Spherical stain-resistant pin insulator preparation method

A technology of pin insulators and insulators, which is applied in the direction of pin insulators, insulators, coatings, etc., can solve the problems of easy dirt accumulation on the surface, insufficient surface smoothness, and influence on airflow, etc., to achieve improved hydrophobicity, excellent hydrophobicity, The effect of reducing surface energy

Inactive Publication Date: 2021-10-08
江西东维电气有限公司
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In the natural environment, various dust particles in the atmosphere are attracted by the electric field force or gravity when passing through the insulator, and are deposited on the surface of the porcelain insulator, and the surface of the porcelain insulator is a hydrophilic glaze, and the surface smoothness is not enough. The surface is easy to accumulate dirt, and the shape and structure of porcelain insulators are also easy to affect the airflow when the wind blows, which usually leads to the accumulation of various flying dust

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Spherical stain-resistant pin insulator preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A method for preparing a spherical pollution-resistant pin insulator, comprising the following steps:

[0028] S1. Prepare the insulator body;

[0029] S2, prepare antifouling paint, comprise:

[0030] a. Weigh 30 parts of raw material organosilicon-modified acrylic resin, 20 parts of modified styrene-acrylic emulsion, 4 parts of modified polytetrafluoroethylene wax emulsion, 1 part of modified nano-silicon nitride, and modified mica in the following parts by weight 1 part of powder, 2 parts of modified nano-hydrated silica, 0.5 parts of aluminum borate whiskers, 0.5 parts of nano-microcrystalline cellulose, 1 part of glass microspheres, 2 parts of methyl tributylketoximosilane, 30 parts of ethyl acetate share;

[0031] Among them, the modification method of silicone-modified acrylic resin is: dissolve 10g of orthosilicate in 4mL of ethanol, add 0.01mL of dilute acid, hydrolyze at 70°C for 3 hours; Polycondensate for 2 hours to obtain a silicone oligomer; combine 5 g o...

Embodiment 2

[0041] A method for preparing a spherical pollution-resistant pin insulator, comprising the following steps:

[0042] S1. Prepare the insulator body;

[0043] S2, prepare antifouling coating, comprise:

[0044] a. Weigh 40 parts of raw material organosilicon-modified acrylic resin, 25 parts of modified styrene-acrylic emulsion, 6 parts of modified polytetrafluoroethylene wax emulsion, 2 parts of modified nano-silicon nitride, and modified mica in the following parts by weight 2 parts of powder, 3 parts of modified nano-hydrated silica, 2 parts of aluminum borate whiskers, 1 part of nano-microcrystalline cellulose, 3 parts of glass beads, 4 parts of methyl tributylketoxime silane, 35 parts of ethyl acetate share;

[0045] Among them, the modification method of silicone-modified acrylic resin is as follows: dissolve 10g of orthosilicate in 4mL of ethanol, add 0.01mL of dilute acid, and hydrolyze it at 80°C for 2 hours; Polycondensate for 1.5 hours to obtain a silicone oligome...

Embodiment 3

[0055] A method for preparing a spherical pollution-resistant pin insulator, comprising the following steps:

[0056] S1. Prepare the insulator body;

[0057] S2, prepare antifouling coating, comprise:

[0058] a. Weigh 50 parts of raw material organosilicon modified acrylic resin, 30 parts of modified styrene-acrylic emulsion, 8 parts of modified polytetrafluoroethylene wax emulsion, 3 parts of modified nano-silicon nitride, and modified mica in the following parts by weight 3 parts of powder, 4 parts of modified nano-hydrated silica, 2.5 parts of aluminum borate whiskers, 1.5 parts of nano-microcrystalline cellulose, 5 parts of glass microspheres, 6 parts of methyl tributylketoxime silane, 40 parts of ethyl acetate share;

[0059] Among them, the modification method of silicone-modified acrylic resin is as follows: dissolve 10g of orthosilicate in 4mL of ethanol, add 0.01mL of dilute acid, and hydrolyze at 90°C for 1 hour; Polycondensate for 1 hour to obtain a silicone ol...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a spherical stain-resistant pin insulator preparation method, and relates to the technical field of insulators. The method comprises the steps: preparing an insulator body; preparing a stain-resistant coating material: drying modified nano hydrated silicon dioxide, modified nano silicon nitride and modified mica powder, adding the dried modified nano hydrated silicon dioxide, modified nano silicon nitride and modified mica powder into an organic silicon modified acrylic resin, uniformly mixing, grinding, continuously adding modified polytetrafluoroethylene wax emulsion, uniformly mixing to obtain a mixture I, adding aluminum borate whiskers, nanocrystalline cellulose and glass micro-beads added into modified styrene-acrylic emulsion, uniformly mixing to obtain a second mixture, uniformly mixing the first mixture and the second mixture, and then adding methyltris (methylethylketoximino) silane and ethyl acetate to prepare a stain-resistant coating material; and coating an insulator body with the stain-resistant coating material. According to the invention, that the prepared insulator has a stain-resistant effect and is not easy to generate pollution flashover.

Description

technical field [0001] The invention relates to the field of insulators, in particular to a method for preparing a spherical pollution-resistant pin-type insulator. Background technique [0002] An insulator is a device that can withstand voltage and mechanical stress installed between conductors of different potentials or between conductors and grounding members. The main function of the insulator is to achieve electrical insulation and mechanical fixation, for which various electrical and mechanical performance requirements are stipulated. If under the specified operating voltage, lightning overvoltage and internal overvoltage, there will be no breakdown or flashover along the surface; under the specified long-term and short-term mechanical load, no damage or damage will occur; After long-term operation under electric load and various environmental conditions, there will be no obvious deterioration; the fittings of the insulator will not produce obvious corona discharge p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/12C09D125/14C09D183/04C09D127/18C09D101/04C09D7/62C09D7/63C09D7/61C09D7/65H01B19/04H01B17/20
CPCC09D143/04C09D7/62C09D7/63C09D7/61C09D7/70C09D7/65H01B19/04H01B17/20C08K2201/011C08L25/14C08L83/04C08L27/18C08L1/04C08K13/06C08K5/5419C08K9/06C08K3/34C08K9/02C08K3/36C08K7/08C08K7/20C08K5/5465
Inventor 李敬李冬生黄建萍
Owner 江西东维电气有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com