Natural stone imitated stain-resistant water permeable brick and preparation method thereof

A technology imitating natural stone and permeable bricks, applied in the direction of coating, etc., can solve the problems such as the pollution resistance of permeable bricks that needs to be improved, and achieve the effect of compact structure, promoting bonding and improving affinity

Active Publication Date: 2021-09-21
温州恒福新型建材有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The pursuit of the quality of permeable bricks is still the direction pursued by researchers who use permeable building materials, and the pollution resistance of existing permeable bricks still needs to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] The present application discloses a preparation method of water resistant bricks of natural stone; a preparation method thereof; a reflective water tile of natural stone, including a brick body of a surface coated paint; the raw material of imitation stone coatings includes the following components : Phenolic resin powder, fluorocarbon emulsion, polylactic acid, modified magnesium aluminum talc, 2-methoxyethyl acetate, inorganic pigment, deionized water, film forming aid.

[0046]Among them, the preparation method of modified magnesium aluminum hydraulite is: 15 parts of deionized water is added to 12 parts of magnesium aluminum, and then 4% of the magnesium aluminum talc weight parts of the laurel ether phosphate, in 40 The mixture was stirred at ° C for 40 in, and 2 parts of methyl methacrylate was added, and then stirred for 2 h; the resulting precipitate was filtered, dried the filter cake at 80 ° C to give the modified magnesium aluminum water talc.

[0047] Bricks inc...

Embodiment 2

[0054] The present application discloses a preparation method of water resistant bricks of natural stone; a preparation method thereof; a reflective water tile of natural stone, including a brick body of a surface coated paint; the raw material of imitation stone coatings includes the following components : Phenolic resin powder, fluorocarbon emulsion, polylactic acid, modified magnesium aluminum talc, 2-methoxyethyl acetate, inorganic pigment, deionized water, film forming aid.

[0055] Among them, the preparation method of modified magnesium aluminum water talc is: 18 parts of deionized water in 15 parts of magnesium aluminum, and then add 6% of magnesium aluminum talc weight parts of the laurel ether phosphate, at 50 At ° C, stirring for 50 min, and finally 4 parts of methyl methacrylate hydroxyethyl methacrylate was added, and stirring was continued for 3 h; filtrate the resulting precipitate, dried the filter cake at 80 ° C to give a modified magnesium aluminum water talc.

...

Embodiment 3

[0063] The present application discloses a preparation method of water resistant bricks of natural stone; a preparation method thereof; a reflective water tile of natural stone, including a brick body of a surface coated paint; the raw material of imitation stone coatings includes the following components : Phenolic resin powder, fluorocarbon emulsion, polylactic acid, modified magnesium aluminum talc, 2-methoxyethyl acetate, inorganic pigment, deionized water, film forming aid.

[0064] Among them, the preparation method of modified magnesium aluminum water talc is: 16 parts of deionized water in 14 parts of magnesium aluminum, and then add 4.5% of the magnesium aluminum talc weight of the laurel ether phosphate, at 45 The mixture was stirred at ° C for 45 min, and 3 parts of methyl methacrylate was added, and stirring was continued for 3 h; filtered the resulting precipitate, dried the filter cake at 80 ° C to give the modified magnesium aluminum water talc.

[0065] Bricks incl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a natural stone imitated stain-resistant water permeable brick and a preparation method thereof. The natural stone imitating stain-resistant water permeable brick comprises a brick body, wherein the surface of the brick body is coated with stone imitating paint; the stone-like coating is prepared from the following raw materials in parts by weight: 20-30 parts of phenolic resin powder; 10-14 parts of a fluorocarbon emulsion; 6-8 parts of polylactic acid; 4-5 parts of modified magnesium aluminum hydrotalcite; 3-4 parts of 2-methoxy ethyl acetate; 8-9 parts of an inorganic pigment; 5-7 parts of deionized water; 1-2 parts of a coalescing agent; the invention relates to a preparation method of a natural stone imitating stain-resistant water permeable brick. The preparation method comprises the following steps: preparing a stone imitating coating; preparing a brick body; and spraying a stone-like coating to finally obtain the stone-like water permeable brick. The pollution-resistant stone-like coating prepared by mixing the phenolic resin powder and the fluorocarbon emulsion is adopted; particles of the modified magnesium-aluminum hydrotalcite improve the regularity of the coating and the flatness of the surface, increase the contact angle between a pollution source and the coating, and are mixed with polylactic acid to form a uniform physical net structure, so pollutants are not easy to adhere, and the pollution resistance of the water permeable brick is improved.

Description

Technical field [0001] The present application relates to the technical field of penetrating bricks, in particular, involving a preparation method of stain resistant bricks of natural stone. Background technique [0002] The water-based brick is a new product for environmentally friendly building materials that solves the city's surface hardening, creating high quality natural living environment, and maintaining urban ecological balance. Due to its structural characteristics of its high permeation and high porosity, the road area water is eliminated, and the groundwater resources are supplemented in time, reduce the foundation sink, alleviate the pressure of urban flood drainage and dredging of pipelines; on the other hand through the brick hole hole The evaporation of the medium moisture reduces the heat absorption and "heat island effect" in the city, and the noise pollution of the city is effective. [0003] For the pursuit of the quality of the water, it is still the directio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D161/06C09D127/12C09D7/62C09D7/63C04B28/00C04B41/65
CPCC09D161/06C09D7/62C09D7/63C04B28/00C04B41/50C04B41/65C08L2205/03C04B14/06C04B14/28C04B2103/0068C04B41/488C04B41/46C04B41/4543C08L27/12C08L67/04C08K9/04C08K3/22C08K5/09
Inventor 郑建东郑建锋
Owner 温州恒福新型建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More