Threaded joint for steel pipe with excellent seizure and corrosion resistances

A technology for threaded fasteners and steel pipes, applied in the direction of pipes/pipe joints/fittings, damage protection, pipeline anticorrosion/rust protection, etc., which can solve problems such as wear, air tightness, reduction, and unstable joint fixation

Inactive Publication Date: 2004-04-07
NIPPON STEEL CORP
View PDF0 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, threaded joints are prone to rust to form air bubbles in the solid lubricating coating or cause peeling, which in turn makes joint fixing unstable, resulting in wear or a decrease in airtightness

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Threaded joint for steel pipe with excellent seizure and corrosion resistances
  • Threaded joint for steel pipe with excellent seizure and corrosion resistances
  • Threaded joint for steel pipe with excellent seizure and corrosion resistances

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0103] The following examples are given to illustrate the invention and are not intended to limit the invention. In the following description, the mating surface of the pin, including the threaded portion and the unthreaded metal contact portion, is referred to as the pin surface, while the corresponding portion of the box is referred to as the box surface.

[0104] Threaded joints (outside diameter: 7 inches, wall thickness: 0.408 inches) are made of carbon steel A, Cr-Mo steel B, 13% Cr steel C and high alloy steel D (see Table 1 for each composition) material, the surface treatment of the pin surface and the box surface is as shown in Table 2, which briefly describes the steel marking of threaded joints (Table 1), the conditions under which the pretreatment including the formation of the bottom layer is carried out, and Conditions for forming a solid lubricating coating or a liquid lubricating coating without heavy metal powder. Measure the thickness of primer and lubricio...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
depthaaaaaaaaaa
surface roughnessaaaaaaaaaa
Login to View More

Abstract

A threaded joint for steel pipe, comprising a pin and a box allowed to be fitted to each other, wherein a porous zinc or zinc alloy layer as a lower layer by a projection plating method and a solid lubrication film (film containing lubricating powder in organic or inorganic binder) or a liquid lubricating film not containing heavy metal powder (example: liquid film formed mainly of high base organic metallic salt such as high base sulphonate) as an upper layer are provided on the thread part and the metal contact part without thread of at least either of the pin and box, whereby the threaded joint can provide excellent seizure resistance, corrosion resistance, and airtightness even after exposed to high temperature, and is allowed to be tightened and loosened repeatedly in a hot oil well without using compound grease containing heavy metal powder.

Description

technical background [0001] The present invention relates to a threaded joint for steel pipes, especially oil well pipes, which has improved wear resistance, rust resistance and air tightness, and can be used without the use of liquid greases containing heavy metal powders, such as complex greases in the case of. Background technique [0002] Oil well tubulars used in oil well drilling, such as pipes and casings, are generally connected to each other by threaded joints. In the past, the depth of oil wells was generally 2,000 to 3,000 meters, but recently, the depth of oil wells in offshore oil wells and other deep wells can reach 8,000 to 10,000 meters. Threaded joints of oil well pipes are subjected to various forces in the service environment, including loads such as axial tension generated by the weight of oil well pipes and threaded joints, the combination of internal and external pressures, and Increased geothermal. Therefore, threaded joints must be able to remain a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): E21B17/042C10M103/00C10M103/02C10M103/06C10M105/72C10M105/74C10M107/38C10M143/02C10M145/20C10M145/24C10M149/18C10M151/04C10M155/00C10M155/02C10M159/20C10M159/22C10M159/24C10N10/02C10N10/04C10N10/06C10N10/08C10N10/12C10N10/14C10N20/00C10N30/06C10N30/12C10N40/00C10N50/02C10N50/08F16L15/00F16L15/04F16L58/08F16L58/18
CPCC10M2207/283C10N2230/12C10M2205/022F16L58/182C10M2219/024C10M2207/2623C10M2223/04F16L15/001C10M2209/084C10M169/02C10M2207/126C10N2230/52F16L58/08C10M2219/0463C10M2223/045C10M2207/0285Y10T428/1393C10N2030/52C10N2030/12
Inventor 后藤邦夫安乐敏朗
Owner NIPPON STEEL CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com