Three-layer composite release film for 3D printing process and preparation method of three-layer composite release film

A technology of layer composite and release film, which is applied in the field of three-layer composite release film for 3D printing process and its preparation, can solve the problems of low light transmittance and easy cracking, and achieve high light transmittance, production efficiency and finished product The effect of high pass rate and long service life

Active Publication Date: 2022-06-10
NINGBO CHANGYANG TECH
View PDF10 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The present invention aims to overcome the problems that the release film in the prior art has the defects of release agent migration, low light transmittance, or easy cracking along the MD direction of tape casting, and is not suitable for 3D printing process, and provides a 3D printing process Using a three-layer composite release film and a preparation method thereof, respectively adopting poly-4-methyl-1-pentene and long-chain branched modified poly-4-methyl-1-pentene as the surface layer and the middle layer, the prepared The release film has excellent release properties without adding a release agent, and the film has high light transmittance and good mechanical properties, which can meet the requirements for use in the 3D printing process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Three-layer composite release film for 3D printing process and preparation method of three-layer composite release film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Comparative Example 1: (The release film is all made of poly-4-methyl-1-pentene):

[0033] Comparative Example 2 (the release film is all made of long-chain branched modified poly-4-methyl-1-pentene):

[0034] The preparation method of the release film for the above-mentioned 3D printing process is as follows:

[0035] Comparative example 3 (too much addition of grafted monomer in B layer):

[0036] Comparative example 4 (only 1,4-butanediol diacrylate is used as graft monomer in layer B):

[0037] Comparative example 5 (only maleic anhydride is used for the graft monomer in layer B):

Embodiment 2

[0039] Table 1: Performance test results of release film

[0040] The release film in Comparative Example 1 is only made of poly-4-methyl-1-pentene, without adding long-chain branched modified poly-4-methyl-1-pentene as the middle layer, although it has better The releasability, but its elongation at break is significantly reduced compared with Example 1, and the service life is reduced. The release film in Comparative Example 2 is all made of long-chain branched modified poly-4-methyl-1-pentene. Although it has better mechanical properties, the haze of the film increases and the release property decreases. Also do not meet the requirements for use in the 3D printing field.

[0041] In Comparative Example 3, during the preparation of long-chain branched modified poly-4-methyl-1-pentene, the amount of grafted monomer added was too much, which exceeded the scope of the present invention, and the permeability of the prepared release film Compared with Example 1, the light rate ...

Embodiment 3

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a three-layer composite release film for a 3D printing process and a preparation method of the three-layer composite release film. The three-layer composite release film comprises a layer B and layers A arranged on the two sides of the layer B, the component of the layer A is poly (4-methyl-1-pentene); the component of the layer B is long-chain branch modified poly (4-methyl-1-pentene); the ratio of the total mass of the layer A to the mass of the layer B is 10: (1-5); the preparation method of the long-chain branch modified poly (4-methyl-1-pentene) comprises the following steps: mixing poly (4-methyl-1-pentene), a grafting monomer and an initiator, and carrying out melt extrusion to obtain the long-chain branch modified poly (4-methyl-1-pentene), and the grafting monomer comprises 1, 4-butanediol diacrylate and maleic anhydride. According to the invention, the poly (4-methyl-1-pentene) and the long-chain-chain modified poly (4-methyl-1-pentene) are respectively used as the surface layer and the middle layer, so that the prepared release film has excellent release property under the condition that a release agent is not added, and the film is high in light transmittance and good in mechanical property and can meet the use requirements in the 3D printing process.

Description

technical field [0001] The invention relates to the technical field of release films, in particular to a three-layer composite release film for 3D printing process and a preparation method thereof. Background technique [0002] Stereolithography (SLA) is a relatively mature 3D printing technology. The photocuring system uses photosensitive resin as raw material, irradiates with low-power ultraviolet light, and shapes the photosensitive resin in a fixed temperature and humidity environment (normal temperature 18-28°C, humidity ≤ 60%-70%). Compared with selected laser sintering (SLS) or selected laser melting (SLM), the light curing system has a simple structure and low cost, and can realize the rapid generation of high-precision complex models. This characteristic determines that the light curing 3D printing technology has more For a wide range of product applications and development prospects. [0003] The release film used in 3D printing SLA is a film material that is fix...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B27/28B32B27/06B29C48/16B29C59/04B29C64/20B29C64/245B33Y30/00
CPCB32B27/28B32B27/08B29C48/16B29C59/04B29C64/20B29C64/245B33Y30/00B32B2307/412B32B2307/558
Inventor 刘欣然赵红陈鹏蒋富云毛丽莎
Owner NINGBO CHANGYANG TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products