Environment-friendly high-whiteness domestic ceramic product and preparation process thereof

A ceramic product, high white technology, applied in the field of ceramics, can solve problems such as difficulty in guaranteeing product performance indicators, narrow firing temperature range, easy deformation and brittleness of products, etc., to achieve large firing range, high yield, and enhanced flexural strength and the effect of thermal shock resistance

Pending Publication Date: 2022-06-21
福建省德化县合和陶瓷技术开发有限公司
View PDF9 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the main varieties of Dehua white porcelain are tea sets, sculpture porcelain, etc. The firing temperature range of the existing technology is very narrow and only about 10°C. The product is easily deformed and brittle, with a flexural strength of about 60 MPa, a whiteness of about 76, and thermal stability. It is 160-20℃, so it is difficult to guarantee the performance indicators of the product in the production process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly high-whiteness domestic ceramic product and preparation process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] This embodiment provides an environmentally friendly high-whiteness daily-use ceramic product, including the following components in parts by weight: 30 parts of Dehua Jinzhukeng kaolin, 8 parts of albite, 3 parts of quartz, 8 parts of zirconium silicate, and 3 parts of bone ash Parts, 25 parts of composite pellets.

[0022] Among them: the composite granular material is obtained by coating fluorite tailings powder and calcined smithsonite powder with Dehua Longque red clay dispersion slurry, and then granulating and drying, with a particle size of 300 mesh. The Dehua Longque red clay dispersion slurry is The mass fraction ratio of raw material, fluorite tailings powder and calcined smithsonite powder is 30:0.8:0.2. The calcination temperature of the calcined smithsonite powder is 800° C., and the particle size is 3 μm; the particle size of the fluorite tailings powder is 3 μm.

[0023] The treatment process of the Dehua Longque red clay dispersion slurry is as follows...

Embodiment 2

[0026] This embodiment provides an environment-friendly high-whiteness daily-use ceramic product, including the following components in parts by weight: 15 parts of Dehua Jinzhukeng kaolin, 12 parts of albite, 6 parts of quartz, 6 parts of zirconium silicate, and 5 parts of bone ash Parts, 30 parts of composite pellets.

[0027] Wherein: the composite granular material is obtained by coating fluorite tailings powder and calcined smithsonite powder with Dehua Longque red clay dispersion slurry, and then granulating and drying, with a particle size of 200 mesh. The Dehua Longque red clay dispersion slurry is The mass fraction ratio of raw material, fluorite tailings powder and calcined smithsonite powder is 25:0.5:0.5. The calcination temperature of the calcined smithsonite powder is 850° C., and the particle size is 4 μm; the particle size of the fluorite tailings powder is 4 μm.

[0028] The treatment process of the Dehua Longque red clay dispersion slurry is as follows: the ...

Embodiment 3

[0031] This embodiment provides an environmentally friendly high-whiteness daily-use ceramic product, including the following components in parts by weight: 20 parts of Dehua Jinzhukeng kaolin, 10 parts of albite, 5 parts of quartz, 8 parts of zirconium silicate, and 4 parts of bone ash. Parts, 35 parts of composite pellets.

[0032] Wherein: the composite granular material is obtained by coating fluorite tailings powder and calcined smithsonite powder with Dehua Longque red clay dispersion slurry, and then granulating and drying, with a particle size of 400 mesh. The Dehua Longque red clay dispersion slurry is The mass fraction ratio of raw material, fluorite tailings powder and calcined smithsonite powder is 50:0.8:0.4. The calcination temperature of the calcined smithsonite powder is 850° C., and the particle size is 4 μm; the particle size of the fluorite tailings powder is 2.5 μm.

[0033] The treatment process of the Dehua Longque red clay dispersion slurry is as follow...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of ceramics, and particularly discloses an environment-friendly high-whiteness domestic ceramic product which comprises Dehua kaolin, albite, quartz, zirconium silicate and composite granules. The composite granules are prepared by coating fluorite tailing powder and calcined smithsonite powder with Dehua Longque red soil dispersed slurry, granulating and drying. The fluorite tailings sintered ceramic is high in whiteness, high in strength, good in thermal shock resistance, suitable for domestic ceramics, energy-saving, environment-friendly, large in sintering range and high in yield due to the fact that the fluorite tailings are recycled. Particularly, in the staged heating, oxidizing and firing process, silicon and aluminum in the Dehua longque red soil dispersed slurry react to serve as mullite crystals, the fluorite tailing powder and the calcined smithsonite powder act synergistically to reduce the melting temperature of the red soil silicon and aluminum, continuous curing of the mullite crystals is accelerated, and a compact framework is formed; the breaking strength and the thermal shock resistance of the green body are favorably enhanced.

Description

technical field [0001] The invention belongs to the technical field of ceramics, and in particular relates to an environment-friendly high-whiteness daily-use ceramic product and a preparation process thereof. Background technique [0002] Dehua is one of the three ancient porcelain capitals in China, as famous as Jingdezhen in Jiangxi and Liling in Hunan. Dehua white porcelain has the reputation of "ivory white", "lard white" and "velvet white" because of its fine production, firm texture, crystal clear jade, and glaze like grease. It is in the white porcelain system of our country. It has a unique style, occupies an important position in the history of ceramic development, and has the reputation of "Oriental Art" internationally. [0003] At present, the main varieties of Dehua white porcelain are tea sets, sculpture porcelain, etc. The firing temperature range of the existing technology is very narrow and only about 10°C. The product is easily deformed and brittle, with ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/04C04B33/13C04B33/132C04B33/24C04B35/185C04B35/622
CPCC04B33/04C04B33/132C04B33/24C04B33/13C04B35/185C04B35/62204C04B2235/3418C04B2235/3472C04B2235/3427C04B2235/9607C04B2235/5436C04B2235/9646Y02P40/60
Inventor 李桂贤刁龙海孙秋丽
Owner 福建省德化县合和陶瓷技术开发有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com