A double-sided, antistatic technology, applied in conductive coatings, coatings, epoxy resin coatings, etc., can solve the problems of dust absorption, affecting processing quality, and damage to electronic components, etc., to achieve strong antistatic ability and avoid The effect of charge accumulation

Pending Publication Date: 2021-08-06
JIXIANGBAO TAICANG RELEASE MATERIAL TECH CO LTD
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Because the base material of ordinary release film is polyester material, which is an insulator, it is easy to generate static electricity in the process of winding and unwinding. Light static electricity will cause dust to be absorbed and affect the quality of post-processing. Heavy static electricity will cause contact with it. Electronic components are damaged by high voltage discharge
[0004] Patent CN109796690A discloses a preparation method of an antistatic multi-color multi-film type release film, which is mixed and granulated by resin powder, auxiliary agent, lubricant, masterbatch, antioxidant, and antistatic agent, and corona treated after molding , and then sprayed with a release agent; the antistatic agent is a mixture of polyacetylene, sodium phosphate, sodium dodecylsulfonate, and ethoxylated stearyl amine, and the antistatic effect is not ideal

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Front and back double-sided anti-static composite release film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Such as figure 1 The front and back double-sided antistatic composite release film shown, from top to bottom, includes front release agent coating 1, front antistatic layer 2, substrate original film layer 3, back antistatic layer 4, back release Forming agent coating 5; The thickness of the original film layer 3 of the substrate is 70 μm; The thickness of the front antistatic layer 2 and the back antistatic layer 4 is 25 μm; The front release agent coating 1 and the back release The thickness of the agent coating 5 is 8 μm.

[0030] Wherein, the base material original film layer is a composite film composed of PET, PE, and PI, which includes the following components by weight ratio: 60 parts of PET particles, 25 parts of PP particles, and 20 parts of PI particles.

[0031] Moreover, the front antistatic layer includes the following components by weight: 25 parts of carbon nanotubes, 35 parts of epoxy resin, 9 parts of silicone oil, 2 parts of defoaming agent, 2 parts ...

Embodiment 2

[0039] A double-sided antistatic composite release film, which includes, from top to bottom, a front release agent coating 1, a front antistatic layer 2, a substrate original film layer 3, a reverse antistatic layer 4, and a reverse release film. Agent coating 5; The thickness of the original film layer 3 of the substrate is 30 μm; The thickness of the front antistatic layer 2 and the back antistatic layer 4 is 15m; The front release agent coating 1 and the back release agent The coating 5 has a thickness of 4 μm.

[0040] Wherein, the base material original film layer is a composite film composed of PET, PE, and PI, which includes the following components by weight ratio: 50 parts of PET particles, 15 parts of PP particles, and 10 parts of PI particles.

[0041] In addition, the front antistatic layer includes the following components by weight: 20 parts of carbon nanotubes, 30 parts of epoxy resin, 5 parts of silicone oil, 0.5 parts of defoaming agent, 0.5 parts of leveling ...

Embodiment 3

[0049] A double-sided antistatic composite release film, which includes, from top to bottom, a front release agent coating 1, a front antistatic layer 2, a substrate original film layer 3, a reverse antistatic layer 4, and a reverse release film. Agent coating 5; The thickness of the original film layer 3 of the substrate is 50 μm; The thickness of the front antistatic layer 2 and the back antistatic layer 4 is 20 μm; The front release agent coating 1 and the back release agent The thickness of the coating 5 is 6 μm.

[0050] Wherein, the original film layer of the base material is a composite film composed of PET, PE, and PI, which includes the following components by weight ratio: 55 parts of PET particles, 20 parts of PP particles, and 15 parts of PI particles.

[0051] Moreover, the front antistatic layer includes the following components by weight: 22.5 parts of carbon nanotubes, 32.5 parts of epoxy resin, 7 parts of silicone oil, 1.25 parts of defoaming agent, 1.25 parts...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a front and back double-sided anti-static composite release film which is characterized by sequentially comprising a front release agent coating layer (1), a front anti-static layer (2), a base material original film layer (3), a back anti-static layer (4) and a back release agent coating layer (5) from top to bottom; the thickness of the base material original film layer (3) is 30-70 [mu]m; the thicknesses of the front anti-static layer (2) and the back anti-static layer (4) are 15-25 [mu]m; and the thicknesses of the front release agent coating layer (1) and the back release agent coating layer (5) are 4-8 [mu]m. The front side and the back side of the front and back double-sided antistatic composite release film have antistatic functions, charge accumulation on the release film is avoided, the release film can be applied to the electronic industry, and static electricity generated by the release film is prevented from breaking down a circuit board of an electronic element.

Description

technical field [0001] The invention belongs to the technical field of release films, in particular to a double-sided antistatic composite release film. Background technique [0002] The release film refers to the film whose surface energy can be distinguished. The release film is not sticky or slightly sticky after contacting with specific materials under limited conditions. It is widely used in electronic power, IT display screens, mobile phones, LCD / PDA, medical, home appliance manufacturing, anti-counterfeiting materials, semiconductors, automobiles, nameplates, ceramic sheet manufacturing, adhesive tape production and die-cutting industries. [0003] With the development of LCD, LED, PC, mobile phone and other industries, the demand for release film is increasing day by day, and the requirements are getting higher and higher. One of them is that the release film has antistatic function. Since the base material of ordinary release film is polyester material, which is a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08J5/18C08J7/04C08J7/044C08J7/06C08L67/02C08L23/12C08L79/08C09D163/00C09D183/04C09D5/24C09D7/61C09D165/00
CPCC08J5/18C08J7/044C08J7/042C08J7/065C09D163/00C09D5/24C09D7/61C09D165/00C08J2367/02C08J2423/12C08J2479/08C08J2463/00C08J2483/04C08J2465/00C08K2003/2231C08K2003/0806C08K2003/0812C08L2201/04C08L2203/16C08L83/04C08K3/041C08K3/22C08K3/08
Inventor 於险峰
Owner JIXIANGBAO TAICANG RELEASE MATERIAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap