Graphene oxide and titanium dioxide composite photocatalyst, cleaning mask and preparation method of cleaning mask

A technology of titanium dioxide and graphene, applied in the direction of physical/chemical process catalysts, chemical instruments and methods, cosmetic preparations, etc., can solve problems such as easy leakage, easy skin irritation, peeling, etc., and achieve easy portability, prevention of acne, Strong cleaning effect

Pending Publication Date: 2021-11-05
TIANJIN FUQIN SCI & TECH
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, makeup remover is favored by more and more consumers because of its fast makeup removal and convenient cleaning, but makeup remover is also inconvenient to carry because of the dosage form, and it is more prone to leakage
After the makeup remover is used up, it is necessary to use facial cleanser for secondary cleaning. This cleaning method is cumbersome and brings a lot of inconvenience to consumers. Moreover, makeup remover generally pays attention to efficacy, which is easy to irritate the skin, and the skin is prone to redness, pain, and Peeling, acne and other phenomena

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Graphene oxide and titanium dioxide composite photocatalyst, cleaning mask and preparation method of cleaning mask
  • Graphene oxide and titanium dioxide composite photocatalyst, cleaning mask and preparation method of cleaning mask
  • Graphene oxide and titanium dioxide composite photocatalyst, cleaning mask and preparation method of cleaning mask

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0058]According to a method for preparing a graphene oxide-titanium dioxide composite photocatalyst provided in an embodiment of the second aspect of the present invention, preparing the graphene oxide-titanium dioxide composite photocatalyst described in the graphene oxide photocatalytic cleaning mask includes the following steps:

[0059] Step 1: mixing deionized water and absolute ethanol to obtain a mixed solution 1; dispersing graphene oxide into the mixed solution 1, and ultrasonically dissolving it uniformly to obtain a graphene oxide solution;

[0060] Step 2: adding the titanium-containing substance into the graphene oxide solution and stirring, after stirring evenly, adding acid and deionized water in turn, and continuing to stir until uniform, to prepare a precursor solution containing titanium element and graphene oxide;

[0061] Step 3: Pour the precursor solution into the reaction kettle, keep the first predetermined temperature for the first predetermined time, c...

Embodiment 1

[0077] Such as figure 1 As shown, the flow chart of preparing graphene oxide photocatalytic cleansing mask with titanium dioxide as titanium source in the embodiment of the present invention. Specific steps are as follows:

[0078] Step 1 S01: Mix deionized water and absolute ethanol at a volume ratio of 2:1, weigh a certain amount of graphene oxide, disperse it into the above solution, and dissolve it ultrasonically for 2 to 3 hours to prepare graphite oxide Alkene solution.

[0079] Step 2 S02: Add a certain amount of titanium dioxide to the graphene oxide solution, stir magnetically for 1 to 2 hours, and then ultrasonically clean for 30 minutes to prepare a precursor solution containing titanium and graphene oxide.

[0080] Step 3 S03: Pour the precursor solution into the reaction kettle, maintain the first predetermined temperature for the first predetermined time, cool the container after the reaction, remove the supernatant, perform centrifugation, wash the precipitate...

Embodiment 2

[0093] Such as figure 2 As shown, in the embodiment of the present invention, using tetrabutyl titanate as a titanium source to prepare a flow chart of graphene oxide photocatalytic cleaning mask, the specific steps are as follows:

[0094] Step 1 S01: Take deionized water and absolute ethanol and mix according to the volume ratio of 2:1, weigh a certain amount of graphene oxide, disperse it into the above solution, and ultrasonically dissolve it for 2 hours to 3 hours to prepare Obtain graphene oxide solution.

[0095] Step 2 S02: Take a certain amount of tetrabutyl titanate and add it to the above graphene oxide solution, stir magnetically for 1 hour to 2 hours until it is transparent and uniform, and then add a certain amount of acetic acid and deionized water dropwise to continue Stir for one hour to two hours to prepare a precursor solution containing titanium element and graphene oxide.

[0096] Step 3 S03: Pour the precursor solution into the reaction kettle, maintai...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The embodiment of the invention discloses a graphene oxide and titanium dioxide composite photocatalyst, a cleaning mask and a preparation method of the cleaning mask, and belongs to the technical field of cosmetics and skin care. The graphene oxide photocatalytic mask comprises a mask layer and a backing layer, wherein the mask layer is arranged on the backing layer, and the mask layer comprises the graphene oxide and titanium dioxide composite photocatalyst, a dispersing agent, film-forming resin and a film-forming cosolvent. The invention further discloses the preparation method of the graphene oxide and titanium dioxide composite photocatalyst and the preparation method of the graphene oxide photocatalytic cleaning mask. According to the graphene oxide and titanium dioxide composite photocatalyst, the cleaning mask and the preparation method of the cleaning mask, the strong adsorption capacity of graphene oxide and the photocatalytic performance of titanium dioxide are utilized, oily secretions and oily cosmetics on the face are quickly adsorbed and decomposed, and therefore the facial skin of the human body is cleaned; and meanwhile, the graphene oxide has high antibacterial performance, is suitable for users with acne on the facial skin, and solves the problem of facial cleaning of oily, makeup and skin sensitive people.

Description

technical field [0001] The embodiments of the present invention relate to the technical field of cosmetics and skin care, in particular to a graphene oxide titanium dioxide composite photocatalyst, a cleansing mask and a preparation method thereof. Background technique [0002] With the improvement of people's living standards and people's constant pursuit of beauty, cosmetics have become people's daily necessities, especially the widespread use of color cosmetic products, making people more and more demanding for makeup remover and facial cleansing products. However, makeup remover is favored by more and more consumers because of its fast makeup removal and convenient cleaning, but makeup remover is also inconvenient to carry because of its dosage form, and it is more prone to leakage. After the makeup remover is used up, it is necessary to use facial cleanser for secondary cleaning. This cleaning method is cumbersome and brings a lot of inconvenience to consumers. Moreover...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): A61K8/02A61K8/29A61K8/19A61Q17/00A61Q19/00A61Q19/10B01J21/18B01J21/06
CPCA61K8/0212A61K8/29A61K8/19A61Q17/005A61Q19/008A61Q19/10B01J21/18B01J21/063A61K2800/26B01J35/39
Inventor 王鹤
Owner TIANJIN FUQIN SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap