Preparation method of plywood for bakelite box

A technology for plywood and bakelite boxes, which is applied in the field of preparation of plywood for bakelite boxes, and can solve problems such as decline, moldy service life, and low adhesive strength

Active Publication Date: 2021-12-10
ANJIE PACKAGING SUZHOU CO LTD
View PDF10 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a preparation method of plywood for bakelite boxes, which is obtained by gluing three veneers with an adhesive, so as to solve the problem that the existing adhesives have low bonding strength, are prone to mildew and have a long service life in a hot oxygen environment fall defect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of plywood for bakelite box
  • Preparation method of plywood for bakelite box
  • Preparation method of plywood for bakelite box

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] A method for preparing plywood for bakelite boxes, which is obtained by gluing three veneer boards together with an adhesive;

[0038] The adhesive includes the following raw materials in parts by weight: 20 parts of modified resin, 3 parts of modified graphene, 3 parts of benzyldimethylamine, 1 part of sulfated castor oil, 1 part of sodium dodecylsulfonate, 1 part of o-phenylphenol parts, 10 parts of water;

[0039] The adhesive is made by the following steps:

[0040] Step S1: Add modified resin, sulfated castor oil, sodium dodecylsulfonate, and water into a stirring tank, and stir for 1 hour at a rotation speed of 1000 r / min to obtain a mixture;

[0041] Step S2: After the mixture and the modified graphene were ultrasonically treated at a frequency of 8 kHz for 30 min, benzyldimethylamine was added and stirred for 3 h at a rotational speed of 1500 r / min to prepare an adhesive.

[0042] Modified resin is made by the following steps:

[0043] Step A1: Add p-chloroto...

Embodiment 2

[0050] A method for preparing plywood for bakelite boxes, which is obtained by gluing three veneer boards together with an adhesive;

[0051] The adhesive includes the following raw materials in parts by weight: 25 parts of modified resin, 4 parts of modified graphene, 4 parts of benzyldimethylamine, 2 parts of sulfated castor oil, 2 parts of sodium dodecylsulfonate, 2 parts of o-phenylphenol parts, 13 parts of water;

[0052] The adhesive is made by the following steps:

[0053] Step S1: Add modified resin, sulfated castor oil, sodium dodecylsulfonate, and water into a stirring tank, and stir for 1.3 hours at a rotation speed of 1200 r / min to obtain a mixture;

[0054] Step S2: ultrasonically treat the mixture and the modified graphene at a frequency of 9 kHz for 35 min, then add benzyldimethylamine, and stir for 4 h at a rotational speed of 1800 r / min to prepare an adhesive.

[0055] Modified resin is made by the following steps:

[0056] Step A1: Add p-chlorotoluene, p-m...

Embodiment 3

[0063] A method for preparing plywood for bakelite boxes, which is obtained by gluing three veneer boards together with an adhesive;

[0064] The adhesive includes the following raw materials in parts by weight: 30 parts of modified resin, 5 parts of modified graphene, 5 parts of benzyldimethylamine, 3 parts of sulfated castor oil, 3 parts of sodium dodecylsulfonate, 3 parts of o-phenylphenol parts, 15 parts of water;

[0065] The adhesive is made by the following steps:

[0066] Step S1: Add modified resin, sulfated castor oil, sodium dodecylsulfonate, and water into a stirring tank, and stir for 1.5 hours at a rotation speed of 1200 r / min to obtain a mixture;

[0067] Step S2: ultrasonically treat the mixture and the modified graphene at a frequency of 10 kHz for 40 min, then add benzyldimethylamine, and stir for 5 h at a rotational speed of 2000 r / min to prepare an adhesive.

[0068] Modified resin is made by the following steps:

[0069] Step A1: Add p-chlorotoluene, p-...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of plywood for a bakelite box. The plywood is prepared by gluing three veneers with an adhesive, and the adhesive comprises the following raw materials in parts by weight: 20-30 parts of modified resin, 3-5 parts of modified graphene, 3-5 parts of benzyl dimethylamine, 1-3 parts of sulfated castor oil, 1-3 parts of sodium dodecyl sulfate, 1-3 parts of o-phenylphenol and 10-15 parts of water; a molecular chain of the modified resin contains a large number of phenothiazine structures, and a six-membered ring is sandwiched between two benzene rings, so that lone pair electrons of sulfur atoms are delocalized on three rings, nitrogen-hydrogen bonds of phenothiazine are easy to break, the sulfur atoms in molecules can be oxidized to form sulfoxide and sulfone compounds, and the adhesive has a very good thermal oxidation resistance effect; and adhesive failure of the plywood does not occur in the use process of the plywood, normal use of the bakelite box is guaranteed, a molecular side chain of the modified resin contains a polyimide molecular chain, and the polyimide molecular chain is matched with the modified graphene, so that the fracture toughness of the adhesive can be enhanced, and the adhesive effect of the adhesive is better.

Description

technical field [0001] The invention relates to the technical field of preparation of bakelite boxes, in particular to a method for preparing plywood for bakelite boxes. Background technique [0002] Plywood is a three-layer or multi-layer board-like material that is made of wood sections that are peeled into veneers or sliced ​​into thin wood, and then glued with adhesives. Usually, odd-numbered veneers are used, and adjacent layers of veneers are used. The fiber direction of the plywood is glued vertically to each other. Plywood is one of the commonly used materials for furniture. The boards are arranged symmetrically on both sides of the center layer or the board core, and the slabs made of glued veneers criss-crossed according to the direction of wood grain are pressed under heating or non-heating conditions, and the number of layers is generally odd , a few also have even numbers, the difference in physical and mechanical properties in the vertical and horizontal direc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B27D1/08C09J187/00C09J11/04C09J11/06C09J11/08
CPCB27D1/08C09J187/005C09J11/04C09J11/06C09J11/08C08L2201/08C08L91/00C08K9/04C08K3/042C08K5/42
Inventor 胡铁林
Owner ANJIE PACKAGING SUZHOU CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products