A kind of inorganic ecological stone preparation process and inorganic ecological stone maintaining high luminosity

A preparation process and technology of ecological stone, applied in the direction of manufacturing tools, grinding/polishing equipment, control of workpiece feed movement, etc. Long-lasting decorative effect, increased gloss retention and water resistance, the effect of avoiding subtle chemical reactions

Active Publication Date: 2022-07-12
GUANGDONG NADE NEW MATERIALS CO LTD
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the existing inorganic ecological stone has low gloss, which limits its application scenarios
In addition, due to the existence of silicate and calcium powder inside the inorganic ecological stone, the silicate and calcium powder will slowly hydrolyze when encountering the air or the water vapor seeping up from the formation, forming alkaline compounds with low solubility; When the temperature rises and the water vapor evaporates, these alkaline compounds will be precipitated from the inside. With the further volatilization of water, the insoluble alkaline compounds will be precipitated on the surface of the inorganic stone, gradually causing the surface of the stone to whiten. The phenomenon of dusting not only reduces the durable quality of the product but also affects the appearance of the product

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of inorganic ecological stone preparation process and inorganic ecological stone maintaining high luminosity
  • A kind of inorganic ecological stone preparation process and inorganic ecological stone maintaining high luminosity
  • A kind of inorganic ecological stone preparation process and inorganic ecological stone maintaining high luminosity

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-3 and comparative example 1-7

[0060] Take the same batch of inorganic ecological stone produced by a company on the market, and perform high-gloss surface treatment on the above-mentioned inorganic ecological stone according to the preparation process of Examples 1-3 and Comparative Examples 1-7 respectively.

Embodiment 1

[0062] A process for preparing inorganic ecological stone with high luminosity, comprising the following steps:

[0063] (1) Filling and processing steps of large particle pretreatment liquid:

[0064] Use grinding equipment to pre-polish the surface of the inorganic ecological stone, make the surface of the inorganic ecological stone flat, clean the debris on the surface of the inorganic ecological stone, preheat the inorganic ecological stone, and control the temperature at 55 °C; temperature, the large particle pretreatment I was dropped into and coated on the surface of the inorganic ecological stone, and the addition amount of the large particle pretreatment I solution was 10g / m 2 , the drop-in time of large particle pretreatment I is controlled at 5s, the grinding coating time is 30s, the grinding disc revolution speed of the grinding equipment is 90r / min, and the abrasive rotation speed installed on the grinding disc is 900r / min, so that it penetrates into the inorganic...

Embodiment 2

[0070] A process for preparing inorganic ecological stone with high luminosity, comprising the following steps:

[0071] (1) Filling and processing steps of large particle pretreatment liquid:

[0072] Use grinding equipment to pre-polish the surface of the inorganic ecological stone, make the surface of the inorganic ecological stone flat, clean the debris on the surface of the inorganic ecological stone, preheat the inorganic ecological stone, and control the temperature at 60 °C; temperature, the large particle pretreatment I was dropped into and coated on the surface of the inorganic ecological stone, and the addition amount of the large particle pretreatment I liquid was 13g / m 2, the drop-in time of large particle pretreatment I is controlled at 6s, the grinding and coating time is 40s, the grinding disc revolution speed of the grinding equipment is 115r / min, and the abrasive rotation speed installed on the grinding disc is 1000r / min, so that it penetrates into the inorga...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
surface temperatureaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation process for maintaining high luminosity of inorganic ecological stone and inorganic ecological stone, and relates to the technical field of inorganic stone preparation. The particle high-gloss nano-liquid high-gloss treatment step, (3) the gloss-enhancing waterproof liquid gloss-enhancing and waterproof treatment step. The inorganic ecological stone prepared by the preparation process of the inorganic ecological stone of the invention can achieve excellent results in terms of gloss, gloss retention, antifouling and waterproof ability, whitening of the stone surface, and dust protection ability.

Description

technical field [0001] The invention relates to the field of inorganic stones, in particular to a preparation process of inorganic ecological stones with high luminosity and inorganic ecological stones. Background technique [0002] At present, stone is a type of building material that is used in the field of architectural decoration and is in great demand. Natural stone (granite, marble) is naturally solemn and has good weather resistance and durability. It is widely used in outdoor floors, walls, cylinders, legs, bases and steps of buildings. Compared with building materials such as tiles In general, artificial stone materials are easy to obtain, easy to form, and low cost, and their application in the field of architectural decoration has attracted more and more attention. Inorganic ecological stone is an artificial stone that is closest to natural stone in the imitation stone category. Its internal structure is a crystal structure similar to cement solidification, mainl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B41/52B24B7/22B24B49/00
CPCC04B41/52B24B7/22B24B49/006C04B41/4905C04B41/4539C04B41/5035C04B41/5006C04B41/483C04B41/4876C04B41/47Y02W30/91
Inventor 张中明刘鸿福
Owner GUANGDONG NADE NEW MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com