Antibacterial sanitary mobile phone film and preparation method thereof

A mobile phone film and hygienic technology, which is applied in the field of antibacterial and hygienic mobile phone film and its preparation, can solve the problems of affecting the service life of mobile phones, being fragile and not resistant to scratches, and easily breeding various bacteria.

Active Publication Date: 2021-10-01
江西昊泽光学膜科技有限公司
View PDF14 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Mobile phone film is usually used to beautify the mobile phone, and at the same time protect the LCD screen of the mobile phone. As we all know, with the development of the economy and the continuous improvement of people's living standards, smart phones have become an indispensable tool in people's lives. Smart phone screens Made of glass, it is fragile and not resistant to scratches, which affects the service life of the mobile phone. Therefore, tempered glass mobile phone film has become a necessity;
[0003] However, today's smart phones use large-screen touch screens, and various operations are performed on the mobile phone through human fingers. Because there are many bacteria on the hands, it is easy to contaminate the mobile phone film. Due to the particularity of electronic products, washing and other methods cannot be used. Clean, so it is often easier to breed various bacteria on the mobile phone film, resulting in worrying about the hygiene of the mobile phone, which in turn affects the health of the user;

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antibacterial sanitary mobile phone film and preparation method thereof
  • Antibacterial sanitary mobile phone film and preparation method thereof
  • Antibacterial sanitary mobile phone film and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] Present embodiment is a kind of preparation method of antibacterial antifouling emulsion, comprises the following steps:

[0048] A1: Add 150mL of tetrahydrofuran, 3.0g of magnesium powder, and 15.4g of 2-bromopropane into a three-necked flask equipped with a stirrer, a constant pressure dropping funnel, and an airway, and pass in nitrogen protection, at room temperature and at a stirring rate of 200r / min The reaction was stirred for 2h under the condition of , then 5.2g of anhydrous lithium chloride was added, and the stirring was continued for 5min, and then 40mL of 2-bromo-3,3,3-trifluoropropene solution was added dropwise at -60°C, 2 -Bromo-3,3,3-trifluoropropene solution is a solution formed by dissolving 2-bromo-3,3,3-trifluoropropene in tetrahydrofuran according to 44g:100mL, and the dropping rate is controlled at 1mL / min. After the completion, the reaction was stirred at a constant temperature for 2 hours to obtain intermediate 1, and then carbon dioxide gas was...

Embodiment 2

[0054] Present embodiment is a kind of preparation method of antibacterial antifouling emulsion, comprises the following steps:

[0055] A1: Add 150mL of tetrahydrofuran, 3.0g of magnesium powder, and 15.4g of 2-bromopropane into a three-necked flask equipped with a stirrer, a constant pressure dropping funnel, and an airway, and pass in nitrogen protection, at room temperature and at a stirring rate of 300r / min The reaction was stirred for 3h under the condition of , then 5.2g of anhydrous lithium chloride was added, and the stirring was continued for 10min, and then 40mL of 2-bromo-3,3,3-trifluoropropene solution was added dropwise at -60°C, 2 -Bromo-3,3,3-trifluoropropene solution is a solution formed by dissolving 2-bromo-3,3,3-trifluoropropene in tetrahydrofuran according to 44g:100mL, and the rate of addition is controlled at 2mL / min. After the completion, the reaction was stirred at a constant temperature for 3 hours to obtain intermediate 1, and then carbon dioxide gas...

Embodiment 3

[0061] This embodiment is a preparation method of an antibacterial and hygienic mobile phone film, comprising the following steps:

[0062] Step 1: Weigh 40 parts of antibacterial and antifouling emulsion from Example 1, 1 part of curing agent, 5 parts of cosolvent, 5 parts of deionized water, 3 parts of film-forming aid, and 1.5 parts of leveling agent according to parts by weight , 1.5 parts of coupling agent and 0.5 parts of defoamer, set aside;

[0063] Step 2: Add the antibacterial and antifouling emulsion into the mixer, add curing agent and co-solvent under the condition of stirring speed of 800r / min, continue to shear for 20min, then add deionized water, film-forming aid, leveling agent in sequence The agent and the coupling agent continue to shear for 1 hour, then add the defoamer and stir for 10 minutes under the condition that the stirring speed is 100 r / min, then let it stand for 2 hours, and filter to obtain the antibacterial sanitary coating;

[0064] Step 3: Pr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
quality scoreaaaaaaaaaa
quality scoreaaaaaaaaaa
Login to View More

Abstract

The invention discloses an antibacterial sanitary mobile phone film and a preparation method thereof, and relates to the field of mobile phone films.The preparation method comprises the steps that an antibacterial antifouling emulsion, a curing agent, a cosolvent, deionized water, a coalescing agent, a flatting agent, a coupling agent and a defoaming agent are stirred to be uniform, then standing and filtering are conducted, and antibacterial sanitary coating is obtained; the antibacterial sanitary coating is sprayed to a rectangular glass sheet subjected to ultrasonic cleaning, an antibacterial sanitary coating is formed after drying, finally, rubberizing is carried out, packaging is carried out after inspection is qualified, and the antibacterial sanitary mobile phone film is obtained. The antibacterial and antifouling emulsion is formed by polymerization of four monomers including methyl methacrylate, butyl acrylate, an intermediate 3 and an intermediate 5, the intermediate 3 endows the antibacterial and antifouling emulsion with good stain-resistant and self-cleaning effects, a formed coating is not prone to being contaminated by stains and easy to clean, and the intermediate 5 endows the antibacterial and antifouling emulsion with good antibacterial and antiviral performance, so that the antibacterial and antifouling emulsion is good in anti-fouling and self-cleaning effects. Therefore, bacterium breeding is avoided, and the cleanliness of the mobile phone film is guaranteed.

Description

technical field [0001] The invention relates to the field of mobile phone film sticking, in particular to an antibacterial and hygienic mobile phone film and a preparation method thereof. Background technique [0002] Mobile phone film is usually used to beautify the mobile phone, and at the same time protect the LCD screen of the mobile phone. As we all know, with the development of the economy and the continuous improvement of people's living standards, smart phones have become an indispensable tool in people's lives. Smart phone screens Made of glass, it is fragile and not resistant to scratches, which affects the service life of the mobile phone. Therefore, tempered glass mobile phone film has become a necessity; [0003] However, today's smart phones use large-screen touch screens, and various operations are performed on the mobile phone through human fingers. Because there are many bacteria on the hands, it is easy to contaminate the mobile phone film. Due to the parti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/12C09D5/14C08F220/14C08F220/18C08F220/22C08F220/34C09J7/20
CPCC09D133/16C09D5/14C08F220/14C08F220/1804C09J7/20C09J2301/122C09J2400/143C08F220/22C08F220/34
Inventor 余正波黄晓
Owner 江西昊泽光学膜科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com