Preparation method of traditional Chinese medicine molecule doped polypyrrole nanoparticles
A technology of polypyrrole nanometer and polyvinylpyrrolidone, which is applied in the field of preparation of polypyrrole nanoparticle, can solve the problems of difficult control and preparation, achieve long-term inhibition of remaining tumor activity, simple preparation process, and low cost
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0029] This embodiment provides a preparation method of polypyrrole nanoparticles doped with traditional Chinese medicine molecules, comprising the following steps:
[0030] S1. Add 1g of polyvinylpyrrolidone (PVP) and 25ml of ultrapure water into a 50ml round bottom flask, stir for 0.5h at room temperature, and mark it as No. 1;
[0031] Add 0.0907g dopamine after the stirring is completed;
[0032] Add 0.25ml of the prepared ginsenoside Rh1 aqueous solution (40mg / ml);
[0033] S2. Add 130 μL of pyrrole monomer to the solution prepared in step S1, and continue stirring to fully dissolve it;
[0034] S3, add 1ml ferric chloride hexahydrate solution (0.75g / ml) to the solution prepared in step S2, stir for 3h, seal three circles of sealing paper at the bottle mouth, prevent air interference, fully react;
[0035] S4. Centrifuge at a speed of 12000r / min for 30 minutes to fully precipitate. After the reaction is complete, wash with a large amount of ethanol / acetone mixture, and ...
Embodiment 2
[0037] This embodiment provides a preparation method of polypyrrole nanoparticles doped with traditional Chinese medicine molecules, comprising the following steps:
[0038] S1. Add 0.2g polyvinylpyrrolidone (PVP) and 25ml ultrapure water into a 50ml round bottom flask, stir for 0.5h at room temperature, and mark it as No. 1;
[0039] Add 0.3g of dopamine after the stirring is completed;
[0040] Add 0.25ml of the prepared ginsenoside Rh1 aqueous solution (8mg / ml);
[0041] S2. Add 70 μL of pyrrole monomer to the solution prepared in step S1, and continue stirring to fully dissolve it;
[0042] After S3, 10min, add 1ml ferric chloride hexahydrate solution (0.2g / ml) to the solution prepared in step S2, stir for 3h, seal three circles of sealing paper at the bottle mouth, prevent air interference, and fully react;
[0043] S4. Centrifuge at a speed of 12000r / min for 30 minutes to fully precipitate. After the reaction is complete, wash with a large amount of ethanol / acetone mix...
Embodiment 3
[0045] This embodiment provides a preparation method of polypyrrole nanoparticles doped with traditional Chinese medicine molecules, comprising the following steps:
[0046] S1. Add 2g of polyvinylpyrrolidone (PVP) and 25ml of ultrapure water into a 50ml round bottom flask, stir for 0.5h at room temperature, and mark it as No. 1;
[0047] Add 0.0241g dopamine after the stirring is completed;
[0048] Add 0.25ml of prepared ginsenoside Rh1 aqueous solution (80mg / ml);
[0049] S2. Add 570 μL of pyrrole monomer to the solution prepared in step S1, and continue stirring to fully dissolve it;
[0050] After S3, 10min, add 1ml ferric chloride hexahydrate solution (2.50g / ml) to the solution prepared in step S2, stir for 3h, seal three circles of sealing paper at the bottle mouth, prevent air interference, fully react;
[0051] S4. Centrifuge at a speed of 12000r / min for 30 minutes to fully precipitate. After the reaction is complete, wash with a large amount of ethanol / acetone mixt...
PUM
Property | Measurement | Unit |
---|---|---|
Concentration | aaaaa | aaaaa |
Concentration | aaaaa | aaaaa |
Diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com