A preparation process and technology of magnetic particles, which are used in the manufacture of inductors/transformers/magnets, ferrous oxides, iron oxides/iron hydroxides, etc.

Pending Publication Date: 2022-08-05
阜阳德润磁材科技有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to provide a magnetic particle preparation process, which cannot be filled with nitrogen gas in the device during the preparation process. The chemical properties of nitrogen gas are relatively inactive, which can avoid the reaction with the external gas during the preparation process, resulting in the failure of the preparation result. The problem of preset standards occurs to solve the problems raised in the above background technology

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Magnetic particle preparation process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0030] In the description of the present invention, it should be understood that the terms "center", "longitudinal", "lateral", "length", "width", "thickness", "upper", "lower", "front", " rear, left, right, vertical, horizontal, top, bottom, inside, outside, clockwise, counterclockwise, etc., or The positional relationship is based on the orientation or positional relationship shown in the accompanying drawings, only for the convenience of describing the present invention and simplifying the description, rather than indicating or implying that the device or element referred to must have a specific orientation, be constructed and operated in a specific orientation, Therefore, it should not be construed as a limitation of the present invention.

[0031] In the description of the present invention, "plurality" means two or more, unless otherwise expressly and specifically defined.

[0032] In the description of the present invention, it should be noted that, unless otherwise ex...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a magnetic particle preparation process, and belongs to the technical field of magnetic particle preparation. The method comprises the following steps: extracting silicate and carbonate in sodium hydroxide, standing the extracted solution for 20 minutes, screening out impurities in the solution, pouring the screened solution into cooling equipment for cooling, standing the standing extracting solution, cooling and standing, magnetically stirring in a magnetic stirrer, mixing ferric chloride and polyacrylic acid, putting the mixed substance into a closed vessel, and uniformly stirring. Filling the inner cavity of the closed vessel with nitrogen, increasing the temperature of the inner cavity of the closed vessel while filling the nitrogen, magnetically stirring the mixed substance, heating to 220 DEG C, treating, pouring a sodium hydroxide solution into a mixed solution of ferric chloride and polyacrylic acid, observing whether the color change of the solution meets the requirement, and packaging and leaving a factory. In the preparation process, the device is filled with nitrogen, the chemical property of the nitrogen is inactive, and the situation that the preparation result does not reach the preset standard due to the fact that the nitrogen reacts with external gas in the preparation process can be avoided.

Description

technical field [0001] The present invention relates to the technical field of magnetic particle preparation, and more particularly, to a magnetic particle preparation process. Background technique [0002] Magnetic particles refer to colloidal composite materials that can be uniformly dispersed in a certain base liquid. Because of its superparamagnetic properties, high specific surface area, and functional groups that can be modified. Therefore, antigens / antibodies, enzymes, nucleic acids / oligonucleotides, small molecule drugs, etc. are immobilized on its surface. In addition to surgical operations, chemical drugs, biological toxins and radionuclides are mainly used, but the selectivity of drug treatment is low. , large toxic and side effects, anti-tumor drugs quickly disappear from the site of action and other defects. Polymer-coated magnetic particles for in vivo therapy have become a new technology for drug-targeted release. In this technology, anticancer drugs are co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08J3/12C08J3/14C08L33/02C08K3/22H01F41/02C01G49/08
CPCC08J3/12C08J3/14H01F41/02C01G49/08C08J2333/02C08K2003/2265C08K2003/2275
Inventor 张威峰冷俊志
Owner 阜阳德润磁材科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap