Coal mine composite colloid fire preventing and extinguishing material and preparation method thereof

A kind of anti-fire extinguishing and colloidal technology, which is applied in the direction of fire prevention equipment, etc., can solve the problems of not being able to accumulate to high places, easy to block pipes, and long gel time, etc., to achieve improved mechanical properties, good water retention and flame retardancy, and high fluidity Effect

Active Publication Date: 2021-08-06
河南中煤矿业科技发展有限公司
View PDF14 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Among them, the colloidal materials mainly include cement fly ash gel materials and polymer gel materials. Among them, cement fly ash gel materials have been used earlier, and are cheap, non-toxic, and have good permeability. They have been used until now. The disadvantages are: The usage amount is large, the gel time is long, it cannot be piled up at a high place, and the fluidity is poor, it is easy to block the pipeline, and it is easy to crack after the gel layer is formed; the polymer gel material has good fluidity, good fire prevention effect, and the gel layer High strength, but its cost is relatively high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A coal mine composite colloid fire-preventing material is made of the following raw materials in parts by weight: 1 part of sodium carboxymethylcellulose, 2 parts of agar, 12 parts of fly ash, 0.1 part of polyacrylamide, 6 parts of crosslinking agent, 1 part of sodium bicarbonate, 3 parts of flame retardant, 3 parts of foaming agent, 90 parts of water.

[0029] Wherein the crosslinking agent is a metal ion crosslinking agent supported by montmorillonite.

[0030] The cross-linking agent is prepared by the following steps:

[0031] 1) Slowly drop the sodium hydroxide solution into the aluminum chloride solution. After the drop is completed, the temperature is raised rapidly until the solution boils. After 30 minutes, it is cooled to obtain aluminum hydroxy;

[0032] 2) Add montmorillonite to hydroxyaluminum, stir and mix at 70°C for 60-70min, filter under reduced pressure, and dry to obtain the product;

[0033] The molar ratio of sodium hydroxide to aluminum chloride ...

Embodiment 2

[0042] A coal mine composite colloid fire prevention material is made of the following raw materials in parts by weight: 1.2 parts of sodium carboxymethylcellulose, 1.8 parts of agar, 13 parts of fly ash, 0.12 parts of polyacrylamide, 6.5 parts of crosslinking agent, 1.2 parts of sodium bicarbonate, 3.2 parts of flame retardant, 3.5 parts of foaming agent, 90 parts of water.

[0043] Wherein the crosslinking agent is a metal ion crosslinking agent supported by montmorillonite.

[0044] The cross-linking agent is prepared by the following steps:

[0045]1) Slowly drop the sodium hydroxide solution into the aluminum chloride solution. After the drop is completed, the temperature is raised rapidly until the solution boils. After 30 minutes, it is cooled to obtain aluminum hydroxy;

[0046] 2) Add montmorillonite to hydroxyaluminum, stir and mix at 70°C for 60-70min, filter under reduced pressure, and dry to obtain the product;

[0047] The molar ratio of sodium hydroxide to alu...

Embodiment 3

[0052] A coal mine composite colloid fire-preventing material is made of the following raw materials in parts by weight: 1.5 parts of sodium carboxymethylcellulose, 1.5 parts of agar, 14 parts of fly ash, 0.15 parts of polyacrylamide, 7 parts of crosslinking agent, 1.5 parts of sodium bicarbonate, 3.5 parts of flame retardant, 4 parts of blowing agent, 95 parts of water.

[0053] Wherein the crosslinking agent is a metal ion crosslinking agent supported by montmorillonite.

[0054] The cross-linking agent is prepared by the following steps:

[0055] 1) Slowly drop the sodium hydroxide solution into the aluminum chloride solution. After the drop is completed, the temperature is raised rapidly until the solution boils. After 30 minutes, it is cooled to obtain aluminum hydroxy;

[0056] 2) Add montmorillonite to hydroxyaluminum, stir and mix at 75°C for 60-70min, filter under reduced pressure, and dry to obtain the product;

[0057] The molar ratio of sodium hydroxide to alumin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a coal mine composite colloid fire preventing and extinguishing material. The material is prepared from the following raw materials in parts by weight: 1-2 parts of sodium carboxymethyl cellulose, 1-2 parts of agar, 12-15 parts of coal ash, 0.1-0.2 part of polyacrylamide, 3-5 parts of a cross-linking agent, 1-2 parts of sodium bicarbonate, 3-4 parts of a flame retardant, 3-5 parts of a foaming agent and 90-100 parts of water. The material is low in cost, good in water retention and flame retardance and excellent in fire preventing and extinguishing performance.

Description

technical field [0001] The invention relates to the technical field of fire prevention and extinguishing materials for mines. Background technique [0002] Coal mine fires are likely to cause accidents such as gas and dust explosions, which are extremely harmful. Therefore, fire prevention and control is the focus of coal mine safety production. The main cause of fires in coal mines is coal seam spontaneous combustion, and due to fully mechanized top coal mining and gas drainage technologies used in coal mine mining, air leakage in gobs or a large amount of residual coal are likely to cause coal seam spontaneous combustion. The main means of fire prevention and extinguishing in coal mines at present adopts fire extinguishing materials, which have high safety and remarkable effect. [0003] Commonly used anti-fire extinguishing materials include colloidal materials, mud, foam, and inhibitors, etc. The mechanism of anti-fire extinguishing is: using quantitative addition equip...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A62D1/00A62D1/06A62D1/04
CPCA62D1/0064A62D1/06A62D1/005A62D1/0071
Inventor 郝宇吴立军
Owner 河南中煤矿业科技发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com