Hydrogel mask preparation method as well as product and application thereof

A hydrogel mask and composite hydrogel technology, applied in the field of cosmetics, can solve problems such as skin damage, and achieve the effects of prolonging the shelf life and promoting the growth of fibroblasts

Pending Publication Date: 2022-02-11
SHANGHAI NAT ENG RES CENT FORNANOTECH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, some hydrogel components may contain chemical cross-linking agents, such as glutaraldehyde, which may cause potential damage to the skin. Therefore, the use of biological components to prepare hydrogel masks has great application prospects

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hydrogel mask preparation method as well as product and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A hydrogel facial mask, which uses electrospinning to prepare a silk fiber film containing antibacterial nanoparticles, and then co-ferments the silk fiber and sugarcane hydrolyzate to make the bacterial fiber and silk fiber composite and cross-linked to obtain a composite hydrogel Glue mask, prepared according to the following steps:

[0023] (1) Dissolve 0.5g nano-zinc oxide ZnO NPs in a 35% silk fibroin SF solution, mix well at 60°C to obtain a concentrated spinning solution; inject the well-mixed spinning solution into a 10 mL syringe, set The electrospinning voltage is 18kv, the flow rate is 0.25 mL / h, and the electrospinning is carried out within a receiving distance of 18 cm to obtain a silk fiber membrane containing nano-zinc oxide; Autoclave for 20 minutes, dry for later use;

[0024] (2) After the bagasse is hydrolyzed and detoxified, add 1% yeast extract and 0.5% tryptone, sterilize at 121°C, 0.07~0.1MPa for 20 minutes, and use it as a culture medium; then i...

Embodiment 2

[0030] A kind of hydrogel facial mask substrate, is similar to embodiment 1 step, is prepared according to the following steps:

[0031] (1) 1g of ZnO NPs was dissolved in a 40% silk fibroin SF solution, and mixed evenly at 60°C to obtain a concentrated spinning solution; inject the mixed spinning solution into a 10 mL syringe, set the electrostatic The spinning voltage was 18 kv, the electrospinning was carried out at a flow rate of 0.25 mL / h, and within a receiving distance of 18 cm to obtain a silk fibroin fiber membrane containing nano-zinc oxide; Autoclave for 20 minutes, dry for later use;

[0032] (2) After the bagasse is hydrolyzed and detoxified, add 1% yeast extract and 0.5% tryptone, sterilize at 121°C, 0.07~0.1MPa for 20 minutes, and use it as a culture medium; then inoculate Acetobacter acetobacter with 10% inoculum In the culture medium, after mixing evenly, a fermentation broth is obtained;

[0033] (3) Pour the fermentation broth into the culture vessel equip...

Embodiment 3

[0036] A kind of hydrogel facial mask substrate, is identical with embodiment 2 steps, is prepared according to the following steps:

[0037] (1) 1g of ZnO NPs was dissolved in a 40% silk fibroin SF solution, and mixed evenly at 60°C to obtain a concentrated spinning solution; inject the mixed spinning solution into a 10 mL syringe, set the electrostatic The spinning voltage was 18 kv, the electrospinning was carried out at a flow rate of 0.25 mL / h, and within a receiving distance of 18 cm to obtain a silk fibroin fiber membrane containing nano-zinc oxide; Autoclave for 20 minutes, dry for later use;

[0038](2) After the bagasse is hydrolyzed and detoxified, add 1% yeast extract and 0.5% tryptone, sterilize at 121°C, 0.07~0.1MPa for 20 minutes, and use it as a culture medium; then inoculate Acetobacter acetobacter with 10% inoculum In the culture medium, after mixing evenly, a fermentation broth is obtained;

[0039] (3) Pour the fermentation broth into the culture vessel e...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a hydrogel mask preparation method as well as a product and the application thereof. An electrostatic spinning mode is adopted, a fibroin fiber membrane of antibacterial nanoparticles is prepared, then fibroin fibers and sugarcane hydrolysate are co-fermented, bacterial fibers and the fibroin fibers are compounded and crosslinked, and the composite hydrogel mask is obtained. By adopting an electrostatic spinning mode, the nano antibacterial particles are directly woven into fibers, so that the mask base material has antibacterial ability, no additional antibacterial component is needed when the beautifying component is added, and the shelf life of the mask is prolonged. Through the subsequent co-culture fermentation of the fibroin fiber membrane and the sugarcane fermentation liquor, the bacterial cellulose and the fibroin fiber are compounded and cross-linked, so that the hydrogel mask base material is prepared. After the hydrogel mask base material adsorbs beautifying active ingredients rich in sugarcane extracts, a hydrogel mask can be obtained, and the mask has the effects of whitening, moisturizing, diminishing inflammation and promoting fibroblast growth.

Description

technical field [0001] The invention relates to a preparation method of a hydrogel facial mask and its product and application. Specifically relates to a preparation method of bacterial cellulose / silk fiber composite hydrogel facial mask prepared by electrospinning and fermentation processes. The invention belongs to the technical field of cosmetics. Background technique [0002] The improvement of living standards has prompted more people to pay attention to the beauty field. Among them, facial mask is a product for facial skin care and beauty. Because of its convenient use and remarkable effect, it has attracted the attention of beauty lovers and has been widely recognized in the market. Traditional facial masks are usually stick-type, mud-cream-type, etc. These types of facial masks usually contain beautifying liquids, which use their direct contact with the face to promote the nutrients in the mask to enter the stratum corneum of the skin surface to achieve moisturizing...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): A61K8/9794A61K8/9789A61K8/73A61K8/64A61K8/34A61K8/27A61K8/02A61Q19/00A61Q19/02A61P29/00
CPCA61K8/9794A61K8/9789A61K8/735A61K8/64A61K8/345A61K8/27A61K8/0212A61Q19/00A61Q19/02A61P29/00A61K2800/85A61K2800/413
Inventor 崔大祥徐艳徐颖湉朱君杨迪诚
Owner SHANGHAI NAT ENG RES CENT FORNANOTECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com