc., can solve the problems of poor strength, water resistance, low oil resistance, penetration, etc., to improve water resistance, ensure printability, and ensure writeability. Effect

Inactive Publication Date: 2005-06-22
中科纳米技术工程中心有限公司
View PDF0 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] One of the purposes of the present invention is to provide a composition for improving the hydrophobicity and oleophobicity of paper products, so as to solve the problem of poor strength, low water resistance and oil resistance of current paper products and paper packaging materials, and the phenomenon of penetration will occur after a long time of use. question

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Example 1, in parts by weight.

[0029] The paint formulation is

[0030] China clay 100 parts

[0031] 10 parts styrene butadiene latex

[0032] Japan Asahi Glass Company AG-710 Organic Fluorine Resin Emulsion 5 parts

[0033] Cross-linkable paraffin emulsion 4 parts

[0034] Carboxymethyl cellulose 0.2 parts

[0035] Appropriate amount of water

[0036] Make 100 parts of China clay into a water slurry with a solid content of 65%, stir at high speed for 1 hour, then turn to low speed stirring and simultaneously add 10 parts of styrene butadiene latex, 5 parts of organic fluororesin emulsion AG-710, 4 1 part of crosslinkable paraffin wax emulsion, 0.2 part of carboxymethyl cellulose, and finally diluted with water to make the solid content 60%.

Embodiment 2

[0037] Embodiment 2, in parts by weight.

[0038] The paint formulation is:

[0039] Calcium carbonate 100 parts

[0040] Acrylic latex 12 parts

[0041] Ciba's Oleophobol C organic fluorine resin emulsion 8 parts

[0042] Cross-linkable paraffin emulsion 2 parts

[0043] High viscosity hydroxyethyl fiber 0.2 parts

[0044] Appropriate amount of water

[0045] Make 100 parts of calcium carbonate into a water slurry with a solid content of 70%, stir at high speed for 1 hour, then turn to low speed and simultaneously add 10 parts of acrylic latex, 8 parts of organic fluorine resin emulsion OleophobolC, and 2 parts of crosslinkable paraffin Emulsion, 0.2 parts of high-viscosity hydroxyethyl fiber, and finally diluted with water to make its solid content 65%.

Embodiment 3

[0046] Embodiment 3, in parts by weight.

[0047] The paint formulation is:

[0048] Titanium dioxide 50 parts

[0049] Starch 10 parts

[0050] 6 parts of Scotchgard FC organic fluorine resin emulsion of 3M Company in the United States

[0051] 3 parts cross-linkable paraffin emulsion

[0052] High viscosity hydroxyethyl fiber 0.2 parts

[0053] Appropriate amount of water

[0054]10 parts starch, starch suspended in cold water (20°C) at a concentration of 12% by weight and then dispersed by continuous steam injection jet cooking where the starch slurry was pumped at a pressure of 67 psia and a temperature of 148°C" in the steam stream of the "cooking chamber". Samples were collected and cooled to 65°C until use. At the same time, 50 parts of titanium dioxide were made into a water slurry with a solid content of 50%, stirred at a high speed for 1 hour, then turned to low speed and simultaneously added 80 parts of the prepared starch slurry, 8 parts of organic fluorores...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a composition for increasing hydrophobic and oleophobic behavior of paper product and method which comprises, preparing slurry from 50-100 parts of gasket material, or gasket material and pigment, high speed agitating, low speed agitating and charging 1-20 parts of bonding agent, 1-10 parts of organic fluorine resin emulsion, 0.5-15 parts of crosslinkable wax emulsion, 0.05-5 parts of flowing deformation modifier, diluting to obtain a solid content of 20-80%.

Description

technical field [0001] The invention relates to a hydrophobic and oleophobic composition, in particular to a hydrophobic and oleophobic composition for endowing paper packaging materials and products and paper disposable tableware with excellent water and oil repellency and a preparation method thereof. Background technique [0002] The impact of plastic packaging materials and products and plastic disposable tableware on the environment has aroused widespread concern, and some aspects have restricted their use. Paper packaging materials and products and paper disposable tableware are emerging high-grade materials, which are environmentally friendly, can be printed, and have certain water repellency. Moreover, it is resistant to folding, wear-resistant, recyclable and recyclable, and has no pollution to the environment. It is an ideal material to replace plastics. In recent years, paper packaging materials and products and disposable tableware have...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D21H19/44D21H21/16
Inventor 江雷刘必前李兰
Owner 中科纳米技术工程中心有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More