Rapid crystallization hot melt adhesive for counter material and preparation method of rapid crystallization hot melt adhesive

A hot-melt adhesive and crystallization technology, applied in the direction of adhesives, adhesive types, polyurea/polyurethane adhesives, etc., can solve the problems of wrinkling due to high temperature deformation, affecting the appearance of shoes, and uncomfortable wearing, etc., to achieve improved Crystallization speed, good heat resistance, fast crystallization effect

Pending Publication Date: 2022-07-22
河北邦泰氨纶科技有限公司 +1
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, there are still some problems and room for improvement in the current commercially available Gangbao materials, because Gangbao materials are melted and processed from hot melt adhesive particles into hot-melt film for reuse. In order to pursue processing efficiency, the processing factory hopes that Gangbao materials can be formed as quickly as possible.
In addition, Gangbao also has the phenomenon of wrinkling during wearing or being deformed by high temperature, which not only affects the appearance of the shoes, but also causes problems such as uncomfortable wearing and grinding feet

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rapid crystallization hot melt adhesive for counter material and preparation method of rapid crystallization hot melt adhesive
  • Rapid crystallization hot melt adhesive for counter material and preparation method of rapid crystallization hot melt adhesive
  • Rapid crystallization hot melt adhesive for counter material and preparation method of rapid crystallization hot melt adhesive

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0054] A kind of quick crystallization hot melt adhesive for gang treasure material, the raw material comprises the following components by mass:

[0055] 100 parts of polyester polyol, 3.5 parts of diisocyanate, 0.3 part of antioxidant, 0.2 part of anti-hydrolysis agent, 0.3 part of light stabilizer, 0.2 part of lubricant and 0.01 part of catalyst;

[0056] Wherein, the polyester polyol is a mixture of polyhexanediol 1,9-nonanedicarboxylate diol (M=5500) and polyethylene adipate diol (M=6000) in a mass ratio of 2:1 ;

[0057] The diisocyanate is a mixture of toluene diisocyanate and hydrogenated diphenylmethane diisocyanate in a mass ratio of 2:1;

[0058] The preparation method of fast crystallization hot melt adhesive for Gangbao material is as follows:

[0059] (1) adding the poly-1,9-nonanedicarboxylate hexanediol of M=5500 and the polyhexylene adipate diol of M=6000 into the insulation kettle A according to the mass ratio of 2:1 , then add antioxidant, anti-hydrolysis a...

Embodiment 2

[0064] A kind of quick crystallization hot melt adhesive for gang treasure material, the raw material comprises the following components by mass:

[0065] 100 parts of polyester polyol, 4.1 parts of diisocyanate, 0.4 part of antioxidant, 0.3 part of anti-hydrolysis agent, 0.3 part of light stabilizer, 0.3 part of lubricant and 0.006 part of catalyst;

[0066] Wherein, the polyester polyol is a mixture of polybutylene 1,9-nonanedicarboxylate diol (M=5000) and polybutylene adipate diol (M=5000) in a mass ratio of 1:1 ;

[0067] The diisocyanate is a mixture of diphenylmethane diisocyanate and hexamethylene diisocyanate in a mass ratio of 1:1.

[0068] The preparation method of fast crystallization hot melt adhesive for Gangbao material is as follows:

[0069] (1) adding the polybutylene 1,9-nonane dicarboxylate diol of M=5000 and the polybutylene adipate diol of M=5000 into the insulation kettle A according to mass ratio 1:1 , then add antioxidant, anti-hydrolysis agent, ligh...

Embodiment 3

[0074] A kind of quick crystallization hot melt adhesive for gang treasure material, the raw material comprises the following components by mass:

[0075] 100 parts of polyester polyol, 2.8 parts of diisocyanate, 0.6 part of antioxidant, 0.4 part of anti-hydrolysis agent, 0.5 part of light stabilizer, 0.4 part of lubricant and 0.01 part of catalyst;

[0076] Among them, the polyester polyol is a mixture of polyethylene 1,9-nonanedicarboxylate diol (M=5000) and polyethylene adipate diol (M=7000) in a mass ratio of 1:2 ;

[0077] Diisocyanate is a mixture of toluene diisocyanate and hexamethylene diisocyanate in a mass ratio of 4:1;

[0078] The preparation method of fast crystallization hot melt adhesive for Gangbao material is as follows:

[0079] (1) Polyethylene 1,9-nonane dicarboxylate diol of M=5000 and polyethylene adipate diol of M=7000 are added in insulation kettle A according to mass ratio 1:2 , then add antioxidant, anti-hydrolysis agent, light stabilizer, lubrica...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a rapid crystallization hot melt adhesive for a counter material and a preparation method of the rapid crystallization hot melt adhesive, and relates to the technical field of polyurethane hot melt adhesives. The hot melt adhesive is prepared from the following raw materials in parts by mass: 100 parts of polyester polyol, 2 to 5 parts of diisocyanate, 0.3 to 0.6 part of an antioxidant, 0.2 to 0.4 part of an anti-hydrolysis agent, 0.3 to 0.5 part of a light stabilizer, 0.2 to 0.4 part of a lubricant and 0.005 to 0.01 part of a catalyst, the polyester polyol is single polyester polyol or mixed polyester polyol, and the diisocyanate is single diisocyanate or mixed diisocyanate. The preparation method comprises the following steps: mixing the polyester polyol, the antioxidant, the anti-hydrolysis agent, the light stabilizer, the lubricant and the catalyst, heating, uniformly stirring, reacting with the diisocyanate, granulating, and drying to obtain the rapid crystallization hot melt adhesive for the counter material.

Description

technical field [0001] The invention relates to the technical field of polyurethane hot-melt adhesives, in particular to a rapid crystallization hot-melt adhesive for gang treasure materials and a preparation method thereof. Background technique [0002] As one of the most important materials for shoemaking, Gangbao is used in huge amounts every year. It is mainly used for shaping the front toe and heel of shoes. After shaping, the shape of the shoes is straight and round, and it is not easy to deform. The comfort and beauty of the shoes have been greatly improved. . [0003] Gangbao is divided into chemical film Gangbao (Shuigangbao) and hot melt glue Gangbao. Chemical film Gangbao is not environmentally friendly, it needs to be brushed to be compounded, and it is easy to deform. In the past, leather pulp Gangbao and chemical film Gangbao were used in shoemaking. , using water immersion softening method and soaking solvent (toluene) softening method, but the product is thi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J175/06C08G18/42
CPCC09J175/06C08G18/4238C08G18/4202C08G2170/20
Inventor 韩风安郎增科贾振兴郑玉成李帅滑冰涛赵莉莉郎东辉郎潇李思奇
Owner 河北邦泰氨纶科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products