Formula and technique for high strength double face leatheroid of chemical fiber with plastic being coated

A kind of artificial leather, high-strength technology, applied in textiles and papermaking, etc., can solve the problems of artificial leather with a large amount of glue, unstable quality, unreasonable material selection, etc., achieve important economic and social benefits, reduce workload, and improve work. The effect of efficiency

Inactive Publication Date: 2003-05-07
安兰祚 +2
View PDF0 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the artificial leather used in my country's truck tarpaulins is made of polyester staple fiber fabrics, which are made of plastic coating. Due to the unreasonable selection of base fabric materials and the shortcomings of the plastic coating method and formula process, PVC rubber is used in the base fabric. Rolling on cloth, rolling, plasticizing, and process production, resulting in artificial leather with many glues, heavy weight, unstable quality, waste material, low strength, rough surface, narrow surface width, easy aging, and short life. Meet the requirements of railway standards

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0045] 1. Preparation of PVC glue

[0046] ①According to the components and weights listed below, weigh them in turn and simply mix the components in an appropriate container for stirring:

[0047] Component Weight (kg)

[0048] 1. PVC paste resin 100

[0049] 2. Flame retardant system

[0050] Antimony trioxide (Sb 2 o 3 ) 5~50

[0051] Phosphate Triester 5~80

[0052] 3. Plasticizing system

[0053] Octyl phthalate (DOP) 5D~20D

[0054] Dioctyl Zedioate (DOS) 0~50

[0055] 4. Stable system

[0056] Non-toxic liquid compound stabilizer 0~15

[0057] ② Transfer to a high-speed mixer and stir evenly;

[0058] ③Put the stirred rubber on the three-roller grinder for two grindings

[0059] 2. Coating production process

[0060] ①One-time plastic coating process roadmap is as follows:

[0061] Cloth release—→impregnation—→rolling—→smoothing—→vertical oven—→top width

[0062] —→Horizontal Oven—→Cutting Side—→Rolling Cloth

[0063] ②Secondary plastic coating process r...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

An artificial dual-surface leather is prepared by coating plastics on both surfaces of high-strength chemical fibre fabric. Its preparing process includes preparing PVC mucilage containing flame retardant, plasticizer and stabilizer, feeding cloth, immersing, rolling levelling, baking, plasticizing and winding.

Description

technical field [0001] The invention relates to a method for producing artificial leather, in particular to the manufacture of high-strength chemical fiber-coated plastic-coated double-sided artificial leather for railway wagon tarpaulins. Background technique [0002] At present, the artificial leather used in my country's truck tarpaulins is made of polyester staple fiber fabrics, which are made of plastic coating. Due to the unreasonable selection of base fabric materials and the shortcomings of the plastic coating method and formula process, PVC rubber is used in the base fabric. Rolling on cloth, rolling, plasticizing, and process production, resulting in artificial leather with many glues, heavy weight, unstable quality, waste material, low strength, rough surface, narrow surface width, easy aging, and short life. Meet the requirements of railway standards. Contents of the invention [0003] The purpose of the present invention is to overcome the shortcomings of the e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06N3/06
Inventor 安兰祚赵文昌李荣峰刘洪新高绪坤
Owner 安兰祚
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap